The effect of potential on the high-temperature fatigue crack growth response of low alloy steels, part 2: Sulfide-potential interaction

Corrosion Science

Volumn 41, Issue 2, 1998, Pages 401-415

  Moshier, W C ^a   James, L A ^a  

^a WESTINGHOUSE ELECTRIC COMPANY   (United States)

Author keywords

[No Author keywords available]

Indexed keywords

ANODIC POLARIZATION; CORROSION FATIGUE; CRACK INITIATION; CRACK PROPAGATION; ELECTRIC POTENTIAL; HYDROGEN SULFIDE; OXIDATION; THERMAL EFFECTS;

ENVIRONMENTALLY ASSISTED CRACKING (EAC);

STEEL CORROSION;

CRACK PROPAGATION; FATIGUE CRACK; STEEL; SULFIDE;

EID: 0345643344     PISSN: 0010938X     EISSN: None     Source Type: Journal    
DOI: 10.1016/S0010-938X(98)00111-5     Document Type: Article

References (16)

1. J.D. Atkinson, J. Yu, Z.-Y. Chen, Corros. Sci. 38(5) (1996) 755.
2. H. Hänninen, K. Törrönen, M. Kemppainen, S. Salonen, Corros. Sci. 23(6) (1983) 663.
3. H. Hänninen, W. Cullen, M. Kemppainen, Corrosion 46(7) (1990) 563.
4. W.A. Van Der Sluys, R.H. Emanuelson, in Third International Symposium on Environment Degradation of Materials in Nuclear Power Systems - Water Reactors. TMS-AIME, 1988, p. 277.
5. L.A. James, W.A. Moshier, Corros. Sci. (this issue).
6. Y. Katada, N. Nagata, S. Sato, ISIJ International 33(8) (1993) 877.
7. J.D. Atkinson, Fourth International Symposium on Environment Degradation of Materials in Nuclear Power Systems - Water Peactors, NACE, 1990, pp. 8-64.
8. G. Gabetta, E. Caretta, Corrosion Chemistry Within Pits, Crevices and Cracks. Her Majesty's Stationery Office, London, 1987, p. 287.
9. P.L. Andresen, L.M Young, Corrosion 51(3) (1995) 223.
10. D.D. Macdonald, H. Song, K. Makela, K. Yoshida, Corrosion 49(1) (1993) 8.
11. L.A. James, J. Pressure Vessel Technology 116 (1994) 122.
12. D.D. Macdonald, A.C. Scott, P. Wentrcek, J. Electrochem Soc. 126(9) (1979) 1618.
13. P. Cohen. (Ed.), The ASME Handbook on Water Technology for Thermal Power Systems, ASME, New York, NY, 1989.
14. M.E. Indig, K.B. Groot, Corrosion 25 (1974) 92.
15. T. Zakroczymski, in: R.A. Oriani, J.P. Hirth, M. Smialowski, (Ed.), Hydrogen Degradation of Ferrous Alloys . Noyes Publications, Park Ridge, New Jersey, 1985, p. 215.
16. G.L. Wire, Y.Y. Li, Fatigue and Fracture - 1996, Vol. 1. ASME Publication PVP - Vol. 323, 1996, pp. 269-289.