Volumn 130, Issue 4, 2004, Pages 723-742

Significance of morphology changes at a propagating crack edge

Author keywords

Crack face morphology; Dynamic crack propagation; Localization; Self similarity

Indexed keywords

BOUNDARY LAYERS; COALESCENCE; CRACK PROPAGATION; FRACTURE MECHANICS; MICROCRACKS; SEPARATION; SHEAR FLOW; SHEAR STRESS; SURFACES; TURBULENCE;

EID: 11144283689     PISSN: 03769429     EISSN: None     Source Type: Journal    
DOI: 10.1007/s10704-004-2825-7     Document Type: Article
Times cited : (6)

References (43)
  • 3
    • 0026122728 scopus 로고
    • Relationships between fracture parameters and fracture surface roughness of brittle polymers
    • K. Arakawa K. Takahashi 1991 Relationships between fracture parameters and fracture surface roughness of brittle polymers International Journal of Fracture 48 103 114
    • (1991) International Journal of Fracture , vol.48 , pp. 103-114
    • Arakawa, K.1    Takahashi, K.2
  • 5
    • 0009231269 scopus 로고
    • The formation of equilibrium cracks during brittle fracture.General ideas and hypotheses. Axially-symmetric cracks
    • English translation from PMM 23 (1959), 434-444
    • Barenblatt, G.I. (1959). The formation of equilibrium cracks during brittle fracture. General ideas and hypotheses. Axially-symmetric cracks. Journal of Applied Mathematics Mechanics 23, 622-636. English translation from PMM 23 (1959), 434-444.
    • (1959) Journal of Applied Mathematics Mechanics , vol.23 , pp. 622-636
    • Barenblatt, G.I.1
  • 9
    • 11144349099 scopus 로고
    • Sprängämnes verkan vid kontaktdetonation mot granitplattor
    • Report 109:15 from the Royal Swedish Fortification Board, Stockholm 1960
    • Broberg, K.B. (1960). Sprängämnes verkan vid kontaktdetonation mot granitplattor. Report 109:15 from the Royal Swedish Fortification Board, Stockholm 1960 .
    • (1960)
    • Broberg, K.B.1
  • 11
    • 0001824375 scopus 로고
    • On the behaviour of the process region at a fast running crack tip
    • (edited by Kawata K. and Shioiri J.) Springer-Verlag Berlin Heidelberg
    • Broberg K.B. (1979). On the behaviour of the process region at a fast running crack tip. In High Velocity Deformation of Solids (edited by Kawata K. and Shioiri J.) Springer-Verlag Berlin Heidelberg 182-194
    • (1979) High Velocity Deformation of Solids , pp. 182-194
    • Broberg, K.B.1
  • 14
    • 0031139168 scopus 로고    scopus 로고
    • The cell model of materials
    • Broberg, K.B. (1996) The cell model of materials. Computational Mechanics 19, 447-452.
    • (1996) Computational Mechanics , vol.19 , pp. 447-452
    • Broberg, K.B.1
  • 18
    • 84984525422 scopus 로고
    • Admissible speeds for plane-strain self-similar shear cracks with friction but lacking cohesion
    • Burridge R. (1973). Admissible speeds for plane-strain self-similar shear cracks with friction but lacking cohesion. Geophysics Journal of Royal Astronomical Society 35, 439-455.
    • (1973) Geophysics Journal of Royal Astronomical Society , vol.35 , pp. 439-455
    • Burridge, R.1
  • 19
    • 0030867117 scopus 로고    scopus 로고
    • Micromechanics of Coalescence -I. Synergistic effects of elasticity, plastic yielding and multi-size-scale voids
    • Faleskog, J. and Shih, C.F., (1997). Micromechanics of Coalescence -I. Synergistic effects of elasticity, plastic yielding and multi-size-scale voids. Journal of Mechanics and Physics of Solids 45, 21 50.
    • (1997) Journal of Mechanics and Physics of Solids , vol.45 , pp. 21-50
    • Faleskog, J.1    Shih, C.F.2
  • 21
    • 0003443551 scopus 로고    scopus 로고
    • Cambridge University Press Cambridge UK
    • Hull, D. (1999). Fractography. Cambridge University Press Cambridge UK
    • (1999) Fractography
    • Hull, D.1
  • 22
    • 0001759909 scopus 로고
    • Stress intensity factors at tips of branched cracks under various loadings
    • Isida, M. and Noguchi H., (1992). Stress intensity factors at tips of branched cracks under various loadings. International Journal of Fracture 54, 293-316.
    • (1992) International Journal of Fracture , vol.54 , pp. 293-316
    • Isida, M.1    Noguchi, H.2
  • 23
    • 0000305448 scopus 로고
    • Process region changes for rapidly propagating cracks
    • Johnson E., (1992). Process region changes for rapidly propagating cracks. International Journal of Fracture 55, 47-63.
    • (1992) International Journal of Fracture , vol.55 , pp. 47-63
    • Johnson, E.1
  • 24
    • 0002950403 scopus 로고
    • Process region influence on crack branching
    • Johnson, E. (1992). Process region influence on crack branching. International Journal of Fracture 57, R27-R29.
    • (1992) International Journal of Fracture , vol.57
    • Johnson, E.1
  • 25
    • 0027589229 scopus 로고
    • Process region influence on energy release rate and crack tip velocity during rapid crack propagation
    • Johnson, E. (1993). Process region influence on energy release rate and crack tip velocity during rapid crack propagation. International Journal of Fracture 61, 183-187.
    • (1993) International Journal of Fracture , vol.61 , pp. 183-187
    • Johnson, E.1
  • 26
    • 0035482317 scopus 로고    scopus 로고
    • Simulations of microcracking in the process region of ceramics with a cell model
    • Johnson, E. (2001). Simulations of microcracking in the process region of ceramics with a cell model. International Journal of Fracture 111, 361-380.
    • (2001) International Journal of Fracture , vol.111 , pp. 361-380
    • Johnson, E.1
  • 27
    • 0004848411 scopus 로고
    • On the propagation direction of bifurcated cracks
    • (edited by Sih G.C.) Noordhoff International Publishing Leyden
    • Kalthoff, J.F., (1973). On the propagation direction of bifurcated cracks. In Dynamic Crack Propagation, (edited by Sih G.C.) Noordhoff International Publishing Leyden, 449-458.
    • (1973) Dynamic Crack Propagation , pp. 449-458
    • Kalthoff, J.F.1
  • 28
    • 0017633830 scopus 로고
    • Relation between crack velocity and the stress intensity factor in birefringent polymers
    • ASTM STP 627 (edited by Hahn, G.T. and Kanninen, M.F.) American Society for Testing and Materials
    • Kobayashi, T. and Dally, J.W. (1977). Relation between crack velocity and the stress intensity factor in birefringent polymers. In Fast Fracture and Crack Arrest, ASTM STP 627 (edited by Hahn, G.T. and Kanninen, M.F.) American Society for Testing and Materials 257-273
    • (1977) Fast Fracture and Crack Arrest , pp. 257-273
    • Kobayashi, T.1    Dally, J.W.2
  • 29
    • 0022659127 scopus 로고
    • When does a crack grow under mode II conditions?
    • Melin, S., (1986). When does a crack grow under mode II conditions? International Journal of Fracture 30, 103-114.
    • (1986) International Journal of Fracture , vol.30 , pp. 103-114
    • Melin, S.1
  • 31
    • 0018305892 scopus 로고
    • Determination of the growth of branched cracks by numerical methods
    • Pärletun L.G. (1979). Determination of the growth of branched cracks by numerical methods. Engineering Fracture and Mechanics 11, 343-358.
    • (1979) Engineering Fracture and Mechanics , vol.11 , pp. 343-358
    • Pärletun, L.G.1
  • 32
    • 2242418440 scopus 로고
    • An experimental investigation into the mechanics of dynamic fracture
    • Ph. D. Thesis, California Institute of Technology, Pasadena, California
    • Ravi-Chandar, K. (1982). An experimental investigation into the mechanics of dynamic fracture . Ph. D. Thesis, California Institute of Technology, Pasadena, California.
    • (1982)
    • Ravi-Chandar, K.1
  • 33
    • 0032282934 scopus 로고    scopus 로고
    • Dynamic fracture of nominally brittle materials
    • Ravi-Chandar, K. (1998). Dynamic fracture of nominally brittle materials. International Journal of Fracture 90, 83-102.
    • (1998) International Journal of Fracture , vol.90 , pp. 83-102
    • Ravi-Chandar, K.1
  • 34
    • 0021494342 scopus 로고
    • An experimental investigation into dynamic fracture: II Microstructural aspects
    • Ravi-Chandar, K. and Knauss, W.G. (1984) An experimental investigation into dynamic fracture: II Microstructural aspects. International Journal of Fracture 26, 65-80.
    • (1984) International Journal of Fracture , vol.26 , pp. 65-80
    • Ravi-Chandar, K.1    Knauss, W.G.2
  • 35
    • 0031125451 scopus 로고    scopus 로고
    • On the role of microcracks in the dynamic fracture of brittle materials
    • Ravi-Chandar, K. and Yang, B. (1997). On the role of microcracks in the dynamic fracture of brittle materials. Journal of Mechanics and Physics of Solids 45, 535-563.
    • (1997) Journal of Mechanics and Physics of Solids , vol.45 , pp. 535-563
    • Ravi-Chandar, K.1    Yang, B.2
  • 36
    • 0036610705 scopus 로고    scopus 로고
    • Intersonic shear cracks and fault ruptures
    • Rosakis, A.J. (2002). Intersonic shear cracks and fault ruptures. Advances in Physics 51, 1189 1257.
    • (2002) Advances in Physics , vol.51 , pp. 1189-1257
    • Rosakis, A.J.1
  • 37
    • 0035297041 scopus 로고    scopus 로고
    • Experimental observations of intersonic crack growth in asymmetrically loaded unidirectional composites plates
    • Rosakis, A.J. and Coker, D. (2000). Experimental observations of intersonic crack growth in asymmetrically loaded unidirectional composites plates. Philosophical Magazine A A81, 571-595.
    • (2000) Philosophical Magazine A , vol.A81 , pp. 571-595
    • Rosakis, A.J.1    Coker, D.2
  • 38
    • 0033591368 scopus 로고    scopus 로고
    • Cracks faster than the shear wave speed
    • Rosakis, A.J., Samudrala, O. and Coker, D. (1999). Cracks faster than the shear wave speed. Science 284, 1337-1340.
    • (1999) Science , vol.284 , pp. 1337-1340
    • Rosakis, A.J.1    Samudrala, O.2    Coker, D.3
  • 39
    • 0008801933 scopus 로고
    • Velocity effects in fracture
    • edited by Averbach, B.L., Felbeck, D.K., Hahn G.T. and Thomas, D.A.) John Wiley & Sons New York
    • Schardin, H. (1959). Velocity effects in fracture. In Fracture (edited by Averbach, B.L., Felbeck, D.K., Hahn G.T. and Thomas, D.A.) John Wiley & Sons, New York, 297-329.
    • (1959) Fracture , pp. 297-329
    • Schardin, H.1
  • 40
    • 0001294816 scopus 로고    scopus 로고
    • Micro-branching instability and the dynamic fracture of brittle materials
    • E. Sharon, J. Fineberg Micro-branching instability and the dynamic fracture of brittle materials Physical Review B 1996 54 7128 7149.
    • (1996) Physical Review B , vol.54 , pp. 7128-7149
    • Sharon, E.1    Fineberg, J.2
  • 41
    • 0012000767 scopus 로고
    • Dynamic fracture toughness and crack propagation in brittle material
    • (edited by Kawata, K. and Shioiri, J.) Springer-Verlag Tokyo
    • T. Shioya, F. Zhou, Dynamic fracture and crack propagation in brittle material. Constitutive Relation in High/Very High Strain Rates (edited by Kawata, K. and Shioiri, J.) Springer-Verlag Tokyo 1995 105 112
    • (1995) Constitutive Relation in High/Very High Strain Rates , pp. 105-112
    • Shioya, T.1    Zhou, F.2
  • 42
    • 58149364799 scopus 로고
    • Ductile crack growth - I. A numerical study using computational cells with microstructurally-based length scales
    • L. Xia, C.F. Shih, Ductile crack growth - I. A numerical study using computational cells with microstructurally-based length scales Journal of Mechanics and Physics of Solids 1995 43 233 259
    • (1995) Journal of Mechanics and Physics of Solids , vol.43 , pp. 233-259
    • Xia, L.1    Shih, C.F.2


* 이 정보는 Elsevier사의 SCOPUS DB에서 KISTI가 분석하여 추출한 것입니다.