Failure of weld joints between carbon steel pipe and 304 stainless steel elbows

Engineering Failure Analysis

Volumn 12, Issue 2, 2005, Pages 181-191

  Ul Hamid, Anwar ^a   Tawancy, Hani M ^a   Abbas, Nureddin M ^a  

^a KING FAHD UNIVERSITY OF PETROLEUM AND MINERALS   (Saudi Arabia)

Author keywords

Cracks; Failure analysis; Heat affected zone; Hydrogen damage; Welds

Indexed keywords

CARBON STEEL; COOLING; CRACKS; HYDROGEN; LEAKAGE (FLUID); PEARLITE; PETROCHEMICAL PLANTS; QUENCHING; SCANNING ELECTRON MICROSCOPY; STEEL PIPE; X RAY ANALYSIS;

CARBON STEEL (CS) PIPES; HYDROGEN RICH MEDIUM;

WELDING;

CARBON STEEL; CRACKING; FAILURE ANALYSIS; HYDROGEN CORROSION; STAINLESS STEEL; WELD;

EID: 12444336975     PISSN: 13506307     EISSN: None     Source Type: Journal    
DOI: 10.1016/j.engfailanal.2004.07.003     Document Type: Article

References (5)

1. ASTM Standard A53-90b. Annual book of ASTM standards. vol. 01.01. American Society for Testing of Metals; 1993. p. 1
2. Welding and brazing. In: Metals handbook, vol. 6, 8th ed. Metals Park (OH): American Society of Metals; 1971. p. 252
3. Welding and brazing. In: Metals handbook, vol. 6, 8th ed. Metals Park (OH): American Society of Metals; 1971. p. 274
4. Failure analysis and prevention. In: Metals handbook, vol. 10, 8th ed. Metals Park (OH): American Society of Metals; 1971. p. 343
5. Failure analysis and prevention. In: Metals handbook, vol. 10, 8th ed. Metals Park (OH): American Society of Metals; 1971. p. 230