Evaluation of residual stress relief of aluminum alloy 7050 by using crack compliance method

Transactions of Nonferrous Metals Society of China (English Edition)

Volumn 13, Issue 5, 2003, Pages 1190-1193

  Wang, Qiu Cheng ^a,b   Ke, Ying Lin ^b   Xing, Hong Yan ^a   Weng, Ze Yu ^a   Yang, Fang Er ^a  

^a ZHEJIANG UNIVERSITY OF TECHNOLOGY   (China)

^b ZHEJIANG UNIVERSITY   (China)

Author keywords

Aluminum alloy; Crack compliance method; Evaluation; Residual stress; Stress relief

Indexed keywords

CRACKS; EVALUATION; HEAT TREATMENT; RESIDUAL STRESSES; STRESS RELIEF;

CRACK COMPLIANCE METHOD; SOLUTION HEAT TREATMENT;

ALUMINUM ALLOYS;

EID: 1642417824     PISSN: 10036326     EISSN: None     Source Type: Journal    
DOI: None     Document Type: Article

References (10)

1. WANG Qiu-cheng, KE Ying-lin. Prediction of residual stress-induced warpage while machining aircraft monolithic parts[A]. CHEN Ding-chang, Narutaki N, Yamane Y, et al. Proc 6th Int Conf on Progress of Machining Technology[C]. Beijing: Aviation Industry Press, 2002. 707-710.
2. WANG Qiu-cheng, KE Ying-lin. Control and relief of residual stresses in high-strength aluminum alloy parts for aerospace industry[J]. Journal of Aeronautical Materials, 2002, 22(3): 59-62. (in Chinese)
3. Davis J R, Davidnson G M, Lampman S R, et al. ASM Handbook(Vol.4)-Heat Treating[M]. USA: ASM International, 1995. 841-879.
4. Escobar K, Gonzalez B, Ortiz J, et al. On the residual stress control in aluminum alloy 7050[J]. Mater Sci Forum, 2002, 396-402: 1235-1240.
5. Tanner D A, Robinson J S, Cudd R L. Cold compression residual stress reduction in aluminum alloy 7010[J]. Mater Sci Forum, 2000, 347-349: 235-240.
6. Prime M B. Residual stress measurement by successive extension of a slot: the crack compliance method[J]. Applied Mechanics Reviews, 1999(2): 75-96.
7. Cheng W, Finnic I. An overview of the crack compliance method for residual stress measurement[A]. SEM. Proc of 4th Int Conf on Residual Stress (ICRS-4)[C]. Baltimore, USA: Society for Experimental Mechanics, 1994. 449-458.
8. WANG Qiu-cheng, KE Ying-lin, ZHANG Qiao-fang. Evaluation of residual stress depth profiling in 7075 aluminum alloy plates[J]. ACTA Aeronautica et Astronautica Sinica, 2003, 24(4): 336-338. (in Chinese).
9. Prime M B, Hill M R. Residual stress, stress relief, and inhomogeneity in aluminum plate[J]. Scripta Materialia, 2002, 46(1): 77-82.
10. Totten G E, Mackenzie D S. Aluminum quenching technology: a review[C]. Mater Sci Forum, 2000, 331-337: 589-594.