Effect of an inhibitor on the stress corrosion cracking behavior of alloy 600 in a high-temperature caustic solution

Corrosion

Volumn 61, Issue 5, 2005, Pages 403-410

  Yi, Yongsun ^a   Kim, H ^a   Park, Y ^a   Kim, J ^a  

^a Korea Atomic Energy Research Institute   (South Korea)

Author keywords

Alloy 600; Corrosion current density; Inhibitor; Intergranular stress corrosion cracking

Indexed keywords

ALKALINITY; ALLOYS; CAUSTIC SODA; CERIUM COMPOUNDS; CURRENT DENSITY; HIGH TEMPERATURE EFFECTS; POLARIZATION; STRAIN RATE; STRESS CORROSION CRACKING;

LINEAR POLARIZATION METHODS; OPEN CIRCUIT POTENTIAL (OCP); SLOW STRAIN RATE TEST (SSRT); SODIUM HYDROXIDE (NAOH);

CORROSION INHIBITORS;

ALLOY; CORROSION INHIBITOR; STRESS CORROSION CRACKING;

EID: 20844460467     PISSN: 00109312     EISSN: None     Source Type: Journal    
DOI: 10.5006/1.3280639     Document Type: Article

References (14)

1. D.R. Diercks, W.J. Shack, J. Muscara, Nucl. Eng. Design 194 (1999): p. 19.
2. B.W. Brisson, R.G. Ballinger, A.R. McIlree, Corrosion 54, 7 (1998): p. 504.
3. P.M. Scott, "An Overview of Internal Oxidation as a Possible Explanation of Intergranular Stress Corrosion Cracking of Alloy 600 in PWRs," Proc. 9th Int. Symp. on Environmental Degradation of Materials in Nuclear Power Systems - Water Reactors (Warrendale, PA: The Minerals, Metals, and Materials Society [TMS], 1999), p. 3.
4. M.J. Partridge, W.S. Zemitis, J.A. Gorman, "Correlation of Secondary-Side IGA/SCC Degradation of Recirculating Steam Generator Tubing with the On-Line Addition of Boric Acid," EPRI Report TR-101010s (1992).
5. J. Daret, J.P.N. Paine, M.J. Partridge, "Model Boiler Testing to Evaluate Inhibitors for Caustic-Induced Stress Corrosion Cracking of Alloy 600 Tubes," Proc. 7th Int. Symp. on Environmental Degradation of Materials in Nuclear Power Systems - Water Reactors (Houston, TX: NACE International, 1995), p. 177.
6. U.C. Kim, K.M. Kim, J.S. Kang, E.H. Lee, H.P. Kim, J. Nucl. Mater. 302 (2002): p. 104
7. H. Kawamura, H. Hirano, Corrosion 55, 6 (1999): p. 596.
8. D.H. Hur, J.S. Kim, J.S. Baek, J.G. Kim, Corrosion 58, 12 (2002): p. 1,031.
9. J. Jankowski, R. Juchniewicz, Corros. Sci. 20 (1980): p. 841.
10. M. Stern, A.L. Geary, J. Electrochem. Soc. 104 (1957): p. 56.
11. B.P. Miglin, J.P. Paine, "Slow Strain Rate Testing to Evaluate Inhibitors for Stress Corrosion Cracking of Alloy 600, " Proc. 6th Int. Symp. on Environmental Degradation of Materials in Nuclear Power Systems - Water Reactors (Warrendale, PA: The Minerals, Metals, and Materials Society [TMS], 1993), p. 303.
12. M. Popovic, E. Romhanji, J. Mater. Process. Technol. 125-126 (2002): p. 275.
13. P.M. Scott, P. Combrade, "On the Mechanisms of Secondary Side PWR Steam Generator Tube Cracking," Proc. 8th Int. Symp. on Environmental Degradation of Materials in Nuclear Power Systems - Water Reactors (La Grange, IL: American Nuclear Society [ANS], 1997), p. 65.
14. P.L. Andresen, F.P. Ford, Mater. Sci. Eng. 103, 1 (1988): p. 167.