The influence of material mismatch on the evaluation of time-dependent fracture mechanics parameters

Engineering Fracture Mechanics

Volumn 64, Issue 6, 1999, Pages 765-780

  Tu, Shan Tung ^a   Yoon, Kee Bong ^b  

^a NANJING TECH UNIVERSITY   (China)

^b Chung Ang University   (South Korea)

Author keywords

Creep crack growth; Material mismatch; Testing standard; Time dependent fracture; Weld

Indexed keywords

CRACK PROPAGATION; CREEP; FINITE ELEMENT METHOD; LOADS (FORCES); STRENGTH OF MATERIALS;

MATERIAL MISMATCH; TIME-DEPENDENT FRACTURE;

FRACTURE MECHANICS;

CRACK; CREEP; CREEP TEST; FRACTURE MECHANICS;

EID: 0342546010     PISSN: 00137944     EISSN: None     Source Type: Journal    
DOI: 10.1016/S0013-7944(99)00083-1     Document Type: Article

References (18)

1. Maddox S.J. Fatigue strength of welded structures. 1985;Abington Publishing.
2. Coleman M.C., Parker J.D., Walters D.J. The behavior of ferritic weldment in thick section 1/2Cr1/2Mo1/4 V pipe at elevated temperature. Int. J. Pres. Ves. & Piping. 18:1985;277-310.
3. DeWitte M., Cossement G. Creep behavior of 2.25Cr1Mo base material and weldments. Proceedings of VGB-Conferemce "Residual Service Life 1992", Mannheim, 6-7 July 1992. 1992;38.1-38.28.
4. Prager M. Issues in life assessment of chrome-moly welds. Serviceability of petroleum, process and power equipment. vol. PVP-Vol.239:1992;253-265 ASME, New York.
5. Tu S.T., Wu R., Sandstrom R. Design against creep failure for weldments in 0.5Cr0.5Mo 0.25 V pipe. Int. J. Pres. Ves. & Piping. 58:1994;345-354.
6. Hall F.R., Hayhurst D.E. Continuum damage mechanics modeling of high temperature deformation and failure in a pipe weldment. Proc. R. Soc. Lond. A. 433:1991;383-403.
7. Tu S.T., Sandstrom R. Numerical simulation of creep exhaustion of weldments and some design considerations. Wilshire B., Evans R.E. Proceedings of the Fifth International Conference on Creep and Fracture of Engineering Materials and Structures. 1993;695-704 Institute of Materials.
8. ASTM Standard E1457. Standard test method for measurement of creep crack growth rates in metals, 1992.
9. Saxena A, Liaw PK. Remaining life assessment of boiler pressure parts - crack growth studies. Report No. EPRI-CS 4688, Electric Power Research Institute, Palo Alto, CA, 1986.
10. Saxena A, Han J, Banerji K. Creep crack growth behaviour in power plant boiler and steam pipe steels. EPRI Report on Project 2253-10, Electric Power Research Institute, Palo Alto, CA, April, 1987.
11. McCarthy P.R., Shibli I.A., Raynor D. A survey of European creep crack growth data generation from weldments and recommendations for a draft code of practice. Proceedings of International HIDA Conference on Creep and Fatigue Crack Growth in High Temperature Plant, 15-17 April, Paris, France. 1998;S2-12.
12. Segle P., Andersson P., Samuelson L. A parameteric study of creep growth in heterogenous CT specimens by use of finite element simulations. Proceedings of International HIDA Conference on Creep and Fatigue Crack Growth in High Temperature Plant, 15-17 April, Paris, France. 1998;S2-17.
13. Tu S.T., Yoon K.B. Welding effect on the structural integrity at high temperature. Proceedings of 1998 Annual Meeting of Korean Welding Society. 1998;11-24 KWS. (Invited Lecture).
14. Tu S.T., Sandstrom R. The evaluation of weldment creep strength reduction factors by experiment and numerical simulations. Int. Pres. Ves. & Piping. 57:1994;335-344.
15. ABAQUS, Version 5.7. Hibbit, Karlsson and Sorensen, Inc, 1997.
16. Riedel R., Rice J.R. Tensile cracks in creeping solids. Proceedings of Fracture Mechanics, 12th Conference, ASTM STP 700. 1980;112-130.
17. Ohji K., Kubo S. Fracture mechanics evaluation of crack growth behaviour under creep and creep fatigue conditions. Ohtani R., Ohnami M., Inoue T. High temperature creep-fatigue. 1988;91-113 Elsevier, London.
18. Shih CF. Tables of Hutchinson-Rice-Rosengren singular field quantities. Material Research Laboratories, Brown University, MRL E-147, 1983.