Structural modifications and fibre processing of hydroxy-functionalised mesogenic polyazomethines

Polymer

Volumn 44, Issue 26, 2003, Pages 7829-7841

  Adell, J M ^a   Alonso, M P ^a   Barbera J ^a   Oriol, L ^a   Pinol M ^a   Serrano, J L ^a  

^a CSIC   (Spain)

Author keywords

Mechanical properties; Nematic fibres; Polyazomethines

Indexed keywords

COPOLYMERIZATION; DIFFERENTIAL SCANNING CALORIMETRY; FIBERS; MELTING; MICROSTRUCTURE; SCANNING ELECTRON MICROSCOPY; STRUCTURE (COMPOSITION); TENSILE PROPERTIES; THERMODYNAMIC PROPERTIES; X RAY DIFFRACTION ANALYSIS;

FLEXIBLE SPACERS; STRUCTURAL ALTERATIONS;

ORGANIC POLYMERS;

2 METHYL 1,4 PHENYLENEDIAMINE; 4 METHYL 1,3 PHENYLENEDIAMINE; ALKANE DERIVATIVE; AZO COMPOUND; DIAMINE; HYDROXYL GROUP; IRON; NICKEL; UNCLASSIFIED DRUG; VANADIUM; ZINC;

ARTICLE; CHEMICAL MODIFICATION; CHEMICAL STRUCTURE; FIBER; MELTING POINT; POLYMERIZATION; REDUCTION; SYNTHESIS; TEMPERATURE DEPENDENCE; THERMAL ANALYSIS; X RAY DIFFRACTION;

POLYMER SCIENCE;

EID: 0742287175     PISSN: 00323861     EISSN: None     Source Type: Journal    
DOI: 10.1016/j.polymer.2003.10.032     Document Type: Article

References (16)

1. Demus D., Goodby J., Gray G.W., Spiess H.W., Vill V. Handbook of liquid crystals. High molecular weight liquid crystals. vol. 3:1998;VCH-Wiley, Weinheim.
2. Sawyer L.C., Jaffe M. J Mater Sci. 21:1986;1897.
3. Morgan PW, US Patent, 4122070, 1978.
4. Morgan P.W., Pletcher T.C., Kwolek S.L. Polym Prepr. 24:1983;470.
5. Morgan P.W., Kwolek S.L., Pletcher T.C. Macromolecules. 20:1987;729.
6. Wojtkowski P.W. Macromolecules. 20:1987;740.
7. Barberá J., Oriol L., Serrano J.L. Liq Cryst. 12:1992;37.
8. Barberá J., Cerrada P., Oriol L., Piñol M., Serrano J.L. Liq Cryst. 22:1997;483.
9. Cerrada P., Oriol L., Piñol M., Serrano J.L., Iribarren I., Muñoz-Guerra S. Macromolecules. 29:1996;2515.
10. Cerrada P., Oriol L., Piñol M., Serrano J.L., Alonso P.J., Puértolas J.A., Iribarren I., Muñoz-Guerra S. Macromolecules. 32:1999;3565.
11. Alonso P.J., Martínez J.I., Oriol L., Piñol M., Serrano J.L. Adv Mater. 6:1994;663.
12. Oriol L., Alonso P.J., Martínez J.I., Piñol M., Serrano J.L. Macromolecules. 27:1994;1869.
13. Cerrada P., Oriol L., Piñol M., Serrano J.L. J Am Chem Soc. 119:1997;7581.
14. Cerrada P., Oriol L., Piñol M., Serrano J.L. J Polym Sci: Part A, Polym Chem. 34:1996;2603.
15. Serrano J.L., Sierra T. Serrano J.L. Metallomesogens. Synthesis, properties and applications. 1996;VCH-Wiley, Weinheim.
16. Values obtained for as-spun fibres were 8.9 GPa, 252 MPa and 3.3% for the elastic modulus, tensile strength and elongation at break, respectively. For thermally annealed fibres under tension the corresponding values were 18.4 GPa, 388 MPa and 2.2% Data taken from Ref. [9].