Modeling Weld Solidification Cracking Behavior in Aluminum Alloys-Analysis of Fracture Initiation

ASM Proceedings of the International Conference: Trends in Welding Research

Volumn , Issue , 1998, Pages 695-699

  Brooks, J A ^a   Dike, J J ^a  

^a SANDIA NATIONAL LABORATORIES   (United States)

Author keywords

[No Author keywords available]

Indexed keywords

FRACTURE INITIATION;

CRACK INITIATION; FINITE ELEMENT METHOD; FRACTURE; GROWTH (MATERIALS); MATHEMATICAL MODELS; SOLIDIFICATION; WELDS;

ALUMINUM ALLOYS;

EID: 1442282351     PISSN: None     EISSN: None     Source Type: Conference Proceeding    
DOI: None     Document Type: Conference Paper

References (17)

1. Feng, Z.,"A Methodology for Quantifying the Thermal and Mechanical Conditions for Weld Solidification Cracking"., Ph.D. Dissertation, Ohio State University, 1993.
2. Feng, Z., and Tsai, C. L., "Modeling the Thermomechanical Conditions at Weld Pool", Proc. Modeling and Control of Joining Processes, Orlando, FL, Dec. 1993, ed. T. Zacharia, AWS, 525-532, 1994.
3. Zacharia, T., and Aramayo, G. A., "Modeling of Thermal Stresses in Welds", Proc. Modeling and Control of Joining Processes, Orlando, FL, Dec. 1993, ed. T. Zacharia, AWS, 533-540, 1994.
4. Feng, Z., Zacharia, T., and David, S. A., "Modeling of Thermomechanical Conditions in the Sigmajig Weldability Test", Proc. 4th International Conference on Trends in Welding Research, Gatlinburg, TN, June, 1995, Ed. H. B. Smartt, J. A. Johnson, S. A. David, 621-626.
5. Feng, Z., Zacharia, T., and David, S. A., "Thermal Stress Development in a Nickel Based Superalloy During Weldability Test", Welding Journal Research Suppliment, 470s-483s, Nov. 1997.
6. Liu, W., "Computational Analysis and Prediction of Weld-Solidification Cracking", Comp. Mat. Sci., 4 (3), 212-219, 1995.
7. Brooks, J. A., Dike, J. J., and Krafcik, J. S., "On Modeling Weld Solidification Cracking", Proc. Modeling and Control of Joining Processes, Orlando, FL, Dec. 1993, ed. T. Zacharia, AWS, 174-185, 1994.
8. Dike, J. J., Brooks, J. A., and Krafcik, J. S., "Finite Element Modeling and Verification of Thermal-Mechanical Behavior in the Weld Pool Region", Proc. 4th Int. Conf. on Trends in Welding Research, Gatlinburg, TN, Ed. H. B. Smartt, J. A. Johnson, S. A. David, 159-164, 1995.
9. Dike, J. J., Brooks, J. A., Bammann, D. J., and Li, M., "Thermal-Mechanical Modeling and Experimental Validation of Weld Solidification Cracking in 6061-T6 Aluminum", Proc. of ASM Int'l European Conf. on Welding and Joining Science and Technology, Madrid, Spain, 269-277, 1997.
10. Dike, J.J., Brooks, J.A., Bammann, D.J., Li, M., Krafcik, J.S., and Yang, N.Y.C., "Predicting Weld Solidification Cracking Using Damage Mechanics - LDRD Summary Report", Sandia National Laboratories report SAND97-8256, 1997.
11. Dike, J. J., Brooks, J. A., and Li, M., "Comparison of Failure Criteria in Weld Solidification Cracking Simulations", Proc. 4th Int. Seminar on Numerical Analysis of Weldability, Graz, Austria, 1997.
12. D. J. Bammann, M. L. Chiesa, M. F. Horstemeyer, and L. W. Weingarten, "Failure in Ductile Materials using Finite Element Methods," Structural Crashworthiness and Failure, N. Jones and T. Wierzbicki, eds. (Elsevier Applied Science, New York, NY, 1993), 1-54.
13. D. J. Bammann, M. L. Chiesa, and G. C. Johnson, "Modeling Large Deformation and Failure in Manufacturing Processes," Theoretical and Applied Mechanics 1996, T. Tatsumi, E. Watanabe, and T. Kambe, eds. (Elsevier Applied Science, New York, NY, 1997), 359-376.
14. Matsuda, F., Nakagawa, H., and Sarada, K., "Dynamic Observation of Solidification and Solidification Cracking During Welds with Optical Microscope, I", Transactions of JWRI 11(2):67-77, 1982.
15. Matsuda, F., Nakagawa, H., Nakata, K., Kohmoto, H., and Hondo, Y,. "Quantitative Evaluation of Solidification Brittleness of Weld Metal During Solidification by Means of In-situ Observation and Measurement I", Transactions JWRI 12(1):65-72, 1983.
16. Matsuda, F., Nakagawa, H., and Tomita, S., Quantitative Evaluation of Solidification Brittleness of Weld Metal During Solidification by In-situ Observation and Measurement (Report IV) - Effect of Grain-boundary Sliding on Strain-rate Dependence of Critical Strain Required for Solidification Crack Initiation. Trans. of JWRI 16(2):89-95, 1987.
17. Matsuda, F., Nakagawa, K., Kohmoto, H., Honda, Y., and Matsubara, Y, "Quantitative evaluation of solidification brittleness of weld metal during solidification by in-situ observation and measurement (Report II) - Solidification ductility curves for steels with the MISO technique", Trans. of JWRI 12(1): 73-80, 1983.