Volumn 26, Issue 3, 2004, Pages 211-219

In-situ SEM study of fatigue crack growth behaviour in IN718

Author keywords

Crack closure; Fatigue; In situ fatigue experiment; IN718; Paris regime; SEM; Slip bands

Indexed keywords

ALUMINUM ALLOYS; DEFORMATION; FATIGUE OF MATERIALS; FRACTURE; MICROCRACKS; MICROSTRUCTURE; SCANNING ELECTRON MICROSCOPY; STRESS INTENSITY FACTORS; SURFACE ROUGHNESS;

EID: 0345375305     PISSN: 01421123     EISSN: None     Source Type: Journal    
DOI: 10.1016/S0142-1123(03)00172-5     Document Type: Article
Times cited : (87)

References (15)
  • 1
    • 0030233496 scopus 로고    scopus 로고
    • Crack closure effect on crack growth rate at 650 °C in double notched specimens of a nickel base superalloy
    • Pommier S., Prioul C., Lautridou J.C., Bompard P. Crack closure effect on crack growth rate at 650 °C in double notched specimens of a nickel base superalloy. Fatigue Fract Eng Mater Struct. 19:(9):1996;1117-1128.
    • (1996) Fatigue Fract Eng Mater Struct , vol.19 , Issue.9 , pp. 1117-1128
    • Pommier, S.1    Prioul, C.2    Lautridou, J.C.3    Bompard, P.4
  • 2
    • 0035479428 scopus 로고    scopus 로고
    • Crack growth in IN718 at high temperature
    • Andersson H., Persson C., Hansson T. Crack growth in IN718 at high temperature. Int J Fatigue. 23:(9):2001;817-827.
    • (2001) Int J Fatigue , vol.23 , Issue.9 , pp. 817-827
    • Andersson, H.1    Persson, C.2    Hansson, T.3
  • 3
    • 0029324726 scopus 로고
    • In-situ SEM measurements of crack closure for small fatigue cracks in aluminium 2024-T351
    • Halliday M.D., Poole P., Bowen P. In-situ SEM measurements of crack closure for small fatigue cracks in aluminium 2024-T351. Fatigue Fract Eng Mater Struct. 18:(6):1995;717-729.
    • (1995) Fatigue Fract Eng Mater Struct , vol.18 , Issue.6 , pp. 717-729
    • Halliday, M.D.1    Poole, P.2    Bowen, P.3
  • 4
    • 0034427556 scopus 로고    scopus 로고
    • Small crack growth and fatigue life predictions for high-strength aluminium alloys. Part II: Crack closure and fatigue analysis
    • Newman J.C., Wu X.R., Swain M.H., Zhao W., Philips E.P., Ding C.F. Small crack growth and fatigue life predictions for high-strength aluminium alloys. Part II: crack closure and fatigue analysis. Fatigue Fract Eng Mater Struct. 23:(1):2000;59-72.
    • (2000) Fatigue Fract Eng Mater Struct , vol.23 , Issue.1 , pp. 59-72
    • Newman, J.C.1    Wu, X.R.2    Swain, M.H.3    Zhao, W.4    Philips, E.P.5    Ding, C.F.6
  • 5
    • 0032114733 scopus 로고    scopus 로고
    • On plane stress-plane strain interactions in fatigue crack growth
    • Bao H., McEvily A.J. On plane stress-plane strain interactions in fatigue crack growth. Int J Fatigue. 20:(6):1998;441-448.
    • (1998) Int J Fatigue , vol.20 , Issue.6 , pp. 441-448
    • Bao, H.1    Mcevily, A.J.2
  • 6
    • 0033227627 scopus 로고    scopus 로고
    • eff estimation procedures on 6061-T and 2024-T3 aluminum alloys
    • eff estimation procedures on 6061-T and 2024-T3 aluminum alloys. Int J Fatigue. 21:(S1):1999;S47-S57.
    • (1999) Int J Fatigue , vol.21 , Issue.S1 , pp. 47-S57
    • Donald, K.1    Paris, P.C.2
  • 7
    • 0033227521 scopus 로고    scopus 로고
    • Service load fatigue damage - A historical perspective
    • Paris P.C., Tada H., Donald J.K. Service load fatigue damage - a historical perspective. Int J Fatigue. 21:(S1):1999;S35-S46.
    • (1999) Int J Fatigue , vol.21 , Issue.S1 , pp. 35-S46
    • Paris, P.C.1    Tada, H.2    Donald, J.K.3
  • 8
    • 0035214679 scopus 로고    scopus 로고
    • A fatigue crack driving force parameter with load ratio effects
    • Kujawski D. A fatigue crack driving force parameter with load ratio effects. Int J Fatigue. 23:(S1):2001;S239-S246.
    • (2001) Int J Fatigue , vol.23 , Issue.S1 , pp. 239-S246
    • Kujawski, D.1
  • 9
    • 0036833142 scopus 로고    scopus 로고
    • High temperature fatigue crack growth in two metals under constant and variable amplitude loading
    • Månson T., Skantz J., Nilsson F. High temperature fatigue crack growth in two metals under constant and variable amplitude loading. Int J Fatigue. 24:(11):2002;1159-1168.
    • (2002) Int J Fatigue , vol.24 , Issue.11 , pp. 1159-1168
    • Månson, T.1    Skantz, J.2    Nilsson, F.3
  • 11
    • 0344578055 scopus 로고    scopus 로고
    • Micromechanisms of fatigue crack growth in a forged Inconel 718 nickel-based superalloy
    • Mercer C., Soboyejo A.B.O., Soboyejo W.O. Micromechanisms of fatigue crack growth in a forged Inconel 718 nickel-based superalloy. Mater Sci Eng. A270:(2):1999;308-322.
    • (1999) Mater Sci Eng , vol.A270 , Issue.2 , pp. 308-322
    • Mercer, C.1    Soboyejo, A.B.O.2    Soboyejo, W.O.3
  • 12
    • 0014577059 scopus 로고
    • Coarse slip model of fatigue
    • Neumann P. Coarse slip model of fatigue. Acta Metall. 17:1969;1219-1225.
    • (1969) Acta Metall , vol.17 , pp. 1219-1225
    • Neumann, P.1
  • 13
    • 0024874061 scopus 로고
    • Three-dimensional aspects of plasticity-induced fatigue crack closure
    • Chermahini R.G., Shivakumar K.N., Newman J.C., Blom A.F. Three-dimensional aspects of plasticity-induced fatigue crack closure. Eng Fract Mech. 34:(2):1989;393-401.
    • (1989) Eng Fract Mech , vol.34 , Issue.2 , pp. 393-401
    • Chermahini, R.G.1    Shivakumar, K.N.2    Newman, J.C.3    Blom, A.F.4
  • 15
    • 0014809315 scopus 로고
    • Fatigue crack closure under cyclic tension
    • Elber W. Fatigue crack closure under cyclic tension. Eng Fract Mech. 2:(1):1970;37-45.
    • (1970) Eng Fract Mech , vol.2 , Issue.1 , pp. 37-45
    • Elber, W.1


* 이 정보는 Elsevier사의 SCOPUS DB에서 KISTI가 분석하여 추출한 것입니다.