An investigation of the embrittlement in X20CrMoV12.1 power plant steel after long-term service exposure at elevated temperature

Materials Science and Engineering: A

Volumn 383, Issue 2, 2004, Pages 224-228

  Hu, Zheng Fei ^a   Yang, Zhen Guo ^b  

^a TONGJI UNIVERSITY   (China)

^b FUDAN UNIVERSITY   (China)

Author keywords

12 Cr heat resistant steel; Carbide coarsening; Embrittlement; Segregation

Indexed keywords

AUSTENITE; CARBIDES; DEGRADATION; EMBRITTLEMENT; GRAIN BOUNDARIES; MICROSTRUCTURE; POWER PLANTS; PRECIPITATION (CHEMICAL);

CARBIDE COARSENING; RETEMPERING; SERVICE EXPOSURE; STEAM PIPES;

STEEL;

STEEL;

EID: 11144249269     PISSN: 09215093     EISSN: None     Source Type: Journal    
DOI: 10.1016/j.msea.2004.05.080     Document Type: Article

References (10)

1. K. Borggreen, P.B. Mortensen, Long-term Properties of Fracture of X20CrMoV12.1, The Danish Corrosion Center, November 1989a
2. Hahn D.B. Bendick D.W. VGB Kraftwerks Technik 11 2000 85
3. Murphy M.C. Brance G.D. JISI 206 1968 266
4. Vodarek V. Strang A. Scripta Mat. 38 1998 101
5. P.J. Ennis, A. Zielinska-Lipiec, A. Filemonowicz, Quantitative comparison of the microstructure of high chromium steels for advanced power stations. In: A. Strang, J. Cawley, G.W. Greenwood (Eds.), Microstructure of High Temperature Materials, No.2, The Institute of Materials, 1998, p. 135
6. Eggeler G. Acta Metall. 37 1989 3225
7. P. Battaini, D. Dangelo, G. Marino, J. Hald, Interparticle distance evolution on steam pipes' 12% Cr steel during power plants' service time. In: B. Wilshire, R.W. Evans (Eds.), Proceedings of the 4th International Conference on Creep and Fracture of Engineering Materials and Structures, The Institute of Metals, 1-6 April 1990, p. 1039
8. Zheng-Fei H. Zhen-Guo Y. J. Mater. Eng. Perf. 12 2003 106
9. A. Strang, V. Vodarek, Microstructural stability of creep resistant martensitic 12% Cr steels. In: A. Strang, J. Cawley, G.W. Greenwood (Eds.), Microstructure of High Temperature Materials, No. 2, The Institute of Materials, 1998, p. 117
10. Viswanathan R. Metall. Trans. A 2 1971 809