Thick and hard anodized aluminum film with large pores for surface composites

Transactions of Nonferrous Metals Society of China (English Edition)

Volumn 14, Issue SUPPL. 2, 2004, Pages 166-169

  Wang, Hui ^a   Wang, Hao Wei ^a  

^a SHANGHAI JIAO TONG UNIVERSITY   (China)

Author keywords

Anodization; Ce salt; Hardness; Large pores; Organic carboxylic acid; Thickness

Indexed keywords

ADDITIVES; ALUMINA; FABRICATION; FILMS; HARDNESS; SELF LUBRICATING COMPOSITES;

ANODIZATION; CERIUM SALT; LARGE PORE; ORGANIC CARBOXYLIC ACID; THICKNESS;

ANODIC OXIDATION;

EID: 11444254318     PISSN: 10036326     EISSN: None     Source Type: Journal    
DOI: None     Document Type: Article

References (15)

1. Chou S M, Leidheiser H Jr. Wear of anodized aluminum under three body conditions [J]. Ind Eng Chem Prod Res, 1986, 25: 473-478.
2. Abdul-Mabdi F, Eyre T S. Wear of coatings on aluminum and its alloys [A]. Proc 1st Int'l Conf Surf Eng [C]. Cambridge: The Welding Institute, 1986. 203-222.
3. Skoneczny W, Tokarz A. Mechanism of destructive changes in oxide covered surface caused by friction [J]. Wear, 1994(169): 209-214.
4. XU Tao, CHEN Jian-min. The pore-enlargement and self-lubrication treatment of anodic oxide film of aluminum [J]. Wear, 1996, 196(1-2): 214-218.
5. 2 in the pores of anodic films on aluminium [J]. Journal of University of Science and Technology Beijing, 1991, 13(3): 273.
6. 2 precursor films on anodized aluminum [J]. Wear, 1997(206): 187-196.
7. 2 precursors [J]. Tribology Transactions, 1999(1): 202-204.
8. ZHAO Yan-chun, CHEN Miao. Preparation and self-lubrication treatment of ordered porous anodic alumina film [J]. Materials Chemistry and Physics, 2003(82): 370-374.
9. YANG Bo-xuan, CHEN Jian-min. Development of zinc stearate-base self-lubricating anodic oxidized Al by electrochemical in-situ synthesizing method [J]. Chinese Journal of Materials Research, 1998, 12(1): 69-70.
10. Maejima M, Saruwatari K. Friction behaviour of anodic oxide film on aluminum impregnated with molybdenum sulfide compounds [J]. Surface and Coatings Technology, 2000, 132(2-3): 105-110.
11. WU Shen-ming. A new technology and its application of oxidation of oxalic acid positive pole [J]. Shanghai Astronavigation, 1996, 5: 66-68.
12. Ono S, Masulo N. Evaluation of pore diameter of anodic porous films formed on aluminum [J]. Surface and Coating Technology, 2003(169-170): 139-142.
13. WANG Zhu-tang. The Treatment Handbook of Aluminum-based Materials and its Surfaces [M]. Nanjing: The Scientific and Technical Publishing Company of Jiangsu, 1992. 304-361.
14. LI Ling-jie, LI Di. Effect of rare earth salts on anodizing of aluminum alloy [J]. Journal of the Chinese Rare Earth Society, 2001, 19(4): 350-354.
15. Hinton B R W, Arnott D R. The inhibition of aluminum alloy corrosion by cerous Coating [J]. Metals Forum, 1984, 7(4): 211-213.