Influence of spent catalyst used for catalytic cracking in a fluidized bed on sulphate corrosion of cement mortars: I. Na2SO4 medium

Cement and Concrete Research

Volumn 34, Issue 5, 2004, Pages 759-767

  Bukowska, Maria ^a   Pacewska, Barbara ^a   Wilińska, Iwona ^a  

^a WARSAW UNIVERSITY OF TECHNOLOGY   (Poland)

Author keywords

Pozzolan; Sulphate attack; Waste catalyst

Indexed keywords

ADDITIVES; COMPRESSIVE STRENGTH; CORROSION; FLUID CATALYTIC CRACKING; FLUIDIZED BEDS; MORTAR; POZZOLAN; SAND; SODIUM COMPOUNDS; STANDARDS;

CORROSION DAMAGE; SULFATE ATTACK; SUPERPLASTICIZERS; WASTE CATALYSTS;

CEMENTS;

EID: 1942503973     PISSN: 00088846     EISSN: None     Source Type: Journal    
DOI: 10.1016/j.cemconres.2003.08.007     Document Type: Article

References (23)

1. Su N., Fang H.-Y., Chen Z.-H., Liu F.-S. Reuse of waste catalysts from petrochemical industries for cement substitution. Cem. Concr. Res. 30:2000;1773-1783.
2. Paya J., Monzo J., Borrachero M.V. Fluid catalytic cracking catalyst residue (FC3R): an excellent mineral by-product for improving early-strength development of cement mixtures. Cem. Concr. Res. 29:1999;1773-1779.
3. Pacewska B., Bukowska M., Wilińska I., Swat M. Modification of the properties of concrete by a new pozzolan - a waste catalyst from the catalytic process in a fluidized bed. Cem. Concr. Res. 32:2002;145-152.
4. Su N., Chen Z.-H., Fang H.-Y. Reuse of spent catalyst as fine aggregate in cement mortar. Cem. Concr. Compos. 23:2001;111-118.
5. Paya J., Monzo J., Borrachero M.V. Physical, chemical and mechanical properties of fluid catalytic cracking catalyst residue (FC3R) blended cements. Cem. Concr. Res. 31:2001;57-61.
6. Swat M., Kubissa J., Kubissa W. Spent catalyst as highly effective additive for concrete. Inż. Bud. 4:1997;180-181.
7. Bukowska M., Pacewska B., Wilińska I., Swat M. Effect of saturated brine medium on the properties of Portland cement concretes and mortars dosed with zeolite aluminosilicate. XII Konferencja Naukowo Techniczna KONTRA'2000, Warszawa-Zakopane, maj. 2000;35-42.
8. Kurdowski W. The Chemistry of Cement. 1991;PWN, Warszawa.
9. Pacewska B., Wilińska I., Bukowska M. Hydration of cement slurry in the presence of spent cracking catalyst. J. Therm. Anal. Calorim. 60:2000;71-78.
10. Khatib J.M., Wild S. Sulphate resistance of metakaolin mortar. Cem. Concr. Res. 28:1998;83-92.
11. Czarnecki L., Mierzwa J. Sulphate corrosion of concrete - an intensity of aggressive environment influence. XI Konferencja Naukowo Techniczna KONTRA'98, Warszawa-Zakopane, maj. 1998;71-78.
12. Gruener M. Corrosion and Corrosion - Protection of Concrete. 1983;Arkady, Warszawa.
13. Gollop R.S., Taylor H.F.W. Microstructural and microanalytical studies of sulfate attack: III. Sulfate-resisting Portland cement: reactions with sodium and magnesium sulfate solutions. Cem. Concr. Res. 25:1995;1581-1590.
14. Gollop R.S., Taylor H.F.W. Microstructural and microanalytical studies of sulfate attack: IV. Reactions of a slag cement paste with sodium and magnesium sulfate solutions. Cem. Concr. Res. 26:1996;1013-1028.
15. Bensted J. The chemistry of efflorescence. Cement, Wapno, Beton. (4):2001;133-142.
16. Irassar E.F., Di Maio A., Batic O.R. Sulfate attack on concrete with mineral admixtures. Cem. Concr. Res. 26:1996;113-123.
17. Rendell F., Jauberthie R. The deterioration of mortar in sulphate environments. Constr. Build. Mater. 13:1999;321-327.
18. Akoz F., Turker F., Koral S., Yuzer N. Effects of raised temperature of sulfate solutions on the sulfate resistance of mortars with and without silica fume. Cem. Concr. Res. 29:1999;537-544.
19. Miletić S., Ilić M., Ranogajec J., Marinović-Neducin M., Djurić M. Portland ash cement degradation in ammonium-sulfate solution. Cem. Concr. Res. 28:1998;713-725.
20. Turker F., Akoz F., Koral S., Yuzer N. Effects of magnesium sulfate concentration on the sulfate resistance of mortars with and without silica fume. Cem. Concr. Res. 27:1997;205-214.
21. Garbacik A., Chładzyński S. Standardisation aspects of determination of the cement resistance to sulphate attack. XI Konferencja Naukowo Techniczna KONTRA'98, Warszawa-Zakopane, maj. 1998;107-115.
22. PN-EN 196-1, Methods of testing cement: Part 1. Determination of strength (1994).
23. O'Farrel M., Wild S., Sabir B.B. Pore size distribution and compressive strength of waste clay brick mortar. Cem. Concr. Compos. 23:2001;81-91.