Analysis of initiation and propagation of stress corrosion cracks in sensitized Type 304 stainless steel in high-temperature water

Corrosion

Volumn 60, Issue 12, 2004, Pages 1104-1112

  Haruna, T ^a   Zhang, S ^b   Shibata, T ^c  

^a OSAKA UNIVERSITY   (Japan)

^b NORTH CHINA ELECTRIC POWER UNIVERSITY   (China)

^c FUKUI UNIVERSITY OF TECHNOLOGY   (Japan)

Author keywords

Crack initiation; Crack propagation; High temperature water; In situ observation; Intergranular stress corrosion cracking; Sensitization; Sulfate

Indexed keywords

ACTIVATION ENERGY; CRACKS; GROWTH (MATERIALS); PROBABILITY DISTRIBUTIONS; THERMAL EFFECTS;

CUMULATIVE NUMBER; SLOW STRAIN RATES; STRESS CORROSION CRACKS;

CORROSION;

HIGH TEMPERATURE; STAINLESS STEEL; STRESS CORROSION CRACKING; TESTING;

EID: 11044220208     PISSN: 00109312     EISSN: None     Source Type: Journal    
DOI: 10.5006/1.3299224     Document Type: Article

References (28)

1. P.M. Scott, A.E. Truswell, "The Measurement of Crack Length and Shape During Fracture and Fatigue," ed. J. Beevers (Sheffield, U.K.: Engineering Materials Advisory Services, 1980), p. 69.
2. T. Hattori, S. Yamauchi, H. Kanazaki, Y. Kondo, T. Endo, Mitsubishi Juko Giho 23 (1986): p. 460 (in Japanese).
3. S. Nakajima, M. Kikuchi, M. Shima, "Automatic Measurement for Monitoring Crack Growth with Electric Potential Technique," JAERI-M82-149 (Ibaraki, Japan: Japan Atomic Energy Research Institute, 1982).
4. R.N. Parkins, Corrosion 46 (1990): p. 178.
5. T. Kawakubo, M. Hishida, Boshoku-Gijutsu (Corros. Eng.) 31 (1982): p. 19.
6. T. Kawakubo, M. Hishida, Corrosion 40 (1984): p. 120.
7. N. Nagata, Y. Katada, Tetsu-to-Hagane 74 (1988): p. 718.
8. T. Shibata, T. Haruna, Boshoku-Gijutsu (Corros. Eng.) 41 (1992): p. 809.
9. E. Kikuchi, T. Shibata, J. Kuniya, T. Haruna, Zairyo-to-Kankyo 44 (1995): p. 343.
10. S. Zhang, T. Shibata, T. Haruna, Corros. Sci. 39 (1997): p. 1,725.
11. S. Zhang, T. Shibata, T. Haruna, Corrosion 54 (1998): p. 428.
12. 2+ on IGSCC of Sensitized 304 Stainless Steel," Proc. Int. Conf. on Water Chemistry '98 (Tokyo, Japan: Japan Atomic Industrial Forum, Inc., 1998), p. 323.
13. S. Zhang, T. Shibata, T. Haruna, "Competition between Inhibition and Acceleration by Anions to IGSCC of Sensitized Type 304 Stainless Steel," Proc. of Int. Conf. on Water Chemistry '98 (Tokyo, Japan: Japan Atomic Industrial Forum, Inc., 1998), p. 839.
14. S. Zhang, T. Shibata, T. Haruna, Corros. Sci. 41 (1999): p. 853.
15. S. Zhang, T. Shibata, T. Haruna, Corrosion 55 (1999): p. 462.
16. S. Zhang, T. Shibata, T. Haruna, Corros. Sci. 42 (2000): p. 1,071.
17. T. Shibata, S. Zhang, T. Haruna, J. Phys. IV 10 (2000): p. PR6-185.
18. JIS-G 0580, "Method of Electrochemical Potentiokinetic Reactivation Ratio Measurement for Stainless Steels," Japan Industrial Standards (Tokyo, Japan: Japan Standards Association, 1986).
19. P.L. Andresen, Corrosion 38 (1982): p. 53.
20. W.E. Ruther, W.K. Soppet, T.F. Kassner, Corrosion 44 (1988): p. 791.
21. T. Haruna, Y. Fushiwaki, T. Shibata, "Effect of Temperature on Initiation and Propagation of Stress Corrosion Cracks by Direct Observation," Proc. Int. Symp. on Mechanism of Material Degradation and Non-Destructive Evaluation in Light Water Reactors, eds. S. Ishino, B.L. Eyre, I. Kimura (Fukui, Japan: Institute of Nuclear Safety System, Inc., 2002), p. 421-424.
22. P.L. Andresen, Corrosion, 49, 9 (1993): p. 714.
23. F.P. Ford, "Mechanisms of Environmental Cracking in Systems Peculiar to the Power Generation Industry," EPRI Contract RP 1332-1, EPRI Report NP2589 (Palo Alto, CA: Electric Power Research Institute, 1982).
24. F.P. Ford, M.J. Povich, Corrosion, 35 (1979): p. 569.
25. K. Agrawal, G.A. Welch, J.A. Begley, R.W. Staehle, "Stress Corrosion of Sensitized and Quench-Annealed Type 304 Stainless Steel in High-Purity Water," CORROSION/78, paper no. 187 (Houston, TX NACE International, 1978).
26. D.A. Hale, Trans. ASME 108, 1 (1986): p. 44.
27. E.L. White, W.E. Berry, W.K. Boyd, "Influence of Combined Environmental Effects on Stress Corrosion Cracking of Welded Stainless Steel Piping," EPRI Contract RP3113, 3rd Quarterly Report, Jul.-Dec. (Palo Alto, CA: Electric Power Research Institute, 1977).
28. E.D. Eason, J. Padmanaban, "A Model of Expected Time to Failure by IGSCC in 304 Stainless Steel," Report FAA-M-82-12-4 (Palo Alto, CA: Failure Analysis Associates, 1982).