A survey of test methods for scale adhesion measurement

Materials at High Temperatures

Volumn 22, Issue 1-2, 2005, Pages 121-129

  Hou, P Y ^a   Saunders, S R J ^b  

^a LAWRENCE BERKELEY NATIONAL LABORATORY   (United States)

^b NATIONAL PHYSICAL LABORATORY   (United Kingdom)

Author keywords

Scale adhesion measurements; Spallation of oxides sales

Indexed keywords

COMPRESSIVE STRENGTH; CRACK PROPAGATION; INDENTATION; INTERFACES (MATERIALS); TENSILE TESTING;

POWER GENERATION BOILERS; SCALE CRACKING; SPALLATION PROCESS;

ADHESION;

EID: 24944529872     PISSN: 09603409     EISSN: None     Source Type: Journal    
DOI: 10.1179/mht.2005.014     Document Type: Conference Paper

References (47)

1. Armitt, J., Holmes, D.R., Manning, M.I., Meadowcroft, D.B. and Metcalfe, E. The spalling of steam-grown oxide from superheater and reheater tube steels. EPRI report FP-686, February (1978).
2. 3/(0001)/Cu(111) interface. Inter. Sci., 3, 289-302 (1996).
3. Mao, S.X. and Evans, A.G. The influence of blunting on crack growth at oxide/metal interfaces. Acta Mater., 45, 4263-4270 (1997).
4. Evans, A.G., Hutchinson, J.W. and Wei, Y. Interface adhesion: effects of plasticity and segregation. Acta Mater., 47, 4093-4113 (1999).
5. Schutze, M., Ito, S., Przybilla, W., Eshsler, H. and Bruns, C. Test methods and data on the mechanical properties of protective oxide scales. Mater. High Temp., 18, 39-50 (2001).
6. Chalker, P.R., Bull, S.J. and Rickerby, D.S. A review of the methods for the evaluation of coating-substrate adhesion. Mater. Sci. Eng., A.140, 583-592 (1991).
7. Hou, P.Y. and Atkinson, A. Methods of measuring adhesion for thermally grown oxide scales. Mater. High Temp., 12, 119-126 (1994).
8. Saunders, S., Banks, J., Osgerby, S., Rickerby, D. and Chunnilall, C. An evaluation of tests for the adhesion of thermal barrier coatings. Mater. Sci. Forum, 369-372, 775-783 (2001).
9. Hutchinson, J.W. and Suo, Z. Mixed mode cracking in layered materials. Adv. Appl. Mech., 29, 63-191 (1991).
10. Timoshenko. S. and Gere, J.M. Theory of Elastic Stability. Engineering Society Monograph, New York (1936).
11. Evans, A.G. and Hutchinson, J.W. On the mechanics of delamination and spalling in compressed films. Inst. J. Solids Struc., 20, 455-466 (1984).
12. Hutchinson, J.W., Thouless, M.D. and Liniger, E.G. Growth and configurational stability of circular, buckling-driven film delaminations. Acta Metall. Mater., 40, 295-308 (1992).
13. Evans, H.E. and Lobb, R.C. Conditions for the initiation of oxidescale cracking and spallation. Corros. Sci., 24, 209-222 (1984).
14. Hou, P.Y., Zhang, H and Cannon, R.M. unpublished results, 1994.
15. Cannon, R.M., Dalgleish, B.J., Dauskardt, R.H., Oh, T.S. and Ritchie, R.O. Cyclic fatigue-crack propagation along ceramic/metal interfaces. Acta Mater., 39, 2145-2156 (1991).
16. Dirks-Eichen, A., Schumann, E. and Ruhle, M. Unterschungen zur hochtemperaturoxidation von NiAl, paper presented at Werkstoffe Woche, Stuttgart (1997).
17. Suga, T. and Elssner, G. Bond strength determination of metal-to-ceramic joints by a bend test method. Z. Werkstofftech., 16, 75-80 (1985).
18. Atkinson, A. and Guppy, R. Measurement of adhesion of oxides grown on nickel and nickel alloys. Mater. Sci. Technol., 7, 1031-1041 (1991).
19. Coddet, C., Chaze, A.M. and Beranger, G. Measurements of the adhesion of thermal oxide films: application to the oxidation of titanium. J. Mater. Sci., 22, 2969-2974 (1987).
20. Huntz, A.M., Zhao, J.G., Boumaza, A. and Moulin, G. Parameters affecting oxide adherence in nickel based alloys and techniques allowing estimation of adhesion. Mater. Sci. Technol., 4, 470-478 (1988).
21. 3/NiAl interfaces and their relationship to scale adhesion. In: Opila, E., Hou, P., Maruyama, T., Pieraggi, B., McNallan, M., Shifler, D. and Wuchina, E.(eds), High Temperature Corrosion and Materials Chemistry, IV, Electrochemical Society, PV 2003-16, pp. 40-50 (2003).
22. Personal communication, S Osgerby and A Fry, NPL
23. Quadakkers, W.J., Ennis, P.J., Zurek J. and Michalik M. Steam oxidation of ferritic steels, In: Opila, E., Hou, P., Maruyama, T., Pieraggi, B., McNallan, M., Shifler, D. and Wuchina, E. (eds), High Temperature Corrosion and Materials Chemistry, IV, Electrochemical Society, PV 2003-16 (2003).
24. Nagl, M.M., Evans, W.T., Saunders, S.R.J. and Hall, D.J. Investigation of failure of brittle layers under compressive stresses using acoustic emission. Mater. Sci. Technol., 8, 1043-1049 (1992).
25. Nagl, M.M., Evans, W.T., Hall, D.J. and Saunders, S.R.J. An in situ investigation of the tensile failure of oxide scales. Oxid. Met., 42, 431-449 (1994).
26. Nagl, M.M. Saunders, S.R.J. Evans, W.T. and Hall, D.J. The tensile failure of nickel oxide scales at ambient and growth temperature. Corros. Sci., 35, 965-977 (1993).
27. Saunders, S., Banks, J., Osgerby, S. Rickerby, D and Chunnilall, C. An evaluation of tests for the adhesion of thermal barrier coatings. Mater. Sci. Forum, 369-372, 775-784 (2001).
28. Kekare, S., Hou, P.Y. and Cannon, R.M. Interfacial fracture energies of thermally grown NiO on Ni determined by room temperature 4-point bend tests, unpublished paper (1994).
29. Agrawal, D.C. and Raj, R. Measurement of the ultimate shear strength of a metal-ceramic interface. Acta Metall, 37, 1265-1270 (1989).
30. Bull, S.J. Microscopy of failure in the scratch adhesion testing of oxide scales. Microscopy of Oxidation, 3, pp. 309-319. The Institute of Metals (1997).
31. Laugier, M.T. An energy approach to the adhesion of coatings using the scratch test. Thin Solid Films, 117, 243-249 (1984).
32. Bull, S.J. and Rickerby, D.S. New developments in the modelling of the hardness and scratch adhesion of thin films. Surf. Coatings Techol., 42, 149-164 (1990).
33. Lipkin, D.M. and Clarke, D.R. Measurement of the stress in oxide scales formed by oxidation of alumina-forming alloys. Oxid. Met., 45, 267-280 (1996).
34. 3 scales formed on oxide dispersion-strengthened alloys. Oxid. Met., 56, 119-145 (2001).
35. Pint, B.A., Garratt-Reed, A.J. and Hobbs, L.W. The reactive element effect in commercial ODS FeCrAl alloys. Mater. High Temp., 13, 3-16 (1995).
36. Johnstone, A., Rickerby, D.S. and Morrell, P., Rolls Royce, unpublished
37. Vasinonta, A. and Beuth, J.L. Measurement of interfacial toughness in thermal barrier coating systems by indentation. Eng. Fracture Mech., 68, 843-860 (2001).
38. Hou, P.Y. and Cannon, R.M., Spallation behavior of thermally grown nickel oxide on nickel, manuscript in preparation.
39. Baleix, S., Bernhart, G. and Lours, P. Oxidation and oxide spallation of heat resistant cast steels for superplastic forming tools. Mater. Sci. Eng., A327, 155-166 (2002).
40. Zhang, Y. and Shores, D.A. Cracking and spalling of oxide scale from 304 stainless steel at high temperatures. J. Electrochem. Soc., 141, 1255-1260 (1994).
41. Sarioglu, C., Stiger, M.J., Blachere, J.R., Janakiraman, R., Schumann, E., Ashary, A., Pettit, F.S. and Meier, G.H. The adhesion of alumina films to metallic alloys and coatings. Werk. Korr., 51, 358-372 (2000).
42. Evans, H.E. Spallation of oxide from stainless steel AGR nuclear fuel cladding: mechanisms and consequences. Mater. Sci. Eng., 4, 415-420 (1988).
43. Drory, M.D. and Hutcinson, J.W. Measurement of the adhesion of a brittle film on a ductile substrate by indentation. Proc. R. Soc. Lond. A, 452, 2319-2341 (1996).
44. Osgerby, S., Saunders, S.R.J. and Banks, J, Scale and Coating Adhesion: A procedure for laboratory tests, NPL report CMMT (MN)026 (1998).
45. Osgerby, S, unpublished work NPL (2003).
46. Wang, J.S. and Evans, A.G. Measurement and analysis of buckling and buckle propagation in comopressed oxide layers on superalloy substrates. Acta Mater., 14, 4993-5005 (1998).
47. Mougin, J., Dupeux, M., Galerie, A., and Antoni, L. Inverted blister test to measure adhesion energy of thermal oxide scales on metals or alloys. Mater. Sci. Technol., 18, 1217-1220 (2002).