Stress corrosion cracking of a BaTiO3 ferroelectric ceramics

Materials Letters

Volumn 58, Issue 11, 2004, Pages 1811-1814

  Wang, R M ^a   Chu, W Y ^a   Gao, K W ^a   Su, W Y J ^a   Qiao, L J ^a  

^a UNIVERSITY OF SCIENCE AND TECHNOLOGY BEIJING   (China)

Author keywords

BaTiO3 ceramic; Stress corrosion cracking; Threshold stress intensity factor

Indexed keywords

ATMOSPHERIC HUMIDITY; BARIUM TITANATE; ELECTRIC FIELD EFFECTS; ELECTRODES; FRACTURE TOUGHNESS; HYDROGEN; INTERFACIAL ENERGY; LOAD TESTING; SILICON; STRESS CORROSION CRACKING; TRANSMISSION ELECTRON MICROSCOPY;

CONSTANT LOAD MACHINES; THRESHOLD STRESS INTENSITY FACTORS;

FERROELECTRIC CERAMICS;

EID: 1542332791     PISSN: 0167577X     EISSN: None     Source Type: Journal    
DOI: 10.1016/j.matlet.2003.11.011     Document Type: Article

References (15)

1. Chen C.P., Knapp W.J. Delayed fracture of an alumina ceramic. J. Am. Ceram. Soc. 60:1977;87.
2. Ritter J.E., Humenik J.N. Static and dynamic fatigue of polycrystalline alumina. J. Mater. Sci. 14:1979;626-632.
3. Spearing S.M., Zok F.W., Evans A.G. Stress corrosion cracking in a unidirectional ceramic-matrix composite. J. Am. Ceram. Soc. 77:1994;562-570.
4. Okabe T., Kido M., Miyahara T. Fatigue fracture behavior of oxide ceramics in water. Eng. Fract. Mech. 48:1994;137-146.
5. 7-x ceramic superconductor. Phil. May. 61:1990;209-215.
6. Wang Y., Chu W.Y., Gao K.W., Su Y.J., Qiao L.J. Delayed fracture of lead zirconate titanate ferroelectric ceramics under sustained electric field. Appl. Phys. Lett. 82:2003;1583-1585.
7. Wang Y., Chu W.Y., Su Y.J., Qiao L.J. Stress corrosion cracking of a PZT piezoelectric ceramics. Mater. Lett. 57:2003;1156-1159.
8. Wang Y., Chu W.Y., Su Y.J., Qiao L.J. Anisotropy of corrosion cracking of a PZT piezoelectric ceramics. Mater. Sci. Eng. 95:2002;263-267.
9. Chu W.Y., Yao J., Hsiao C.M. Hydrogen induced slow crack growth in austenitic stainless steels. Metall. Trans. 15A:1984;729-735.
10. Wang Y., Chu W.Y., Qiao L.J., Su Y.J. Hydrogen-induced delayed fracture of PZT ceramics during dynamic charging under constant load. Mater. Sci. Eng. 2003;B98.1.
11. Michalske T.A., Freiman S.W. A molecular mechanism for stress corrosion in vitreous silica. J. Am. Ceram. Soc. 66:1983;284-288.
12. Michalske T.A., Banker B.C. Slow structure model based on strained silicate structures. J. Appl. Phys. 56:1984;2666.
13. Yu H.H., Suo Z. Model of wafer bonding by elastic accommodation. Acta Mater. 47:1999;77.
14. Tromans D. On surface energy and the hydrogen embrittlement of iron and steel. Acta Metall. Mater. 42:1994;2043.
15. J.K. Knott, Fundamental of Fracture Mechanics. London, Butterworths, 109.