Reformulation of container glasses for environmental benefit through lower melting temperatures

Glass Technology

Volumn 46, Issue 1, 2005, Pages 11-19

  Bingham, P A ^a   Marshall, M ^b  

^a UNIVERSITY OF SHEFFIELD   (United Kingdom)

^b Glass Technology Services   (United Kingdom)

Author keywords

[No Author keywords available]

Indexed keywords

COMPOSITION; ENVIRONMENTAL IMPACT; HEAVY METALS; LAWS AND LEGISLATION; MELTING; NITROGEN OXIDES; PARTICLES (PARTICULATE MATTER); REDUCTION;

CHEMICAL DURABILITY; CONTAINER GLASS COMPOSITIONS; CULLETS; MELTING ENERGY;

GLASS;

EID: 19944370523     PISSN: 00171050     EISSN: None     Source Type: Journal    
DOI: None     Document Type: Article

References (50)

1. 5 addition on the properties of container glass. Glass Technol., 2004, 45 (6), 255-8.
2. Bingham, P. A. Container glass formulation: a fresh look at an old problem. Glass, 2003, 80 (11), 336.
3. Bingham, P. A. Carbon Trust project reference 2002-6-32-1-3, "Reformulation of container glass for energy efficiency" final project report, November 2003. Available electronically upon request.
4. Good Practice Guide 127, Energy efficient environmental control in the glass industry - revised, Energy Efficiency Best Practice Programme, published by ETSU, Harwell, Didcot, Oxfordshire, OX11 0QJ, UK.
5. Kremer, H., May, F. & Wirtz, S. The influence of furnace design on the NO formation in high temperature processes. Energy Cons. Man., 2001, 42, 1937-52.
6. Stack emissions monitoring in the UK glass industry. Glass, 2004, 81 (4), 106.
7. Integrated pollution prevention and control (IPPC), Secretary of State's guidance for glass manufacturing activities with melting capacity more than 20 tonnes per day, DEFRA, UK, June 2003; http://www.defra.gov.uk/environment/ppc/ laippc/sg2.pdf
8. Simpson, W. Two decades of raw materials development. Glass, 1989, 66 (12), 475-7.
9. Taylor, R. Minor ingredients and their effects on glass melting and properties. Glass Prod. Tech. Int., 1990, 29-36.
10. 3 in container glass. Glass, 1991, 68 (12), 500-3.
11. Kingsnorth, D. J. & Haigh, M. Lithium mineral boosts glass production efficiency. Ceram. Ind., 1990, 134 (10) 33-6.
12. Kingsnorth, D. J. Adding lithium minerals can reduce melting costs. Glass Ind., 1988, 69 (3) 18-25.
13. Meitz, H. Use of spodumene ore as a flux for glass melting. Glass Technol., 1989, 30 (1), 6-9.
14. Simpson, W. Calumite slag as a glassmaking raw material for the increase of furnace productivity. Glass Technol., 1976, 17 (1), 35-40.
15. The Handbook of Glass Manufacture, Third Edition, Ed. F. V. Tooley, Ashlee Publishing Co. Inc., New York, 1984, 3-18.
16. Lyle, A. K. Design and development of glasses for manufacture of containers. Glass Ind., 1967, May, 252.
17. Loesell, R. E. & Lester, W. R. Container glass compositions 1932 to 1960, Glass Ind., 1961, 623.
18. Stadler, L. E. & Cronin, D. Container glass composition, Glass Ind., 1977, December, 10.
19. Stadler, L. E. & Cronin, D. Container glass composition. Part 2. Glass Ind., 1978, January, 10.
20. Smrcek, A. European container glasses 1982 to 1988. Glastech. Ber., 1990, 63 (10), 309-17.
21. Volf, M. B. Chemical Approach to Glass, Elsevier, 1984.
22. 2O-CaO-MgO in the composition range of technical glasses, Glass Technol., 1972, 13 (3), 88-95.
23. Lakatos, T., Johansson, L.-G. & Simmingskold, B. The effect of some components on the viscosity of glass. Glastekn. Tidskr., 1972, 27 (2), 25-8.
24. 3 on the viscosity of soda-lime-silica glass. Glastekn. Tidskr., 1975, 30 (1), 7-8.
25. 3. Glastekn. Tidskr., 1976, 31 (3), 51-4.
26. Rawson, H. Inorganic glass-forming systems. Academic Press, 1967.
27. Combes, J. M. & Sachot, D. Clear glass composition intended for the production of panes, US Patent 5,656,559, Saint-Gobain Vitrage, August 12th 1997.
28. Bonetti, G. A statistical/mathematical and thermodynamic approach to predicting chemical resistance of glass. Riv, Stn. Sper. Vetro, 1985, 15 (3), 111-20.
29. Kasselouri, V., Kouloumbi, N. & Mendrinos, L. Effect of glass melt on corrosion of the lining of an industrial glass furnace, Glass Technol., 2002, 43 (2), 75-9.
30. Pavlovskii, V. K. & Sobolev, Y. S. Effect of temperature on the corrosion of refractories in glass melts (review). Glass Ceram., 1991, 48 (12), 558-61.
31. Technical University of Berlin, Refractory corrosion rates in various glass melts. Glass, 1992, 69 (2), 58-60.
32. Volf, M. B. Mathematical Approach to Glass, Elsevier, 1988.
33. Weyl, W. Coloured Glasses, Society of Glass Technology, 1951.
34. Hayes, R. R., Brewster, S., Webb, B. W., McQuay, M. Q. & Huber, A. M. Crown incident radiant heat flux measurements in an industrial, regenerative, gas-fired, flat-glass furnace. Exp. Therm. Fl. Sci., 2001, 24, 35-46.
35. Bonetti, G. Considerations for ASTM C-829. Liquidus temperature (devitrification curve). Riv. Stn. Sper. Vetro, 1994, 23 (4), 155-69.
36. Bonetti, G. Mathematical methods for calculation of glass properties as a function of composition. Part 3: viscosity. Riv. Stn. Sper. Vetro, 1998, 27 (4), 175-90.
37. Bonetti, G. Mathematical models for calculating the hydrolytic resistance of glass. Riv. Stn. Sper. Vetro, 1995, 24 (3), 107-18.
38. Karlsson, K. H., Backman, R., Cable, M., Peelen, J. & Hermans, J. Estimation of liquidus temperatures in silicate glasses. Glast. Ber. 2001,74 (7), 187-91.
39. Backman, R., Karlsson, K. H., Cable, M. & Pennington, N. P. Model for liquidus temperature of multi-component silicate glasses. Phys. Chem. Glasses, 1997, 38 (3), 103-9.
40. 2O raw materials on glass melting. Glastech. Ber., 1995, 68 (7), 213.
41. Peddle, C. J. The development of various types of glass. Part XI. The effect of the joint presence of sodium and potassium on the solubility of lead glasses. J. Soc. Glass Technol., 1921, 5, T195-201.
42. Morey, G. W. Properties of glass. American Chemical Society, Reinhold Publishing Corp., 1938.
43. 2O at 1470°C. BGIRA Research Report No. 57, 1978.
44. Allison, R. S. & Turner, W. E. S. Further investigations upon the influence of boric oxide on the rate of melting of the batch, and on the rate of refining and of setting of commercial glasses of the soda-lime-silica type. J. Soc. Glass Tech., 1954, 38, T297-364.
45. Walker, G. E. The influence of boric oxide on the crystallisation of a soda-potash-lime-silica glass. J. Soc. Glass Technol., 1945, 29, T38-47.
46. Beerkens, R. C. & Van Limpt, J. Evaporation in industrial glass melt furnaces. Glastech. Ber., 2001, 74 (9), 245-57.
47. Hwang, J.-H., Park, J.-H., Kim, K.-D. & Choi, S.-S. Influence of mixed alkali oxides on some melt properties of TV screen glass. Glastech. Ber., 2000, 73 (1), 8-17.
48. Kazazoglu, E., Albayrak, G. & Yaraman, A. Effect of MgO / CaO ratio on the melting behaviour of soda-lime-silica glasses. Glastech. Ber., 1983, 56K (1), 19-24.
49. UK glass manufacture. A mass balance study. British Glass, 2003. http://www.britglass.co.uk/Files/UKGlassManufactureAMassBalance.pdf
50. Beerkens, R. G. C. The role of gases in glass melting processes. Glastech. Ber., 1995, 68 (12), 369-80.