Influence of LCF overloads on combined HCF/LCF crack growth

International Journal of Fatigue

Volumn 25, Issue 9-11, 2003, Pages 827-834

  Byrne, J ^a   Hall, R F ^a   Powell, B E ^a  

^a UNIVERSITY OF PORTSMOUTH   (United Kingdom)

Author keywords

Combined high and low cycle fatigue; Fatigue crack growth; Fatigue thresholds; Overloads; Ti 6Al 4V

Indexed keywords

CRACK PROPAGATION; CRACKS; LOADS (FORCES); STRESS INTENSITY FACTORS;

FATIGUE THRESHOLDS;

FATIGUE OF MATERIALS;

EID: 0242577791     PISSN: 01421123     EISSN: None     Source Type: Journal    
DOI: 10.1016/S0142-1123(03)00131-2     Document Type: Conference Paper

References (15)

1. Nicholas T. Critical issues in high cycle fatigue. Int J Fatigue. 21:(Suppl 1):1999;S221-S231.
2. Powell B.E., Duggan T.V., Jeal R.H. The influence of minor cycles on low cycle fatigue crack propagation. Int J Fatigue. 4:1982;4-14.
3. Powell B.E., Duggan T.V. Predicting the onset of high cycle fatigue damage: an application for long crack threshold data. Int J Fatigue. 8:1986;187-194.
4. Powell B.E., Hall R.F., Hawkyard M. The effect of superimposed vibrational stresses on low cycle fatigue crack propagation behaviour. Rie K-T. Third International Conference on Low Cycle Fatigue and Elasto-Plastic Behaviour of Materials, Berlin:1992;552-557 Elsevier.
5. Powell B.E. Crack growth in Ti-6Al-4V under the conjoint action of high and low cycle fatigue. Int J Fatigue. 9:1987;195-202.
6. Powell B.E. Fatigue crack growth behaviour of two contrasting titanium alloys. Int J Fatigue. 17:1995;221-227.
7. Hawkyard M., Powell B.E., Hussey I., Grabowski L. Fatigue crack growth under the conjoint action of major and minor stress cycles. Fatigue Fract Eng Mater Struc. 19:1996;217-227.
8. Evans W.J., Medwell N., Spence S.H. The effect of major-minor cyclic combinations on crack propagation lifing criteria. Twelfth International Symposium on Air Breathing Engines:1995;185 USA: American Institute of Aeronautics and Astronautics.
9. Hall R.F., Powell B.E. The effect of temperature on the growth of cracks subjected to combined major and minor stress cycles. Moura Branco C., Ritchie R.O., Sklenicka V. Mechanical behaviour of materials at elevated temperature. 1996;227-235 Kluwer Academic Publishers.
10. Hall R.F., Powell B.E. Crack growth in IMI 829 at 550 °C under combined high and low cycle fatigue. Mater High Temp. 19:(1):2002;1-8.
11. Hawkyard M., Powell B.E., Stephenson J.M., McElhone M. Fatigue crack growth from simulated flight cycles involving superimposed vibrations. Int J Fatigue. 21:(Suppl 1):1999;S59-S68.
12. Pickard AC. The application of 3-dimensional finite element methods to fracture mechanics and fatigue life predictions. EMAS; 1986.
13. Sadananda K., Vasudevan A.K., Holtz R.L., Lee E.U. Analysis of overload effects and related phenomena. Int J Fatigue. 21:(Suppl 1):1999;S233-S246.
14. Hopkins S.W., Rau C.A., Leverant G.R., Yuen A. Effect of various programmed overloads on the threshold for high frequency fatigue crack growth. Fatigue crack growth under spectrum loads. ASTM STP 505:1976;125-141 ASTM.
15. Wheeler O.E. Spectrum loading and crack growth. J Basic Eng. 94:1972;181-186.