Spalling formation mechanism for gears

Wear

Volumn 254, Issue 12, 2003, Pages 1307-1317

  Ding, Yan ^a   Rieger, Neville F ^b  

^a RMIT UNIVERSITY   (Australia)

^b Stress Technology Incorporated   (United States)

Author keywords

Crack failure; Ligament collapse; Spalling; Subsurface cracks

Indexed keywords

CRACK TIPS; CRACKS; GEAR TEETH; PITTING;

CONTACT SURFACE; CRACK FAILURE; FORMATION MECHANISM; FORMATION PROCESS; GEAR TOOTH CONTACTS; LITERATURE REVIEWS; PITTING AND SPALLING; SUBSURFACE CRACKS;

SPALLING;

EID: 12344263984     PISSN: 00431648     EISSN: None     Source Type: Journal    
DOI: 10.1016/S0043-1648(03)00126-1     Document Type: Article

References (25)

1. Y. Ding, R. Jones, B.T. Kuhnell, Elastic-plastic finite element analysis of spall formation in gears, Wear 197 (1996) 197-205.
2. M. Heems, F. Lagarde, R. Courtel, P. Sorin, C. R. Acad. Sci. 257 (3) (1963) 3293.
3. A.M. Kumar, G.T. Hahn, V. Rubin, Elasto-plastic finite element analyses of two-dimensional rolling and sliding contact deformation of bearing steel, J. Tribol. Trans. ASME 111 (1989) 309-314.
4. L.E. Alban, Systematic Analysis of Gear Failures, ASM International, Metals Park, OH, 1985.
5. R. I. Widner, Rolling Bearing Failures, ASM Metals Handbook, ninth ed., vol. 11, Failure Analysis and Prevention, ASM International, Metals Park, OH, 1986, pp. 490-511.
6. T.E. Tallian, Failure Atlas for Hertz Contact Machine Elements, New York, 1992.
7. S. Way, Pitting due to rolling contact, J. Appl. Mech. Trans. ASME 2 (1935) A49.
8. L.M. Keer, M.D. Bryant, A pitting model for rolling contact fatigue, J. Lubr. Technol. Trans. ASME 105 (1983) 198-205.
9. A.F. Bower, The influence of crack face friction and trapped fluid on surface initiated rolling contact fatigue cracks, Trans. ASME, JOT 110 (1988) 704-711.
10. H.S. Cheng, L.M. Keer, T. Mura, Analytical modelling of surface pitting in simulated gear-teeth contacts, SAE Technical Paper, No. 841086, 1984, pp. 4.987-4.995.
11. J.F. Fleming, N.P. Suh, Mechanics of crack propagation in delamination wear, Wear 44 (1977) 39-56.
12. K. Kaneta, Y. Murakami, T. Okazaki, Growth mechanism of subsurface crack due to Hertzian contact, J. Tribol. Trans. ASME 108 (1986) 134-139.
13. H.-C. Sin, N.P. Suh, Subsurface crack propagation due to surface traction in sliding wear, J. Appl. Mech. Trans. ASME 51 (1984) 317-323.
14. Y. Ding, R. Jones, B.T. Kuhnell, Numerical analysis of subsurface crack failure beneath the pitch line of a gear tooth during engagement, Wear 185 (1995) 141-149.
15. M. Kaneta, H. Yatsuzuka, Y. Murakami, Mechanism of crack growth in lubricated rolling/sliding contact, ASLE Trans. 28 (1985) 407-414.
16. T.M. Clarke, G.R. Miller, L.M.. Keer, H.C. Cheng, The role of near-surface inclusions in the pitting of gears, ASLE Trans. 28 (1) (1985) 111-116.
17. B.D. O'regan, G.T. Hahn, C.A. Rubin, The driving force for Mode II crack growth under rolling contact, Wear 101 (1985) 333-346
18. P.C. Bastias, G.T. Hahn, C.A. Rubin, Finite element modelling of subsurface Mode II cracks under contact loads, Eng. Fracture Mech. 33 (1) (1989) 143-152.
19. L.M. Keer, M.D. Bryant, G.K. Haritos, Subsurface and surface cracking due to Hertzian contact, J. Lubr. Technol. Trans. ASME 104 (1982) 347-351.
20. G.R. Miller, A preliminary analysis of subsurface crack branching under a surface compressive load, J. Tribol. Trans. ASME 110 (1988) 292-296.
21. J.W. Blake, H.S. Cheng, A surface pitting life model for spur gears. Part I. Life prediction, J. Tribol. Trans. ASME 113 (1991) 712-718.
22. H.E. Knechtel, W.F. Kindle, J.L. McCall, R.D. Buchheit, Metallographic Methods, ASM Metal Handbook, eighth ed., vol. 8, American Society of Metals, Metals Park, OH, 1973, pp. 1-14.
23. M.L. Atkin, R.A. Cummins, G.P. Sharp, A Study of Gear Wear in a Model Gearbox, Mechanical Engineering Transactions, The Institute of Engineers, Australia, 1979, pp. 40-52.
24. X.Z. Jin, N.Z. Kang, A study on rolling bearing contact fatigue failure by macro-observation and micro-analysis, in: Proceedings of the International Conference on Wear of Materials, Denver, CO, USA, 1989, pp. 205-213.
25. D.C. Stouffer, L.T. Dame, Inelastic Deformation of Metals: Models, Mechanical Properties, and Metallurgy, Wiley, New York, 1996.