Fatigue life prediction of cross-ply composite laminates

Materials Science and Engineering: A

Volumn 238, Issue 2, 1997, Pages 329-335

  Song, Dong Yeul ^a   Otani, Nobuo ^b  

^a JAPAN FINE CERAMICS CENTER   (Japan)

^b MAEBASHI INSTITUTE OF TECHNOLOGY   (Japan)

Author keywords

CFRP laminates of 0 90 s; Crack density; Fatigue life; Number of cycles; Residual critical strength; Stress amplitude ratio

Indexed keywords

DAMAGE; FATIGUE LIFE ANALYSIS;

CRACKS; FAILURE ANALYSIS; FATIGUE OF MATERIALS; INTERFACES (MATERIALS); LAMINATED COMPOSITES; RESIDUAL STRESSES; STRENGTH OF MATERIALS;

CRACK DENSITY; STRESS AMPLITUDE RATIO;

CARBON FIBER REINFORCED PLASTICS;

EID: 0347245203     PISSN: 09215093     EISSN: None     Source Type: Journal    
DOI: 10.1016/S0921-5093(97)00427-9     Document Type: Article

References (14)

1. R.Y. Kim, W.J. Park, J. Comp. Mat. 14 (1980) 69.
2. G.P. Sendecky, ASTM STP 734 (1981) 245.
3. W.B. Hwang, K.S. Han, ASTM STP 1012 (1989) 87.
4. J.N. Yang, M.D. Liu, J. Comp. Mat. 11 (1977) 176.
5. B. Harris, Fatigue Testing of Fibre Composite, AGARD Lect. Ser. No. 118 (1981) 6.1.
6. A. Kobayashi, N. Otani, Evalution of Materials Degradation Due to Cyclic Loading in Composites, in: A. Salvetti, G. Cavallini (Eds.), Durability and Damage Tolerance in Aircraft Design, Emas, 1985, 247 pp.
7. Y. Lin, Comp. Sci. Technol. 36 (1989) 339.
8. S. Liu, J.A. Nairn, Proc. 5th Tech. Comp. Mat., 1990, 287 pp.
9. S.L. Ogin, P.A. Smith, P.W.R. Beaumont, Comput. Sci. Technol. 24 (1985) 47.
10. N. Otani, D.Y. Song, J. Mater. Sci. 32 (3) (1997) 755.
11. K.L. Reifsnider, A.L. Highsmith, Materials: Experimentation and Design in Fatigue, Westbury House, 1981, 246 pp.
12. A. Kobayashi, N. Otani, Proc. 3rd. Japan-US Comp. Mat., JSCM, 1986, 133 pp.
13. V.D. Azzi, S.W. Tsai, Exp. Mech. 5 (1965) 286.
14. O.H. Griffin, J. Comp. Mat. 17 (1983) 449.