A numerical approach to separate the modes of fracture in interface crack propagation

Journal of Composite Materials

Volumn 39, Issue 3, 2005, Pages 247-264

  Mathews, Mary J ^a   Swanson, Stephen R ^a  

^a Department of Electrical and Computer Engineering   (United States)

Author keywords

Delamination; Interface cracks; Modes of fracture

Indexed keywords

DELAMINATION; FRACTURE; FRACTURE TOUGHNESS; INTERFACES (MATERIALS); MATHEMATICAL MODELS; NUMERICAL ANALYSIS; PROBLEM SOLVING;

ENERGY RELEASE; INTERFACE CRACKS; MATERIAL PROPERTY; MODES OF FRACTURE;

CRACK PROPAGATION;

EID: 17044439568     PISSN: 00219983     EISSN: None     Source Type: Journal    
DOI: 10.1177/0021998305046449     Document Type: Article

References (44)

1. Garg, A.C. (1988). Delaminations - A Damage Mode in Composite Structures, Engineering Fracture Mechanics, 29(5): 557-584.
2. O'Brien, T.K. (1984). Mixed-mode Strain-energy Release Rate Effects on Edge Delamination of Composites, In: Effects of Defects in Composite Materials, ASTM STP 836, pp. 125-142, American Society for Testing and Materials.
3. IIc: Shear Measurement or Sheer Myth?, In: Bucinell, R.B. (ed.) Composite Materials: Fatigue and Fracture, Vol. 7, ASTM STP 1330, pp. 3-18, American Society for Testing and Materials, Philadelphia.
4. Reeder, J.R. and Crews Jr., J.H. (1991). Nonlinear Analysis and Redesign of the Mixed-mode Bending Delamination Test, NASA Technical Memorandum 102777.
5. Benzeggagh, M.L. and Kanane, M. (1996). Measurement of Mixed-mode Delamination Fracture Toughness of Unidirectional Glass/Epoxy Composites with Mixed-Mode Bending Apparatus, Composite Science and Technology, 56: 439-449.
6. O'Brien, T.K. (1984). Characterization of Delamination Onset and Growth in a Composite Laminate, In: Reifsnider K.L. (ed.) Damage in Composite Materials, ASTM STP 775, pp. 140-167, American Society for Testing and Materials, Philadelphia.
7. s Graphite/Epoxy Composite Laminates, Effects of Defects in Composite Materials, ASTM STP 836, pp. 143-160, American Society for Testing and Materials, Philadelphia.
8. Lee, S.M. (1990). Failure Mechanisms of Edge Delaminations of Composites, Journal of Composite Materials, 24: 1200-1212.
9. Pagano, N.J. and Schoeppner, A. (2000). Delamination of Polymer Matrix Composites: Problems and Assessment, In: Kelly, A. and Zweben, C. (eds), Comprehensive Composite Materials, Vol. 2, pp. 433-528, Oxford, Amsterdam, New York.
10. Tay, T. (2003), Characterization and Analysis of Delamination Fracture in Composites: An Overview of Developments from 1990 to 2001, Appl. Mech. Rev., 56 (1): 1-32.
11. Standard Test Method for Mode I Interlaminar Fracture Toughness of Unidirectional Fiber Reinforced Polymer Matrix Composites (1994). ASTM Standard D 5528-94a, In: ASTM Annual Book of Standards, 15.03, pp. 272-281.
12. Russell, A.J. (1991). Initiation and Growth of Mode II Delamination In Toughened Composites, In: O'Brien, T.K. (ed.) Composite Materials: Fatigue and Fracture, Vol. 3, ASTM STP 1110, pp. 226-242, American Society for Testing and Materials, Philadelphia.
13. Standard Test Method for Mixed Mode I - Mode II Interlaminar Fracture Toughness of Unidirectional Fiber Reinforced polymer Matrix Composites (1994). ASTM Standard D 6671-01, ASTM Annual Book of Standards, 15.03, pp. 392-402.
14. Reeder, J.R. and Crews Jr., J.H. (1992). Redesign of the Mixed-Mode Bending Delamination Test to Reduce Nonlinear Effects, Journal of Composites Technology and Research, 14: 12-19.
15. Rice, J.R. (1988). Elastic Fracture Mechanics Concepts for Interfacial Cracks, J. Applied Mechanics, 55: 98-103.
16. Comninou, M. (1990). An Overview of Interface Cracks, Eng. Fracture Mech., 37: 197-208.
17. Hutchison, J.W. and Suo, Z. (1991). Mixed Mode Cracking in Layered Materials, Advances in Applied Mechanics, 29: 63-191.
18. Williams, M.L. (1959). The Stresses Around a Fault or Crack in Dissimilar Media, Bulletins of the Seismological Society of America, 49(2): 199-204.
19. Rice, J.R. and Sih, G.C. (1965). Plane Problems of Cracks in Dissimilar Media, J of Applied Mechanics, 32: 418-423.
20. Erdogan, A.H. (1965). Stress Distribution in Bonded Dissimilar Materials with Cracks, Journal of Applied Mechanics, 32: 403-410.
21. England, A.H. (1965). A Crack between Dissimilar Media, Journal of Applied Mechanics, 32: 400-402.
22. Toya, M. (1992). On Mode I and Mode II Energy Release Rates of an Interface Crack, Intl. J. Fracture, 56: 345-352.
23. Comninou, M. (1977). The Interface Crack, Journal of Applied Mechanics, 44: 631-636.
24. Comninou, M. (1979). The Interface Crack in Combined Tension-Compression and Shear Field, Journal of Applied Mechanics, TRANS. ASME, 46: 345-348.
25. Atkinson, C. (1977). On Stress Singularities and Interfaces in Linear Elastic Fracture Mechanics, International Journal of Fracture, 13(6): 807-819.
26. Chen, E.P. (1985). Finite Element Analysis of a Bi-Material Interface Crack, Theoretical and Applied Fracture Mechanics, 3: 257-262.
27. Sun, C.T. and Jih, C.J. (1987). On Strain Energy Release Rates for Interfacial Cracks in Bi-Material Media, Engineering Fracture Mechanics, 28(1): 13-20.
28. Schoeppner, G.A. and Pagano, N.J. (1998), Stress Fields and Energy Release Rates in Cross-ply Laminates, International Journal of Solids and Structures, 15(11): 1025-1055.
29. Camanho, P.P., Dávila, C.G. and Moura, M.F. (2003), Numerical Simulation of Mixed-Mode Progressive Delamination in Composite Materials, Journal of Composite Materials, 37(16): 1415-1438.
30. Beuth, J.L. (1996). Separation of Crack Extension Modes in Orthotropic Delamination Models, International Journal of Fracture, 77: 305-321.
31. Qian, W. and Sun, C.T. (1998). Methods for Calculating Stress Intensity Factors for Interfacial Cracks between Two Orthotropic Solids, International Journal of Solids and Structures, 35 (25): 3317-3330.
32. O'Brien, T.K. (1998). Interlaminar Fracture Toughness: The Long and Winding Road to Standardization, Composites Part B, 29 (B): 57-62.
33. O'Brien, T.K., Murri, G.B. and Salpekar, S.A. (1989). Interlaminar Shear Fracture Toughness and Fatigue Thresholds for Composite Materials, In: Lagace, P.A. (ed.), Composite Materials: Fatigue and Fracture, Vol. 2, ASTM STP 1012, pp. 222-250, American Society for Testing and Materials, Philadelphia.
34. Davies, P. (1989). Aspects of Delamination Failure in Thermoplastic Composites, In: Armanios, E.A. (ed.), Interlaminar Fracture of Composites, pp. 225-235, Trans Tech Publications, Vermont.
35. Bradley, W.L. (1989). Understanding the Translation of Neat Resin Toughness into Delamination Toughness in Composites, In: Armanios, E.A. (ed.), Interlaminar Fracture of Composites, pp. 225-235, Trans Tech Publications, Vermont.
36. Smiley, A.J. and Pipes, R.B. (1991). Rate Effects on Mode I Interlaminar Fracture Toughness in Composite Materials, Delamination in Advanced Composites, pp. 318-335, Technomic Publishing Co., Pennsylvania.
37. Raju, I.S., Crews Jr., J.H. and Aminpour, M.A. (1988). Convergence of Strain Energy Release Rate Components for Edge-Delaminated Composite Laminates, Engineering Fracture Mechanics, 30(3): 383-396
38. Dattaguru, B., Venkatesha, K.S., Ramamurthy, T.S. and Buchholz, F.G. (1994). Finite Element Estimates of Strain Energy Release Rate Components at the Tip of an Interface Crack under Mode I Loading, Engineering Fracture Mechanics, 49 (3): 451-463.
39. Jones, R., Paul, J., Tay, T.E. and Williams, J.F. (1988). Assessment of the Effect of Impact Damage in Composites, Composite Structures, 10: 51-73.
40. Rybicki, E.F. and Kanninen, M.F. (1977). A Finite Element Calculation of Stress Intensity Factors by a Modified Crack Closure Integral, Engineering Fracture Mechanics, (9): 931-938.
41. Swanson, S.R. (1997). Introduction to Design and Analysis with Advanced Composite Materials, Prentice Hall, New Jersey.
42. Kanninen, M.F. (1973). An Augmented Double Cantilever Beam Model for Studying Crack Propagation and Arrest, International Journal of Fracture, 9: 83-92.
43. Cann, M.T. (2004). An Empirical and Analytical Investigation of the Cure Related Distortion of Flat Composite Laminates, PhD Dissertation, Department of Mechanical Engineering, University of Utah, Salt Lake City, Utah-84112.
44. Venkatesha, Ramamurthy, T.S. and Dattaguru, B. (1998). A Study of the Behavior of Subinterface Cracks in Bimaterial Plates, Engineering Fracture Mechanics, 59:241-252.