Volumn 27, Issue 7, 2005, Pages 773-782

Abnormal near-threshold fatigue crack propagation of Ti alloys: Role of the microstructure

Author keywords

Crack propagation; Fatigue; Mean stress; Microstructure; Threshold; Titanium alloys

Indexed keywords

CRACKS; FATIGUE OF MATERIALS; FRACTURE TOUGHNESS; GRAIN BOUNDARIES; HYDROGEN; MICROSTRUCTURE; STRESSES; TITANIUM ALLOYS; VOLUME FRACTION;

EID: 16244363312     PISSN: 01421123     EISSN: None     Source Type: Journal    
DOI: 10.1016/j.ijfatigue.2005.01.008     Document Type: Article
Times cited : (11)

References (38)
  • 1
    • 0000620435 scopus 로고    scopus 로고
    • Lütjering G, et al, editors NY, USA: Pergamon Press
    • Marci G. In: Lütjering G, et al, editors. Failure mode below 390 K with IMI834. Fatigue 96, vol. 1. NY, USA: Pergamon Press; 1996. p. 493-498.
    • (1996) Failure Mode below 390 K with IMI834. Fatigue 96 , vol.1 , pp. 493-498
    • Marci, G.1
  • 2
    • 0031543178 scopus 로고    scopus 로고
    • Abnormal da/dN-ΔK curves: New failure mode with Ti-alloys
    • G. Marci Abnormal da/dN-ΔK curves: new failure mode with Ti-alloys Mat-wiss u Werkstofftech 28 1997 51 58
    • (1997) Mat-wiss U Werkstofftech , vol.28 , pp. 51-58
    • Marci, G.1
  • 3
    • 0032070206 scopus 로고    scopus 로고
    • Fatigue crack propagation threshold: 'What is it and how is it measured?'
    • G. Marci Fatigue crack propagation threshold: 'what is it and how is it measured?' J Test Eval 3 1998 220 223
    • (1998) J Test Eval , vol.3 , pp. 220-223
    • Marci, G.1
  • 4
    • 0033338223 scopus 로고    scopus 로고
    • Explanation of an apparent abnormality in fatigue crack growth rate curves in titanium alloys
    • M. Lang Explanation of an apparent abnormality in fatigue crack growth rate curves in titanium alloys Acta Mater 11 1999 3247 3261
    • (1999) Acta Mater , vol.11 , pp. 3247-3261
    • Lang, M.1
  • 5
    • 0032058308 scopus 로고    scopus 로고
    • Investigation of an abnormality in fatigue crack growth curves - The Marci effect
    • M. Lang, G.A. Hartman, and J.M. Larsen Investigation of an abnormality in fatigue crack growth curves - the Marci effect Scripta Mater 12 1998 1803 1810
    • (1998) Scripta Mater , vol.12 , pp. 1803-1810
    • Lang, M.1    Hartman, G.A.2    Larsen, J.M.3
  • 6
    • 0030871178 scopus 로고    scopus 로고
    • Atmospheric influence on fatigue crack propagation in titanium alloys at elevated temperature
    • Piascik RS, Saxena A, Gangloff RP, editors ASTM STP 1297. American Society for Testing Materials
    • Sarrazin C, Lesterlin S, Petit J. Atmospheric influence on fatigue crack propagation in titanium alloys at elevated temperature. In: Piascik RS, Saxena A, Gangloff RP, editors. Elevated temperature effects on fatigue and fracture, ASTM STP 1297. American Society for Testing Materials; 1997 p. 117-139.
    • (1997) Elevated Temperature Effects on Fatigue and Fracture , pp. 117-139
    • Sarrazin, C.1    Lesterlin, S.2    Petit, J.3
  • 7
    • 0033907589 scopus 로고    scopus 로고
    • Mean stress and environment effects on near-threshold fatigue crack propagation on a Ti6246 alloy at room temperature and 500 °c
    • J.C. Newman Jr R.S. Piasick
    • C. Sarrazin-Baudoux, Y. Chabanne, and J. Petit Mean stress and environment effects on near-threshold fatigue crack propagation on a Ti6246 alloy at room temperature and 500 °C J.C. Newman Jr R.S. Piasick ASTM STP 1372 2000 341 360
    • (2000) ASTM STP 1372 , pp. 341-360
    • Sarrazin-Baudoux, C.1    Chabanne, Y.2    Petit, J.3
  • 8
    • 0032630276 scopus 로고    scopus 로고
    • Influence of environment and of mean stress on fatigue crack growth at near-threshold stress intensities on a Ti6246 alloy at room temperature and 500 °c
    • C. Sarrazin-Baudoux, Y. Chabanne, and J. Petit Influence of environment and of mean stress on fatigue crack growth at near-threshold stress intensities on a Ti6246 alloy at room temperature and 500 °C Scripta Mater 4 1999 451 457
    • (1999) Scripta Mater , vol.4 , pp. 451-457
    • Sarrazin-Baudoux, C.1    Chabanne, Y.2    Petit, J.3
  • 9
    • 0032208389 scopus 로고    scopus 로고
    • Subcritical crack growth of Ti-6Al-4V at room temperature under high stress ratio loading
    • J.P. Thomas Subcritical crack growth of Ti-6Al-4V at room temperature under high stress ratio loading Scripta Mater 12 1998 1647 1652
    • (1998) Scripta Mater , vol.12 , pp. 1647-1652
    • Thomas, J.P.1
  • 10
    • 0033906901 scopus 로고    scopus 로고
    • max on fatigue crack growth threshold in aluminium alloys
    • J.C. Newman R.S. Piasick
    • max on fatigue crack growth threshold in aluminium alloys J.C. Newman R.S. Piasick ASTM STP 1372 2000 63 77
    • (2000) ASTM STP 1372 , pp. 63-77
    • Newman, J.A.1    Ridell, W.T.2    Piasick, R.S.3
  • 12
    • 0021479910 scopus 로고
    • Influence of texture on fatigue properties of Ti-Al-4V
    • M. Peters, A. Gysler, and G. Lütjering Influence of texture on fatigue properties of Ti-Al-4V Met Trans 15A 1984 1597 1605
    • (1984) Met Trans , vol.15 , pp. 1597-1605
    • Peters, M.1    Gysler, A.2    Lütjering, G.3
  • 13
    • 0018027104 scopus 로고
    • Fatigue crack propagation resistance of beta-annealed Ti-6Al-4V alloys of differing interstitial contents
    • G.R. Yoder, L.A. Cooley, and T.W. Crooker Fatigue crack propagation resistance of beta-annealed Ti-6Al-4V alloys of differing interstitial contents Met Trans 9A 1978 1413 1420
    • (1978) Met Trans , vol.9 , pp. 1413-1420
    • Yoder, G.R.1    Cooley, L.A.2    Crooker, T.W.3
  • 14
    • 0032208389 scopus 로고    scopus 로고
    • Subcritical crack growth of Ti-6Al-4V at room temperature under high stress ratio loading
    • J.P. Thomas Subcritical crack growth of Ti-6Al-4V at room temperature under high stress ratio loading Scripta Mater 12 1998 1647 1652
    • (1998) Scripta Mater , vol.12 , pp. 1647-1652
    • Thomas, J.P.1
  • 15
    • 0042261209 scopus 로고    scopus 로고
    • Mechanisms of primary creep in α/β titanium alloys at lower temperatures
    • S. Suri, T. Neeraj, G.S. Daehn, D.H. Hou, J.M. Scott, and R.W. Hayes Mechanisms of primary creep in α/β titanium alloys at lower temperatures Mater Sci Eng A234-236 1997 996 999
    • (1997) Mater Sci Eng , vol.A234-236 , pp. 996-999
    • Suri, S.1    Neeraj, T.2    Daehn, G.S.3    Hou, D.H.4    Scott, J.M.5    Hayes, R.W.6
  • 17
    • 0019397858 scopus 로고
    • Subcritical crack-growth under sustained load in Ti-6-Al-6V-2Sn
    • S.M.L. Sastry, R.J. Lederich, and B.B. Rath Subcritical crack-growth under sustained load in Ti-6-Al-6V-2Sn Met Trans A 12(A) 1981 83 94
    • (1981) Met Trans A , vol.12 , pp. 83-94
    • Sastry, S.M.L.1    Lederich, R.J.2    Rath, B.B.3
  • 18
    • 0020100698 scopus 로고
    • Temperature dependence of sustained-load subcritical crack growth in Ti-6Al-6V-2Sn
    • R.J. Lederich, S.M.L. Sastry, and P.S. Pao Temperature dependence of sustained-load subcritical crack growth in Ti-6Al-6V-2Sn Met Trans A 13(A) 1982 497 500
    • (1982) Met Trans A , vol.13 , pp. 497-500
    • Lederich, R.J.1    Sastry, S.M.L.2    Pao, P.S.3
  • 19
    • 0016128370 scopus 로고
    • Effect of hydrogen on fracture and inert-environment sustained load cracking resistance of α/β titanium alloys
    • D.A. Meyn Effect of hydrogen on fracture and inert-environment sustained load cracking resistance of α/β titanium alloys Met Trans 5 1974 2405 2413
    • (1974) Met Trans , vol.5 , pp. 2405-2413
    • Meyn, D.A.1
  • 20
    • 0031370254 scopus 로고    scopus 로고
    • Dwell sensitive fatigue in a near alpha titanium alloy at ambient temperature
    • M.R. Bache, M. Cope, H.M. Davies, W.J. Evans, and G. Harrison Dwell sensitive fatigue in a near alpha titanium alloy at ambient temperature Int J Fatigue 19 1 1997 S83 S88
    • (1997) Int J Fatigue , vol.19 , Issue.1
    • Bache, M.R.1    Cope, M.2    Davies, H.M.3    Evans, W.J.4    Harrison, G.5
  • 22
  • 23
    • 0018683114 scopus 로고
    • The effect of hold time on the fatigue properties of a β-processed titanium alloy
    • W.J. Evans, and C.R. Gostelow The effect of hold time on the fatigue properties of a β-processed titanium alloy Metall Trans 10(A) 1979 1837 1846
    • (1979) Metall Trans , vol.10 , pp. 1837-1846
    • Evans, W.J.1    Gostelow, C.R.2
  • 24
    • 0024089101 scopus 로고    scopus 로고
    • Dwell time effects on the fatigue behavior of titanium alloys
    • Z. Song, and D.W. Hoeppner Dwell time effects on the fatigue behavior of titanium alloys Int J Fatigue 10 4 1998 211 218
    • (1998) Int J Fatigue , vol.10 , Issue.4 , pp. 211-218
    • Song, Z.1    Hoeppner, D.W.2
  • 25
    • 0023827822 scopus 로고    scopus 로고
    • Hydrogen embrittlement of a titanium: In situ TEM studies
    • D.S. Shih, I.M. Robertson, and H.K. Birnbaum Hydrogen embrittlement of a titanium: in situ TEM studies Acta Metall 36 1 1998 111 124
    • (1998) Acta Metall , vol.36 , Issue.1 , pp. 111-124
    • Shih, D.S.1    Robertson, I.M.2    Birnbaum, H.K.3
  • 26
    • 0015300738 scopus 로고
    • A new model for hydrogen-assisted cracking (hydrogen embrittlement)
    • C.D. Beachem A new model for hydrogen-assisted cracking (hydrogen embrittlement) Met Trans 3 1972 437 451
    • (1972) Met Trans , vol.3 , pp. 437-451
    • Beachem, C.D.1
  • 27
    • 16244422147 scopus 로고
    • Hydrogen embrittlement of steel and its relation to weld metal cracking
    • N.G. Vaughan, and M.E. de Morton Hydrogen embrittlement of steel and its relation to weld metal cracking Brit Welding J 4 1957 40 61
    • (1957) Brit Welding J , vol.4 , pp. 40-61
    • Vaughan, N.G.1    De Morton, M.E.2
  • 28
    • 0020199379 scopus 로고
    • The influence of microstructure on the susceptibility of titanium alloys to internal hydrogen embrittlement
    • J.E. Hack, and G.R. Leverant The influence of microstructure on the susceptibility of titanium alloys to internal hydrogen embrittlement Met Trans 13(A) 1982 1729 1738
    • (1982) Met Trans , vol.13 , pp. 1729-1738
    • Hack, J.E.1    Leverant, G.R.2
  • 29
    • 0018683114 scopus 로고
    • The effect of hold time on the fatigue properties of a β-processed titanium alloy
    • W.J. Evans, and C.R. Gostelow The effect of hold time on the fatigue properties of a β-processed titanium alloy Met Trans 10(A) 1979 1837 1846
    • (1979) Met Trans , vol.10 , pp. 1837-1846
    • Evans, W.J.1    Gostelow, C.R.2
  • 31
    • 0032046099 scopus 로고    scopus 로고
    • The effect of dwell loading on the strain accumulation behaviour of titanium alloys
    • M.L. Thomsen, and D.W. Hoeppner The effect of dwell loading on the strain accumulation behaviour of titanium alloys Int J Fatigue 4 1998 309 317
    • (1998) Int J Fatigue , vol.4 , pp. 309-317
    • Thomsen, M.L.1    Hoeppner, D.W.2
  • 35
    • 0023421937 scopus 로고
    • Stress relaxation and notch fatigue in Ti-6Al-4V
    • W.J. Evans Stress relaxation and notch fatigue in Ti-6Al-4V Scripta Metall 21 1987 1223 1227
    • (1987) Scripta Metall , vol.21 , pp. 1223-1227
    • Evans, W.J.1
  • 36
    • 0023324619 scopus 로고
    • Influence of microstructure on dwell sensitive fatigue in a near-alpha titanium alloy
    • W.J. Evans Influence of microstructure on dwell sensitive fatigue in a near-alpha titanium alloy Scripta Metall 21 1987 469 474
    • (1987) Scripta Metall , vol.21 , pp. 469-474
    • Evans, W.J.1
  • 37
    • 0006966306 scopus 로고
    • Tension and torsion fatigue testing of a near-alpha titanium alloy
    • M.R. Bache, and W.J. Evans Tension and torsion fatigue testing of a near-alpha titanium alloy Int J Fatigue 14 5 1992 331 337
    • (1992) Int J Fatigue , vol.14 , Issue.5 , pp. 331-337
    • Bache, M.R.1    Evans, W.J.2
  • 38
    • 0028516453 scopus 로고
    • Dwell sensitive fatigue under biaxial loads in a near-alpha titanium alloy IMI 685
    • W.J. Evans, and M.R. Bache Dwell sensitive fatigue under biaxial loads in a near-alpha titanium alloy IMI 685 Fatigue 16 1994 443 452
    • (1994) Fatigue , vol.16 , pp. 443-452
    • Evans, W.J.1    Bache, M.R.2


* 이 정보는 Elsevier사의 SCOPUS DB에서 KISTI가 분석하여 추출한 것입니다.