Synthesis and structure of Na4/3Ce26/3(SiO4)6(F1/3O2/3)2; ionic conductivity in the apatite series Na4/3Ln26/3(SiO4)6(F1/3O2/3)2 (Ln = La, Ce, Gd) and Na4/3Ce26/3(SiO4)6O2

Chemistry of Materials

Volumn 16, Issue 25, 2004, Pages 5220-5222

  Maisonneuve, V ^a   Leduc, E ^a   Bohnke, O ^a   Leblanc, M ^a  

^a UNIVERSITÉ DU MAINE   (France)

Author keywords

[No Author keywords available]

Indexed keywords

CRYSTAL STRUCTURE; HIGH TEMPERATURE EFFECTS; HYDROTHERMAL SYNTHESIS; IONIC CONDUCTION; NEGATIVE IONS; POSITIVE IONS;

APATITES; HYDROTHERMAL METHODS;

COMPLEXATION;

ANION; APATITE; CATION; CERIUM; FLUORINE; OXIDE; SILICON DERIVATIVE; SODIUM; SODIUM DERIVATIVE;

ARTICLE; CHEMICAL ANALYSIS; CHEMICAL BOND; CHEMICAL STRUCTURE; COMPARATIVE STUDY; CONDUCTANCE; ELECTROCHEMISTRY; HIGH TEMPERATURE; STRUCTURE ANALYSIS; SYNTHESIS; TECHNIQUE; TEMPERATURE SENSITIVITY; X RAY CRYSTALLOGRAPHY;

EID: 10444241156     PISSN: 08974756     EISSN: None     Source Type: Journal    
DOI: 10.1021/cm048402j     Document Type: Article

References (16)

1. Archi, Y.; Sakai, H.; Yamamoto, O.; Takeda, Y.; Imanishi, N. Solid State Ionics 1999, 121, 133.
2. Takahashi, T. High Conductivity Solid Ionic Conductors; World Scientific: Singapore, 1987; p 402.
3. Nakayama, S.; Highchi, M. J. Mater. Sci. Lett. 2001, 20, 913.
4. Sansom, J. E. H.; Richings, D.; Slater, P. R. Solid State Ionics: 2001, 139, 205.
5. Abram, E. J.; Sinclair, D. C.; West, A. R. J. Mater. Chem. 2001, 11, 1978.
6. Arikawa, H.; Nishiguchi, H.; Ishihara, T.; Takita, Y. Solid State Ionics 2000, 136-137, 31.
7. Mercier, N.; Leblanc, M. Eur. J. Solid State Chem. 1993, 30, 195.
8. The structure was determined with SHELXL97 (Sheldrick, G. M. SHELXL97, A Program for Crystal Structure Determination; Göttingen University, Germany, 1997) from diffraction data obtained on a Siemens AED2 four-circle diffractometer.
9. Hughes, J. M.; Mariano, A. N.; Drexler, J. W. N. Jb. Miner. Mh. 1992, H7, 311.
10. 2 (approximately 2.3%) was detected.
11. Sansom, J. E. H.; Tolchard, J. R.; Slater, P. R.; Islam, M. S. Solid State Ionics 2004, 167, 17.
12. Platinum plating was deposited on the opposite faces of the pellets (ø ≈ 10 mm, thickness h ≈ 2 mm) and the total DC conductivity was determined under nitrogen atmosphere in the 1 Hz to 10 MHz range with a Solartron SI 1260 frequency response analyzer. Resistance was obtained by refinement of the impedance diagram using an equivalent circuit model of the ZVIEW software, based on the LEVM 6.0 program written by J. R. MacDonald (Z60 and ZVIEW, D. Johnson, Scribner Associates Inc, 1996).
13. Subbarao, E. C. In Science and Technology of Zirconia I; Heuer, A. H., Hobbs, L. W., Eds.; Vol. 3 of the Advances in Ceramics Series; American Ceramics Society: Columbus, OH, 1981.
14. Harwig, H. A., Gerards, A. G. J. Solid State Chem. 1978, 26, 265.
15. Lacorre, Ph., Goutenoire, F., Bohnke, O., Retoux, R., Laligant, Y. Nature 2000, 404, 856.
16. Nakayama, S., Sakamoto, M. J. Eur. Ceram. Soc. 1998, 18, 1413.