Electrochemical polarization and stress corrosion cracking of alloy 690 in 5-M chloride solutions at 25°C

Corrosion

Volumn 61, Issue 1, 2005, Pages 3-11

  Chen, Y Y ^a   Chou, L B ^a   Wang, L H ^b   Oung, J C ^b   Shih, H C ^a  

^a NATIONAL TSING HUA UNIVERSITY   (Taiwan)

^b NONE   (Taiwan)

Author keywords

Alloy 690; Electrochemical hysteresis; General corrosion; Passivation; Pitting corrosion; Potential pH diagram; Slow strain rate test

Indexed keywords

ELECTROCHEMICAL CORROSION; FRACTURE; HYSTERESIS; PASSIVATION; PITTING; STRAIN RATE; STRESS CORROSION CRACKING; TENSILE STRENGTH; TENSILE TESTING;

ELECTROCHEMICAL HYSTERESI; ELECTROCHEMICAL POLARIZATION; GENERAL CORROSION; SLOW STRAIN RATE TEST (SSRT); ULTIMATE TENSILE STRENGH (UTS};

CHLORINE COMPOUNDS;

ELECTROCHEMICAL ANALYSIS; PH; POLARIZATION; STRESS CORROSION CRACKING;

EID: 13244258536     PISSN: 00109312     EISSN: None     Source Type: Journal    
DOI: 10.5006/1.3278159     Document Type: Article

References (26)

1. W.F. Smith, Structure and Properties of Engineering Alloys (New York, NY: McGraw Hill, 1993), p. 321-323.
2. H.H. Uhlig, R.W. Revie, Corrosion and Corrosion Control (New York, NY: John Wiley and Sons, 1991), p. 305-312.
3. D.A. Jones, Principles and Prevention of Corrosion (Englewood Cliffs, NJ: Prentice Hall, 1996), p. 292-294.
4. J. Kocourek, Nucl. Eng. Int. 39 (1994): p. 22.
5. D. Choi, G.S. Was, Corrosion 146, 2 (1990): p. 100.
6. R.C. Newman, H.S. Isaacs, B. Alman, Corrosion 38, 5 (1982): p. 261.
7. R.C. Newman, W.P. Wong, H. Ezuber, A. Garner, Corrosion 45, 4 (1989): p. 282.
8. W. Yang, Z. Lu, D. Huang, D. Kong, G. Zhao, J. Congleton, Corros. Sci. 43 (2001): p. 963-977.
9. W.T. Tsai, C.H. Chou, Mater. Sci. Eng. A288 (2000): p. 5-11.
10. W.T. Tsai, T.F. Wu, J Nucl. Mater. 277 (2000): p. 169-174.
11. M. Pourbaix, Altas of Electrochemical Equilibria in Aqueous Solutions (Houston, TX: Cebelcor, NACE International, 1974), p. 307.
12. E.D. Verink, Jr., Corrosion 23 (1967): p. 371.
13. K.D. Efird, Corrosion 31 (1975): p. 77.
14. S.D. Chyou, H.C. Shih, Bull. Electrochem. 3 (1987): p. 1-6.
15. S.D. Chyou, H.C. Shih, Corrosion 47 (1991): p. 31.
16. N.D. Greene, Experimental Electrode Kinetics (Troy, NY: Rensselaer Polytechnic Institute, 1965), p. 4.
17. A. Atrens, Corrosion 39 (1983): p. 483.
18. ASTM G49-85, "Standard Practice for Preparation and Use of Direct Tension Stress Corrosion Test Specimens," in Annual Book of ASTM Standards, vol. 03.02 (West Conshohocken, PA: ASTM International, 1989), p. 187-191.
19. J. Congleton, H.C. Shih, T. Shoji, R.N Parkins, Corros. Sci. 25 (1985): p. 769.
20. Metals Handbook, "Corrosion," vol. 13 (Materials Park, OH: ASM International, 1988), p. 262.
21. B.E. Wilde, Corrosion 28 (1972): p. 283.
22. B.C. Syrett, D.D. Macdonald, H.C. Shih, Corrosion 36 (1980): p. 130.
23. H.C. Shih, J.C. Oung, J.T. Hsu, J.Y. Wu, F.I. Wei, Mater. Chem. Phys. 37 (1994): p. 230-236.
24. V. Ashworth, P.J. Boden, Corros Sci. 10 (1970): p. 709.
25. M. Pourbaix, Altas of Electrochemical Equilibria in Aqueous Solutions (Houston, TX: Cebelcor, NACE, 1974), p. 264.
26. F.P. Ford, P.L. Andresen, "Development and Use of a Predictive Model of Crack Propagation in 304/316L, A533B/A508, and Inconel 600/182 Alloys in 288°C," Proc. of the 3rd Environmental Degradation of Materials in Nuclear Power Systems-Water Reactors, eds. G.J. Theus, J.R. Weeks (MA: AMS, 1988), p. 789.