Framework for Predicting Stress Corrosion Cracking

ASTM Special Technical Publication

Volumn , Issue 1401, 2001, Pages 131-165

  Staehle, Roger W ^a  

^a UNIVERSITY OF MINNESOTA   (United States)

Author keywords

Accelerated testing; Corrosion based design approach; Environmental definition; Failure definition; Locations for analysis matrix; Material definition; Mode definition; Prediction; Statistical definition; Stress corrosion cracking

Indexed keywords

EID: 1942510553     PISSN: 00660558     EISSN: None     Source Type: Conference Proceeding    
DOI: None     Document Type: Article

References (27)

1. Staehle, R. W., "Understanding 'Situation-Dependent Strength' : A Fundamental Objective in Assessing the History of Stress Corrosion Cracking," Environment Induced Cracking of Metals, NACE-10, B. E. Ives and R. Gangloff, Eds., NACE International, Houston, 1990, pp. 561-612.
2. Staehle, R. W. "Environmental Definition," Materials Performance Maintenance, R. W. Revie, V. S. Sastri, M. Elboujdaini, E. Ghali, D. L. Piron, P. R. Roberge and P. Mayer, Eds., Pergamon Press, Ottawa, 1991, pp. 3-43.
3. Cullen, W. H., "Review of IGA, IGSCC and Wastage of Alloys 600 and 690 in High-Temperature Acidified Solutions," Control of Corrosion on the Secondary Side of Steam Generators, R. W. Staehle, J. A. Gorman and A. R. McIlree, Eds., NACE International, Houston, 1996, pp. 273-304.
4. Pourbaix, M. J. N., Thermodynamics of Dilute Aqueous Solutions, Edward Arnold, London, 1949.
5. Spähn, H., Wagner, G. H., and Steinhoff, U., "Stress Corrosion Cracking and Cathodic Hydrogen Embrittlement in the Chemical Industry," Stress Corrosion Cracking and Hydrogen Embrittlement of Iron Base Alloys, NACE-5, R. W. Staehle, J. Hochmann, R. D. McCright and J. E. Slater, Eds., NACE International, Houston, 1977, pp. 80-110.
6. Coriou, H., Grall, L., Olivier, P., and Willermoz, H., "Influence of Carbon and Nickel Content on Stress Corrosion Cracking of Austenitic Stainless Alloys in Pure or Chlorinated Water at 350° C.," Fundamental Aspects of Stress Corrosion Cracking, NACE-1, R. W. Staehle, A. J. Forty, and D. van Rooyen, Eds., NACE International, Houston, 1969, pp. 352-359.
7. Cox, B., "Environmentally Induced Cracking of Zirconium Alloys - A Review," Journal of Nuclear Materials, Vol. 170, No. 1, 1990, pp. 1-23.
8. Speidel, M. O. and Atrens, A., "Stress Corrosion Cracking and Corrosion Fatigue Fracture Mechanics," Corrosion in Power Generating Equipment, Plenum Press, New York, 1984, pp. 85-132.
9. Kerns, G. E., Wang, M., and Staehle, R. W., "Stress Corrosion Cracking and Hydrogen Embrittlement in High Strength Steels," Stress Corrosion Cracking and Hydrogen Embrittlement of Iron Base Alloys, NACE-5, R. W. Staehle, J. Hochmann, R. D. McCright and J. E. Slater, Eds., NACE International, Houston, 1977, pp. 700-735.
10. Latanision, R. M. and Staehle, R. W., "Stress Corrosion Cracking of Iron Nickel Chromium Alloys," Fundamental Aspects of Stress Corrosion Cracking, NACE-1, R. W. Staehle, A. J. Forty and D. van Rooyen, Eds., NACE International, Houston, 1969, pp. 214-307.
11. Steam Generator Owners Group, Steam Generator Reference Book, EPRI, Palo Alto, 1985.
12. Pickering, H. W., Beck, F. H., and Fontana, M. G., "Wedging Action of Solid Corrosion Product During Stress Corrosion of Austenitic Stainless Steels," Corrosion Journal, Vol. 18, 1962, pp. 230-239.
13. Staehle, R. W. "Lifetime Prediction of Materials in Environments," Uhlig's Corrosion Handbook, 2nd edition, R. W. Revie, Ed., John Wiley and Sons, New York, 2000.
14. Staehle, R. W., "Lifetime Prediction," Proceedings: Corrosion and Its Control in the New Millennium, R. W. Revie and I. Al-Tai, Meeting Chairmen, NACE International Northern Area Eastern Conference and Exhibition, Ottawa, Ontario, Canada, October 24-27, 1999.
15. Staehle, R. W., "Combining Design and Corrosion for Predicting Life," presented as a plenary lecture at Life Prediction of Corrodible Structures, NACE International, Houston, 1994, pp. 138-291.
16. Wang , M. T. and Staehle, R. W., "Effect of Heat Treatment and Stress Intensity Parameters on Crack Velocity and Fractography of AISI 4340 Steel," L'Hydrogene Dans Les Metaux, Vol. 2, Editions Science et Industrie, Paris, 1972, pp. 342-349.
17. Copson, H. R., "Effect of Composition on Stress Corrosion Cracking of Some Alloys Containing Nickel," Physical Metallurgy of Stress Corrosion Fracture, T. Rhodin, Ed., Interscience, New York, 1959, pp. 247-269.
18. Thompson, D. H. and Tracy, A. W., "Influence of Composition on Stress-Corrosion Cracking of Some Copper-Base Alloys," Journal of Metals, Vol. 1, No. 2, 1949, pp. 100-109.
19. Berge, P., "Importance of Surface Preparation for Corrosion Control in Nuclear Power Stations," Materials Performance, Vol. 11, 1997, pp. 56-62.
20. Stachle, R. W. and Gorman, J. A., "Development and Application of Intensity and Operating Diagrams for Predicting the Occurrence and Extent of Stress Corrosion Cracking," Corrosion Science and Engineering: Proceedings of an International Symposium in Honour of Marcel Pourbaix's 85th birthday, Rapports Techniques Vol. 157-158, CEBELCOR, Brussels, 1989, pp. 199-209.
21. Stachle, R. W., "Development and Application of Corrosion Mode Diagrams," Parkins Symposium on Stress Corrosion Cracking, S. M. Bruemmer, E. I. Meletis, R. H. Jones, W. W. Gerberich, F. P. Ford, and R. W. Stachle, Eds., TMS, Warrendale, Pennsylvania, 1992, pp. 199-209.
22. Shibata, T., "1996 W. R. Whitney Award Lecture: Statistical and Stochastic Approaches to Localized Corrosion," Corrosion Journal, Vol. 52, No. 11, 1996, pp. 813-830.
23. Nelson, W., Accelerated Testing: Statistical Models, Test Plans, and Data Analyses, John Wiley and Sons, New York, 1990.
24. Abernethy, R. B., The New Weibull Handbook, Second Edition, R. B. Abernethy Publisher, North Palm Beach, Florida, 1996.
25. Stachle, R. W., Gorman, J. A., Stavropoulos, K. D., and Welty, C. S., Jr., "Application of Statistical Distributions to Characterizing and Predicting Corrosion of Tubing in Steam Generators of Pressurized Water Reactors," Life Prediction of Corrodible Structures, Proceedings of the 3rd International Relations Committee Symposium, NACE International, Houston, 1994, pp. 1374-1399.
26. Jacko, R. J., "Corrosion Evaluation of Thermally Treated Alloy 600 in Primary and Faulted Secondary Water Environments," EPRI NP-6721-SD, EPRI, Palo Alto, 1990.
27. Eason, E. D. and Shusto, L. M., Analysis of Cracking in Small-Diameter BWR Piping, NP-4394, EPRI, Palo Alto, 1986.