Stress corrosion cracking of Al-Mg and Mg-Al alloys

Corrosion

Volumn 60, Issue 12, 2004, Pages 1144-1154

  Jones, R H ^a   Vetrano, J S ^a   Windisch, Jr ^a  

^a PACIFIC NORTHWEST NATIONAL LABORATORY   (United States)

Author keywords

Aluminum alloys; Magnesium alloys; Stress corrosion cracking

Indexed keywords

ALUMINUM ALLOYS; AUTOMOBILES; CRACK PROPAGATION; GRAIN BOUNDARIES; MAGNESIUM ALLOYS; PRECIPITATION (CHEMICAL);

GALVANIC-INDUCED CORROSION; SOLUTION-TREATED CONDITIONS;

STRESS CORROSION CRACKING;

ALUMINUM ALLOY; CORROSION; MAGNESIUM ALLOY; STRESS CORROSION CRACKING;

EID: 11044225696     PISSN: 00109312     EISSN: None     Source Type: Journal    
DOI: 10.5006/1.3299228     Document Type: Article

References (26)

1. R.H. Jones, D.R. Baer, M.J. Danielson, J.S. Vetrano, Met. Mater. Trans. A 32A (2001): p. 1, 699.
2. M.O. Speidel, M.V. Hyatt, Advances in Corrosion Science and Technology, vol. 2, eds. M.G. Fontana, R.W. Staehle (New York, NY: Plenum Press, 1972), p. 115.
3. A.F. Beck, P.R. Sperry, Fundamental Aspects of Stress Corrosion Cracking (Houston, TX: NACE International, 1969), p. 513.
4. D.O. Sprowls, R.H. Brown, Fundamental Aspects of Stress Corrosion Cracking (Houston, TX: NACE, 1969), p. 466.
5. J.R. Pickens, J.R. Gordon, J.A.S. Green, Metal. Trans. A 14A (1983): p. 925.
6. Z.F. Wang, P. Wang, C.L. Briant, K.S. Kumar, "The Effect of Microstructure on the Polarization and Stress Corrosion Cracking in Al-5Mg Alloys," paper no. 373, CORROSION/2000 (Houston, TX: NACE, 2000).
7. J.C. Chang, T.H. Chuang, Metal. Mater. Trans. A 30A (1999): p. 3,191.
8. T. Enjo, T. Kuroda, H. Shinonaga, Trans. JWRI 8, 1 (1979): p. 67.
9. M.C. Carroll, P.I. Gouma, M.J. Mills, G.S. Daehn, B.R. Dunbar, Sci. Mater. 42 (2000): p. 335.
10. J.S. Vetrano, R.E. Williford, R.H. Jones, "Influence of Microstructure and Thermal History on the Corrosion Susceptibility of AA5083," in Automotive Alloys I, ed. S. K. Das (Warrendale, PA: The Minerals, Metals, and Materials Society, 1997), p. 77.
11. J.L. Searles, P.I. Gouma, R.G. Buchheit, Metall. Mater. Trans. 32A (2001): p. 2,859-2,867.
12. P. Doig, J.W. Edington, Proc. R. Soc. London A 339 (1974): p. 37.
13. H. Yukawa, Y. Murata, M. Morinaga, Y. Takahashi, H. Yoshida, Acta Metall. Mater. 43 (1995): p. 681.
14. L.I. Kaigorodova, Mater. Sci. Forum 294-296 (1999): p. 477.
15. R.S. Stampella, R.P.M. Proctor, V. Ashworth, Corros. Sci. 24 (1984): p. 325.
16. W.K. Miller, "Stress Corrosion Cracking of Magnesium Alloys," in Stress Corrosion Cracking: Materials Performance and Evaluation, ed. R.H. Jones (Materials Park, OH: ASM International, 1992), p. 251-263.
17. E.C.W. Perryman, J. Inst. Met. 78 (1951-52): p. 621.
18. L. Fairman, J.M. West, Corros. Sci. 5 (1965): p. 711.
19. W.R. Wearmouth, G.P. Dean, R.N. Parkins, Corros. Sci. 29 (1973): p. 251.
20. K. Ebtehaj, D. Hardie, R.N. Parkins, Corros. Sci. 28 (1988): p. 811.
21. R.B. Mears, R.H. Brown, E.H. Dix, Jr., in Proc. Symp. on Corrosion Cracking (ASTM/AIME, 1945), p. 323.
22. G.O. Ilevbare, J.R. Scully, J. Yuan, R.G. Kelly, Corrosion 56 (2000): p. 227.
23. R.H. Jones, M.J. Danielson, "Role of Hydrogen in Stress Corrosion Cracking of Low-Strength Al-Mg Alloys," in Proc. Hydrogen Effects on Material Behavior and Corrosion Deformation Interactions, eds. N.R. Moody, A.W. Thompson, R.E. Ricker, G.S. Was, R.H. Jones, held Sept. 2002 (Warrendale, PA: TMS, 2003), p. HO1.
24. D. Tanguy, B. Bayle, R. Dif., Th. Magnin, Corros. Sci. 44 (2002): p. 1,163.
25. C. D. S. Tuck, "Evidence for the Formation of Magnesium Hydride on the Grain Boundaries of Al-Mg and Al-Zn-Mg Alloys During Their Exposure to Water Vapour," in Proc. 3rd Int. Conf. on Effect of Hydrogen on Behavior of Materials, eds. I.M. Bernstein, A.W. Thompson (Warrendale, PA: The Metallurgical Society of AIME, 1980), p. 503.
26. E.P. Simonen, R.H. Jones, C.F. Windisch, Jr., "A Transport Model for Characterizing Crack Tip Chemistry and Mechanics During Stress Corrosion Cracking," in New Techniques for Characterizing Corrosion and Stress Corrosion, ed. R.H. Jones (Warrendale, PA: TMS, 1996), p. 141.