The elucidation of load history editing effect on fatigue crack growth by crack closure concept

International Journal of Fatigue

Volumn 27, Issue 3, 2005, Pages 255-262

  Ko, Soon Gyu ^a   Oh, Chung Seog ^b   Choi, Byung Ik ^a  

^a Korea Institute of Machine and Materials   (South Korea)

^b Kumoh National Institute of Technology   (South Korea)

Author keywords

Crack closure; Fatigue crack growth; History editing; Random loading

Indexed keywords

ASPECT RATIO; BOLTS; FATIGUE OF MATERIALS; PARAMETER ESTIMATION; RANDOM PROCESSES; SPECTRUM ANALYSIS;

CRACK CLOSURE; FATIGUE CRACK GROWTH; HISTORY EDITING; RANDOM LOADING;

CRACK PROPAGATION;

EID: 10444244935     PISSN: 01421123     EISSN: None     Source Type: Journal    
DOI: 10.1016/j.ijfatigue.2004.07.009     Document Type: Article

References (29)

1. Conle A, Topper TH. Evaluation of small cycle omission criteria for shortening of fatigue service histories. Int J Fatigue 1979;1(1):23-8.
2. Buch A. Effect of some aircraft loading program modifications on the fatigue life of open hole specimens. Eng Fract Mech 1980;(13):237-56.
3. Heuler P, Seeger T. A criterion for omission of variable amplitude loading histories. Int J Fatigue 1986;8(4):225-30.
4. Lanciotti A, Lazzeri L. Effects of spectrum variations on fatigue crack growth. Int J Fatigue 1992;14(5):319-24.
5. Stephens RI, Dindinger PM, Gunger JE. Fatigue damage editing for accelerated durability testing using strain range and SWT parameter criteria. Int J Fatigue 1997;19(8/9):599-606.
6. Badaliance R, Dill HD, Potter JM. Effects of spectrum variations on fatigue life of composites. In: Daniel IM, editor. Composite Materials: Testing and Design (Sixth Conference), ASTM STP 787. Philadelphia, PA: American Society for Testing and Materials; 1982. p. 274-86.
7. Phillips EP. Effects of truncation of a predominantly compression load spectrum on the life of a notched graphite/epoxy laminate. Fatigue of Fibrous Composite Materials, ASTM STP 723. Philadelphia, PA: American Society for Testing and Materials; 1981 p. 197-212.
8. Nyman T, Ansell H, Blom A. Effects of truncation and elimination on composite fatigue life. Compos Struct 2000;(48):275-86.
9. Oh CS. Application of wavelet transform in fatigue history editing. Int J Fatigue 2001;23(3):241-50.
10. Lin XB, Smith RA. Fatigue shape analysis for corner cracks at fastener holes. Engng Fract Mech 1998;(59):73-87.
11. Grandt Jr AF, Macha DE. Digitized measurements of the shape of corner cracks at fastener holes. Engng Fract Mech 1983;(17):63-73.
12. van Dijk GM, de Jonge JB. Introduction to a fighter aircraft loading standard for fatigue evaluation - FALSTAFF. National Aerospace Laboratory, NLR, MP75017U, Amsterdam, Holland 1975.
13. Kikukawa M, Jono M, Tanaka K. Fatigue crack closure behavior at low stress intensity levels. Proc ICM, 2 1976 p. 254-77.
14. Kikukawa M, Jono M, Tanaka K, Kondo Y, Tabata F, Murata Y. Use of mini-computer for accurate automatic measurement in fatigue test. J Soc Mater Sci Jpn 1980;29:1240-6 [in Japanese].
15. Paris PC, Erdogan F. A critical analysis of crack propagation laws. Trans ASME J Basic Eng 1963;(85):528-34.
16. Annual Book of ASTM Standards, vol. 03.01, 2000, ASTM E606-92.
17. Annual Book of ASTM Standards, vol. 03.01, 2000, ASTM E1012-99.
18. Newman JC, Raju IS. Stress intensity factor equations for cracks in three-dimensional bodies subjected to tension and bending loads. Ch. 9. Computational methods in the mechanics of fracture. Amsterdam: Elsevier; 1986.
19. Empirical fit to unpublished boundary integral analysis at NASA/-Langley Research Center, Hampton, VA.
20. Kim JH, Song JH. Crack growth and closure behaviour of surface cracks under axial loading. Fatigue Fract Eng Mater Struct 1992;(15):477-89.
21. Oh CS, Song JH. Crack growth and closure behaviour of surface cracks under pure bending loading. Int J Fatigue 2001;(23):251-8.
22. Annual Book of ASTM Standards, Vol. 03.01, 2000, ASTM E647-99.
23. Lee SY, Song JH. Crack closure and growth behavior of physically short fatigue cracks under random loading. Eng Fract Mech 2000;(66):321-46.
24. Kim CY, Song JH. Fatigue crack closure and growth behavior under random loading. Eng Fract Mech 1994;(49):105-20.
25. Kikukawa M, Jono M, Kondo Y, Mikami S. Fatigue crack closure and estimation method of crack propagation rate under stationary varying loading conditions including random loading (1st report, effects of mean load and study on wave counting method). Trans JSME 1982;(48):1496-504.
26. Jono M, Song J, Kikukawa M. Fatigue crack growth and crack closure of structural materials under random loading. In: Proceedings of ICF, vol. 9; 1984, p. 1735-42.
27. Jono M, Song J, Sugeta A. Prediction of fatigue crack growth and closure under non-stationary random loading. In: Proceedings of ICOSSAR, vol. 4; 1985, p. 465-74.
28. Elber W, Fatigue crack closure under cyclic tension. Eng Fract Mech 1970;(2):37-45.
29. Suresh S, Ritchie RO. Some considerations on the modeling of oxide-induced fatigue crack closure using solutions for a rigid wedge inside a linear elastic crack. Scripta Metall 1983;(17):575-80.