Near the static fatigue limit in glass

International Journal of Fracture

Volumn 121, Issue 1-2, 2003, Pages 1-7

  Wiederhorn, S M ^a   Dretzke, A ^b   Rodel J ^b  

^a NATIONAL INSTITUTE OF STANDARDS AND TECHNOLOGY   (United States)

^b DARMSTADT UNIVERSITY OF TECHNOLOGY   (Germany)

Author keywords

Atomic force microscopy; Ceramics; Crack growth; Glass; Static fatigue limit; Stress corrosion

Indexed keywords

ATOMIC FORCE MICROSCOPY; CRACK PROPAGATION; FATIGUE TESTING; FRACTURE TOUGHNESS; LEACHING; LIME; SILICATES; STRESS CORROSION CRACKING;

STATIC FATIGUE LIMITS;

GLASS;

ATOMIC FORCE MICROSCOPY; CERAMICS; CORROSION RATE; CRACK PROPAGATION; FRACTURE TOUGHNESS; GLASS; STRESS CORROSION CRACKING;

EID: 0345686404     PISSN: 03769429     EISSN: None     Source Type: Journal    
DOI: 10.1023/A:1026274817003     Document Type: Article

References (9)

1. Charles, R.J. and Hollig, W.B. (1962). in Symposium on Mechanical Strength of Glass and Ways of Improving It, pp. 25-29. Union Scientifique Continentale du Verre, Charleroi, Belgium.
2. Chuan, T.-J. and Fuller, E.R., Jr. (1992). J. Am. Ceram. Soc. 75, 540.
3. Gehrke, E. and Ullner, Ch. (1988). Application of Fractography of Glass to the Study of Environmental Effects on Crack Growth. pp. 77-87 in Advances in Ceramics, V. 22, Fractography of Glasses and Ceramics, Edited by V.D. Fréchette and J.R. Varner), The Americal Ceramic Society, Inc. Westerville OH.
4. Gehrke, E. Ullner, Ch., and Hähnert, M. (1991). J. Mater. Sci. 26, 5445.
5. Guin, J.-P. and Wiederhorn, S.M. (2003). J. Non-Crystalline Solids 316, 12.
6. Hénaux, S. and Cruezet, F. (1997). J. Am. Sci. Let. 16, 1008.
7. Kocer, J. and Collins R.E. (2001). J. Am. Ceram. Soc. 84, 2585.
8. Michalske, T.A. (1977) in Fracture Mechanics of Ceramics, Vol. 5, Surface Flaws, Statistics, and Microcracking, pp. 277-289, (Edited by Bradt, R.C., Evans, A.G., Hasselman, D.P.H. and Lange, F.F.) Plenum Press, New York.
9. Wiederhorn, S.M. and Bolz, L.H. (1970). J. Am. Ceram. Soc. 53, 543.