Ductile crack initiation behavior in steels with compressive prestrain

Journal of Marine Science and Technology

Volumn 10, Issue 1, 2005, Pages 41-52

  Enami, Keitaro ^a  

^a NATIONAL INSTITUTE FOR MATERIALS SCIENCE   (Japan)

Author keywords

Compressive prestrain; Ductile crack initiation; Equivalent plastic strain; Reversed bending test; Stress triaxiality

Indexed keywords

BENDING (DEFORMATION); CRACK INITIATION; DUCTILITY; FINITE ELEMENT METHOD; PLASTICITY; STRAIN; STRESS ANALYSIS;

COMPRESSIVE PRESTRAIN; DUCTILE CRACK INITIATION; EQUIVALENT PLASTIC STRAIN; REVERSED BENDING TESTS; STRESS TRIAXIALITY;

STEEL;

EID: 17444411962     PISSN: 09484280     EISSN: None     Source Type: Journal    
DOI: 10.1007/s00773-004-0187-5     Document Type: Article

References (15)

1. Inoue H, Maenaka H, Sakuma M (1986) Effects of compressive prestrain on fracture toughness (in Japanese). J Soc Nav Archit Jpn 160:450-460
2. Yamamoto M, Yajima H, Matsuoka K, et al (2002) Crack initiation strength of structural steel members having experienced large compressive strain due to buckling deformation (5th report) (in Japanese). J Soc Nav Archit Jpn 192:611-617
3. Teraoka M, Shimanuki H, Morita K, et al (1996) An investigation and analysis on a nine-storey steel building damaged by the 1995 Hyogoken-nanbu earthquake (in Japanese). JSSC Steel Const Eng 3:21-34
4. Okashita K, Ohmichi R, Michiba K, et al (1998) Investigation of the brittle fracture at the corner of a P75 rigid-frame pier in Kobe harbor highway during the Hyogoken-nanbu earthquake (in Japanese). J Struc Mech Eq Eng 591:243-261
5. Mackenzie AC, Hancock JW, Brown DK (1977) On the influence of state of stress on ductile failure initiation in high-strength steels. Eng Fract Mech 9:167-188
6. Hancock JW, Mackenzie AC (1976) On the mechanisms of ductle failure in high-strength steels subjected to multi-axial stress-states. J Mech Phys Solids 24:147-169
7. McClintock FA (1968) A criterion for ductile fracture by the growth of holes. ASME J Appl Mech 35:363-371
8. Rice JR, Tracey DM (1969) On the ductile enlargement of voids in triaxial stress fields. J Mech Phys Solids 17:201-217
9. Shimanuki H, Furuya H, Inoue T, et al (1999) Effect of stress triaxiality and strain rate on ductile fracture initiation in steel (in Japanese). J Soc Nav Archit Jpn 186:475-483
10. Knott JF (1966) Some effects of hydrostatic tension on the fracture behaviour of mild steel. J Iron Steel Inst 204:104-111
11. Knott JF(1967) Effects of strain on notch brittleness in mild steel. J Iron Steel Inst 205:966-969
12. Beremin FM (1983) A local criterion for cleavage fracture of a nuclear pressure vessel. Metal Trans A 14A:2277-2287
13. Tagawa T, Itoh A, Miyata T (1996) Quantitative prediction of embrittlement due to pre-strain for low carbon steels (in Japanese). Q J Jpn Weld Soc 14:429-434
14. An GB, Yoshida S, Ohata M, et al (2001) Strength mismatch effect on ductile crack initiation from notch root of structural steel (in Japanese). J Soc Nav Archit Jpn 190:579-590
15. Ishikawa N, Kobayashi Y, Kurihara M, et al (1999) Ductile crack initiation behavior of structural steel under cyclic loading (in Japanese). Tetsu-to-Hagane 85:71-77