The effect of low-velocity impact on the fatigue life of Sandwich composites

Author keywords

Carbon fiber; Fatigue; Impact; Sandwich composite; Ultrasonic

Indexed keywords

BENDING (DEFORMATION); CARBON FIBERS; COMPOSITE MATERIALS; DELAMINATION; FAILURE (MECHANICAL); FATIGUE OF MATERIALS; IMPACT RESISTANCE;

EID: 20944441425     PISSN: 02638223     EISSN: None     Source Type: Journal    
DOI: 10.1016/j.compstruct.2004.09.027     Document Type: Article
Times cited : (34)

References (24)
  • 1
    • 0034746405 scopus 로고    scopus 로고
    • Experimental set-up for and numerical modeling of bending fatigue experiments on plain woven glass/epoxy composites
    • W. VanPaepegem Experimental set-up for and numerical modeling of bending fatigue experiments on plain woven glass/epoxy composites Compos. Struct. 51 2001 1-8
    • (2001) Compos. Struct. , vol.51 , pp. 1-8
    • VanPaepegem, W.1
  • 2
    • 20944435748 scopus 로고
    • Fatigue of cross-plied, through the thickness reinforced carbon/epoxy composites
    • Masters Thesis, Clemson University
    • Serdinak T. Fatigue of cross-plied, through the thickness reinforced carbon/epoxy composites. Masters Thesis, Clemson University, 1994.
    • (1994)
    • Serdinak, T.1
  • 3
    • 0032100144 scopus 로고    scopus 로고
    • The effects of hail damage on the fatigue strength of graphite/epoxy composite laminate
    • M. Mahinfalah R. Skordahl The effects of hail damage on the fatigue strength of graphite/epoxy composite laminate Compos. Struct. 42 1998 101-106
    • (1998) Compos. Struct. , vol.42 , pp. 101-106
    • Mahinfalah, M.1    Skordahl, R.2
  • 4
    • 0036488066 scopus 로고    scopus 로고
    • Closed prediction of peak load and delaminations onset under small mass impact
    • R. Olsson Closed prediction of peak load and delaminations onset under small mass impact Compos. Struct. 59 2003 341-349
    • (2003) Compos. Struct. , vol.59 , pp. 341-349
    • Olsson, R.1
  • 5
    • 0037210536 scopus 로고    scopus 로고
    • The response of laminated composite plates under low-velocity impact loading
    • Z. Aslan The response of laminated composite plates under low-velocity impact loading Compos. Struct. 59 2003 119-127
    • (2003) Compos. Struct. , vol.59 , pp. 119-127
    • Aslan, Z.1
  • 6
    • 0035336350 scopus 로고    scopus 로고
    • Dynamic models for low-velocity impact damage of composite sandwich panels - Part B: Damage initiation
    • M. Hoo Fatt Dynamic models for low-velocity impact damage of composite sandwich panels - Part B: Damage initiation Compos. Struct. 52 2001 353-364
    • (2001) Compos. Struct. , vol.52 , pp. 353-364
    • Hoo Fatt, M.1
  • 7
    • 0038692271 scopus 로고    scopus 로고
    • Effect of projectile shape during ballistic perforation of VARTM carbon/ epoxy composite panels
    • C. Ulven Effect of projectile shape during ballistic perforation of VARTM carbon/epoxy composite panels Compos. Struct. 61 2003 143-150
    • (2003) Compos. Struct. , vol.61 , pp. 143-150
    • Ulven, C.1
  • 8
    • 0033683260 scopus 로고    scopus 로고
    • Mass criterion for wave controlled impact response of composite plates
    • R. Olsson Mass criterion for wave controlled impact response of composite plates Composites: Part A 31 2000 879-887
    • (2000) Composites: Part A , vol.31 , pp. 879-887
    • Olsson, R.1
  • 9
    • 0035448142 scopus 로고    scopus 로고
    • Finite element modeling of low velocity impact of composite sandwich panels
    • T. Besant Finite element modeling of low velocity impact of composite sandwich panels Composites: Part A 32 2001 1189-1196
    • (2001) Composites: Part A , vol.32 , pp. 1189-1196
    • Besant, T.1
  • 10
    • 85025178536 scopus 로고
    • Impact on laminated composites: Recent advances
    • S. Abrate Impact on laminated composites: Recent advances Appl. Mech. Rev. 41 11 1994 517-539
    • (1994) Appl. Mech. Rev. , vol.41 , Issue.11 , pp. 517-539
    • Abrate, S.1
  • 11
    • 0038269289 scopus 로고    scopus 로고
    • Flexural behavior of sandwich beams fabricated by vacuum-assisted resin transfer molding
    • J. Dai Flexural behavior of sandwich beams fabricated by vacuum-assisted resin transfer molding Compos. Struct. 2003 61
    • (2003) Compos. Struct. , pp. 61
    • Dai, J.1
  • 12
    • 0032978302 scopus 로고    scopus 로고
    • Fatigue life prediction of circular notched CFRP laminates
    • J.S. Huh Fatigue life prediction of circular notched CFRP laminates Compos. Struct. 44 1999 163-168
    • (1999) Compos. Struct. , vol.44 , pp. 163-168
    • Huh, J.S.1
  • 13
    • 0037357441 scopus 로고    scopus 로고
    • Fatigue crack growth and life prediction of foam core sandwich composites under flexural loading
    • N. Kulkarni Fatigue crack growth and life prediction of foam core sandwich composites under flexural loading Compos. Struct. 59 2003 499-505
    • (2003) Compos. Struct. , vol.59 , pp. 499-505
    • Kulkarni, N.1
  • 14
    • 0036468586 scopus 로고    scopus 로고
    • Prediction of the fatigue life of unidirectional glass fiber/epoxy composite laminae using different neural network paradigms
    • H. El Kadi Prediction of the fatigue life of unidirectional glass fiber/ epoxy composite laminae using different neural network paradigms Compos. Struct. 55 2002 239-246
    • (2002) Compos. Struct. , vol.55 , pp. 239-246
    • El Kadi, H.1
  • 15
    • 0036624404 scopus 로고    scopus 로고
    • A micro-mechanics damage approach for fatigue of composite materials
    • G.F. Abdekak A micro-mechanics damage approach for fatigue of composite materials Compos. Struct. 56 2002 413-422
    • (2002) Compos. Struct. , vol.56 , pp. 413-422
    • Abdekak, G.F.1
  • 16
    • 0036896486 scopus 로고    scopus 로고
    • Fatigue damage modeling of composite materials
    • H. Mao fatigue damage modeling of composite materials Compos. Struct. 58 2002 405-410
    • (2002) Compos. Struct. , vol.58 , pp. 405-410
    • Mao, H.1
  • 17
    • 0034082673 scopus 로고    scopus 로고
    • Evaluation of the residual strength degradation in composite laminates under fatigue loading
    • H.A. Whitworth Evaluation of the residual strength degradation in composite laminates under fatigue loading Compos. Struct. 48 2000 261-264
    • (2000) Compos. Struct. , vol.48 , pp. 261-264
    • Whitworth, H.A.1
  • 18
    • 0035426372 scopus 로고    scopus 로고
    • Initiation and growth of transverse and longitudinal cracks in composite cross-ply laminates
    • J. Rebiere Initiation and growth of transverse and longitudinal cracks in composite cross-ply laminates Compos. Struct. 53 2001 173-187
    • (2001) Compos. Struct. , vol.53 , pp. 173-187
    • Rebiere, J.1
  • 19
    • 0036933609 scopus 로고    scopus 로고
    • Probabilistic model of the fatigue life of composite materials for fatigue-curve approximations
    • Y. Paramonov Probabilistic model of the fatigue life of composite materials for fatigue-curve approximations Mech. Compos. Mater. 38 6 2002 741-750
    • (2002) Mech. Compos. Mater. , vol.38 , Issue.6 , pp. 741-750
    • Paramonov, Y.1
  • 20
    • 0036955958 scopus 로고    scopus 로고
    • Fatigue life estimates in woven carbon fabric/epoxy composites at non-ambient temperatures
    • R. Khan Fatigue life estimates in woven carbon fabric/epoxy composites at non-ambient temperatures J. Compos. Mater. 36 22 2002 2517-2535
    • (2002) J. Compos. Mater. , vol.36 , Issue.22 , pp. 2517-2535
    • Khan, R.1
  • 21
    • 0030153223 scopus 로고    scopus 로고
    • Composite fatigue design methodology: A simplified approach
    • T. Nyman Composite fatigue design methodology: A simplified approach Compos. Struct. 35 1996 183-194
    • (1996) Compos. Struct. , vol.35 , pp. 183-194
    • Nyman, T.1
  • 22
    • 0033039143 scopus 로고    scopus 로고
    • Compression, flexure and shear properties of a sandwich composite containing defects
    • A.P. Mouritz Compression, flexure and shear properties of a sandwich composite containing defects Compos. Struct. 44 1999 263-278
    • (1999) Compos. Struct. , vol.44 , pp. 263-278
    • Mouritz, A.P.1
  • 23
    • 0031198870 scopus 로고    scopus 로고
    • Fatigue of foam core sandwich beams - 1 undamaged specimens
    • M. Burman Fatigue of foam core sandwich beams - 1 undamaged specimens Int. J. Fatigue 19 7 1997 551-561
    • (1997) Int. J. Fatigue , vol.19 , Issue.7 , pp. 551-561
    • Burman, M.1
  • 24
    • 0031200020 scopus 로고    scopus 로고
    • Fatigue of foam core sandwich beams - 2 effect of initial damage
    • M. Burman Fatigue of foam core sandwich beams - 2 effect of initial damage Int. J. Fatigue 19 7 1997 563-578
    • (1997) Int. J. Fatigue , vol.19 , Issue.7 , pp. 563-578
    • Burman, M.1


* 이 정보는 Elsevier사의 SCOPUS DB에서 KISTI가 분석하여 추출한 것입니다.