Fractography of the stress corrosion cracking specimens of type 304 stainless steel in high temperature water containing boric acid and lithium ion

Journal of the Chinese Society of Corrosion and Protection

Volumn 24, Issue 1, 2004, Pages 18-19

  Li, Hongmei ^a   Yang, Wu ^b   Cai, Xun ^a   Lu, Zhanpeng ^b  

^a SHANGHAI JIAO TONG UNIVERSITY   (China)

^b SHANGHAI RESEARCH INSTITUTE OF MATERIALS   (China)

Author keywords

304 stainless steel; Fractography; Stress corrosion cracking

Indexed keywords

BORIC ACID; CORROSION; CRACKING; FRACTOGRAPHY; HIGH TEMPERATURE CORROSION; STAINLESS STEEL; STRESS CORROSION CRACKING;

EID: 2142770353     PISSN: 10054537     EISSN: None     Source Type: Journal    
DOI: None     Document Type: Article

References (9)

1. Yang Wu, Zhang Meijie, Zhao Guozhen, Congleton John. A comparison of U - bend and slow strain rate procedures for assessing the SCC resistance of type 304 stainless steel in high - temperature water [J]. Corrosion, 1991, 47(4):226-233
2. Yang Wu, Zhao Guozhen, Zhang Meijie, Congleton John. An AES investigation of the surface films formed on stress corrosion test specimens of type 304 stainless steel in high temperature water[J]. Corros. Sci., 1992, 33(1):89-102
3. Ruther W E, Soppet W K, Kassner T F. Effect of temperature and ionic impurities at very low concentrations on stress corrosion cracking of AISI 304 stainless steel[J] Corrosion, 1988, 44(11):791-799
4. MacDonald D D, Song H. Yoshida K. Corrosion potential measurements on type 304SS and alloy 182 in simulated BWR environments [J]. Corrosion, 1993, 49(1):8-16
5. Congleton J. Berrisford R A, Yang Wu. Stress corrosion cracking of sensitized type 304 stainless steel in doped high - temperature water [J]. Corrosion, 1995, 51(2):901-910
6. Cui Yuexian, Wang Changli. Analysis of Metal Fracture Section [M]. Harbin: Harbin Industry University Publishing Company, 1998
7. Henry G, Horstman D. Macroscope and Microscope Fractography [M]. Beijing: Mechanical Industry Publishing Company, 1990
8. Zuo Jingyi. Stress Corrosion Crack[M]. Xi'an: Xi'an Jiaotong University Publishing Company, 1985
9. Chu Wuyang, Qiao Lijie, Chen qizhi. Fracture and Environmental Fracture[M]. Beijing: Science Press, 2000