Hydrogen effects during SCC propagation of Al-5Mg in 30g/l NaCl solutions

Materials Science Forum

Volumn 331, Issue , 2000, Pages

  Tanguy, D ^a,b   Bayle, B ^b   Dif, R ^a   Magnin, T ^b  

^a ALCAN INTERNATIONAL LIMITED   (Canada)

^b ECOLE DES MINES DE SAINT ETIENNE   (France)

Author keywords

[No Author keywords available]

Indexed keywords

ABSORPTION; CRACK PROPAGATION; CRYSTAL DEFECTS; DISSOLUTION; GRAIN BOUNDARIES; HYDROGEN; RECRYSTALLIZATION (METALLURGY); SODIUM CHLORIDE; SOLUTIONS; STRESS CORROSION CRACKING;

ANODIC DISSOLUTION REACTION; FAST INTERGRANULAR PROPAGATION; HYDROGEN EFFECTS; THIN NOTCHES;

ALUMINUM ALLOYS;

EID: 17044452278     PISSN: 02555476     EISSN: None     Source Type: Conference Proceeding    
DOI: None     Document Type: Article

References (7)

1. E.H. Hollinsworth and H.Y. Hunsicker. « Metals Handbook vol. 13 ». ASM, Metals Park, Ohio, (1987)
2. R. Dif, T. Warner and G.M. Raynaud. Proceedings of ICAA-6. Aluminium Alloys, vol. 3 (1998), p. 1615.
3. M.C. Reboul, Th. Magnin, T.J. Warner. Proceedings of ICAA-3. vol. 2 (1992), p. 453.
4. I.L. Rosenfeld and I.K. Marshakov. Corrosion 20, (1964), p. 115t.
5. T. Magnin, A. Chambreuil and B. Bayle, Acta. Mater. 44, No. 4 (1996), p. 1457.
6. N.J.H. Holroyd. Proceedings of « Environment-induced Cracking of Metals », NACE (1989), p. 311.
7. R.A.H. Edwards. « The Electrochemical Conditions inside Stress Corrosion and Corrosion Fatigue Cracks ». Thesis, Delft University of Technology, Departement of Metallurgy, (1986)