Compressive strength and surface characterization of glass ionomer cements modified by particles of bioactive glass

Dental Materials

Volumn 21, Issue 3, 2005, Pages 201-209

  Yli Urpo, Helena ^a   Lassila, Lippo V J ^a   Närhi, Timo ^a   Vallittu, Pekka K ^a  

^a UNIVERSITY OF TURKU   (Finland)

Author keywords

Bioactive glass; Compressive strength; Glass Ionomer cements; Surface hardness; Young's modulus

Indexed keywords

CHEMICAL MODIFICATION; COMPOSITION; COMPRESSIVE STRENGTH; DENTISTRY; ELASTIC MODULI; ELASTICITY; GLASS; IONOMERS; MICROHARDNESS; RESINS;

BIOACTIVE GLASS; GLASS-IONOMER CEMENTS; SURFACE HARDNESS; TEST SPECIMENS;

DENTAL CEMENT;

BIOGLASS; GLASS IONOMER;

ANALYSIS OF VARIANCE; ARTICLE; CERAMICS; CHEMISTRY; COMPARATIVE STUDY; COMPRESSIVE STRENGTH; DENTAL CARE; ELASTICITY; HARDNESS; IMMERSION; MATERIALS TESTING; SCANNING ELECTRON MICROSCOPY; SPECTROMETRY; SURFACE PROPERTY;

ANALYSIS OF VARIANCE; CERAMICS; COMPRESSIVE STRENGTH; DENTAL STRESS ANALYSIS; ELASTICITY; GLASS IONOMER CEMENTS; HARDNESS; IMMERSION; MATERIALS TESTING; MICROSCOPY, ELECTRON, SCANNING; SPECTROMETRY, X-RAY EMISSION; SURFACE PROPERTIES;

EID: 13444291996     PISSN: 01095641     EISSN: None     Source Type: Journal    
DOI: 10.1016/j.dental.2004.03.006     Document Type: Article

References (26)

1. Wilson A.D., McLean J.W. Glass ionomer cement. 1988;Quintessence Publishing Co, Chicago, IL, USA
2. Van Noort R. Glass-ionomer cements and resin-modified glass-ionomer cements. Introduction to dental materials. 2002;Mosby, Edinburgh, UK. p. 129-30
3. Darvell B.W. Materials science for dentistry. 7th ed :2002;B.W. Darwvell, Hong Kong, China. p. 215-6
4. Antonucci J.M., Stansbury J.W. Polymer-modified glass ionomer cements. J Dent Res. 68:(251):1989;555. Abstr. No. 555
5. Brook I.M., Hatton P.V. Glass-ionomers: bioactive implant materials. Biomaterials. 19:1998;565-571
6. Yap A.U.J., Pek Y.S., Kumar R.A., Cheang P., Khor K.A. Experimental studies on a new bioactive material: HAIonomer cements. Biomaterials. 23:2002;955-962
7. Yli-Urpo H., Forsback A.P., Väkiparta M., Vallittu P.K., Närhi T.O. Release of silica, calcium, phosphorus and fluoride from glass ionomer cement containing bioactive glass. J Biomater Appl. 19:2004;5-20
8. Yli-Urpo H., Närhi T., Söderling E. Antimicrobial effects of glass ionomer cements containing bioactive glass (S53P4) on oral micro-organisms in vitro. Acta Odontol Scand. 6:2003;241-246
9. International Standard ISO 3824-1984(E). Dentistry-Dental silicophosphate cement (hand-mixed). 2nd ed :1984;International organization for standardization, Geneva, Switzerland
10. Wilson A.D. Resin-modified glass-ionomer cements. Int J Prosthodont. 3:1990;425-429
11. Xie D., Brantley W.A., Culbertson B.M., Wang G. Mechanical properties and microstructures of glass-ionomer cements. Dent Mater. 16:2000;129-138
12. Tay F.R., Pashley E.L., Huang C., Hashimoto M., Sano H., Smales R.J., Pashley D.H. The glass-ionomer phase in resin-based restorative materials. J Dent Res. 80:2001;1808-1812
13. Williams J.A., Billington R.W. Changes in compressive strength of glass ionomer restorative materials with respect to time periods of 24 h to 4 months. J Oral Rehab. 18:1991;163-168
14. Pearson G.J., Atkinson A.S. Long-term flexural strength of glass ionomer cements. Biomaterials. 12:1991;658-660
15. Tam L.E., Pulver E., McComb D., Smith D.C. Physical properties of calcium hydroxide and glass-ionomer base and lining materials. Dent Mater. 5:1989;145-149
16. Crisp S., Lewis B.G., Wilson A.D. Characterization of glass-ionomer cements. 1. Long term hardness and compressive strength. J Dent. 4:1976;162-166
17. Mitra S.B., Kedrowski B.L. Long-term mechanical properties of glass ionomers. Dent Mater. 10:1994;78-82
18. Andersson Ö.H., Karlsson K.H., Kangasniemi K. Calcium phosphate formation at the surface of bioactive glass ion vivo. J Non-Cryst Solids. 119:1990;290-296
19. Akashi A., Matsuya Y., Unemori M., Akamine A. The relationship between water absorption characteristics and the mechanical strength of resin-modified glass-ionomer cements in long-term water storage. Biomaterials. 20:1999;1573-1578
20. Kanchanavasita W., Anstice H.M., Pearson G.J. Water sorption characteristics of resin-modified glass-ionomer cements. Biomaterials. 18:1997;343-349
21. Rich J., Jaakkola T., Tirri T., Närhi T., Yli-Urpo A., Seppälä J. In vitro evaluation of poly(ε-caprolactone co-DL-lactide)/bioactive glass composites. Biomaterials. 23:2002;2143-2150
22. Jaakkola T., Rich J., Tirri T., Närhi T., Aho A., Seppälä J., Yli-Urpo A. In vitro Ca-P formation on biodegradable thermoplastic composite of poly(ε-caprolactone-co-DL-lactide) and bioactive glass (S53P4). Biomaterials. 25:2004;575-581
23. Rosenstiel S.F., Land M.F., Crispin B.J. Dental luting agents: a review of the current literature. J Prosthet Dent. 80:1998;280-301
24. Mitsuhashi A., Hanaoka K., Teranaka T. Fracture toughness of resin-modified glass ionomer restorative materials: effect of powder/liquid ratio and powder particle size reduction on fracture toughness. Dent Mater. 19:2003;747-757
25. Cattani-Lorente M.A., Dupuis V., Moya F., Payan J., Meyer J.M. Comparative study of the physical properties of a polyacid-modified composite resin and a resin-modified glass ionomer cement. Dent Mater. 15:1999;21-32
26. McKenzie M.A., Linden R.W.A., Nicholson J.W. The physical properties of conventional and resin-modified glass-ionomer dental cements stored in saliva, proprietary acidic beverages, saline and water. Biomaterials. 24:2003;4063-4069