Modeling the influence of crack path deviations on the propagation of stress corrosion cracks

Hydrogen Effects on Material Behaviour and Corrosion Deformation Interactions - Proc. of the International Conference on Hydrogen Effects on Material Behaviour and Corrosion Deformation Interactions

Volumn , Issue , 2003, Pages 629-638

  Ricker, Richard E ^a  

^a NATIONAL INSTITUTE OF STANDARDS AND TECHNOLOGY   (United States)

Author keywords

[No Author keywords available]

Indexed keywords

CRACK MEASUREMENT TOOLS; CRACK PROPAGATION MEASUREMENTS; FRACTURE ROUGHNESS; STRESS INTENSITY;

CRACK PROPAGATION; FRACTURE; GRAIN SIZE AND SHAPE; MATHEMATICAL MODELS; MICROSTRUCTURE; PLASTICITY; PRECIPITATION (CHEMICAL); STRESS CONCENTRATION; SURFACES;

STRESS CORROSION CRACKING;

EID: 23844464984     PISSN: None     EISSN: None     Source Type: Conference Proceeding    
DOI: None     Document Type: Conference Paper

References (12)

1. M. V. Hyatt and M. O. Speidel, "Stress-Corrosion Cracking of High-Strength Aluminum Alloys," Boeing Commercial Airplane Group, D6-24840, Seattle, WA, (1970).
2. D. O. Sprowls, M. B. Shumaker and J. D. Walsh, "Evaluation of Stress-Corrosion Cracking Susceptibility Using Fracture Mechanics Techniques," Aluminum Company of America, NASA Contract Rpt., NAS 8-21487, Alcoa Center, PA, (1973).
3. A. K. Vasudevan, R. G. Malcolm, W. G. Fricke and R. J. Rioja, "Resistance to Fracture, Fatigue and Stress-Corrosion of Al-Cu-Li-Zr Alloys," ALCOA Laboratories, Tech. Rpt., ONR Cont. No. N00019-80-0569, Alcoa Center, PA, (1985).
4. A. K. Vasudevan and S. Suresh, "Microstructural Effects on Quasi-static Fracture Mech. in Al-Li Alloys: the Role of Crack Geometry," Mater Sci Eng, 72 (1985), 37-49.
5. B. Cotterell and J. R. Rice, "Slightly Curved or Kinked Cracks," Intl J Fract, 16 (2) (1980), 155-169.
6. E. H. Dix, "Acceleration of the Rate of Corrosion by High Constant Stresses," Trans AIME, 137 (1) (1940), 11-40.
7. E. H. Dix, "Al-Zn-Mg Alloys Their Development and Commercial Production," Trans ASM, 42 (1950), 1057-1127.
8. D. O. Sprowls and R. H. Brown, "What Every Engineer Should Know About Stress Corrosion of Aluminum, Part 1," Met Prog, 81 (4) (1962), 79-85.
9. D. O. Sprowls and R. H. Brown, "What Every Engineer Should Know About Stress Corrosion of Aluminum, Part 2," Met Prog, 81 (5) (1962), 77-83.
10. B. Cox, "Environmentally-Induced Cracking of Zirconium Alloys-A Review," J Nucl Mater, 170 (1) (1990), 1-23.
11. B. A. Bilby, G. E. Cardew and I. C. Howard, "Stress Intensity Factors at the Tips of Kinked and Forked Cracks," Proceedings of Fracture 1977, Waterloo, Canada, 3 (1977),
12. S. Suresh and C. F. Shih, "Plastic near-tip Fields for Branched Cracks," Intl J Fract, 30 (1986), 237-259.