EFFECT OF DIFFERENT THERMAL CYCLES ON TBC SPALLATION LIFETIME

ASME International Mechanical Engineering Congress and Exposition, Proceedings (IMECE)

Volumn 1998-X, Issue , 1998, Pages 33-41

  Nusier, S Q ^a   Newaz, G M ^a   Chaudhury, Z A ^a   Chen, X ^a   Khan, J M ^a  

^a Wayne State University   (United States)

Author keywords

[No Author keywords available]

Indexed keywords

AIRCRAFT ENGINES; FICK'S LAWS; GAS TURBINES; SPALLING; THERMAL BARRIER COATINGS; YTTRIA STABILIZED ZIRCONIA; YTTRIUM OXIDE;

FICK'S LAW; HOLDING TIME; MAXIMUM TEMPERATURE; MINIMUM TEMPERATURES; NUMBER OF CYCLES; OXIDE THICKNESS; THERMALLY GROWN OXIDE; THERMALLY-GROWN OXIDE;

THERMAL CYCLING;

EID: 0242499732     PISSN: None     EISSN: None     Source Type: Conference Proceeding    
DOI: 10.1115/IMECE1998-0358     Document Type: Conference Paper

References (18)

1. Aifantis, E. C., 1980, "On the Problem of Diffusion in Solids", Acta Mechanica, Vol. 37, pp. 265-296.
2. Barrett, C.A., and Lowell, C.E., 1975, Oxidation of Metals, 9:307-355 Brindley, W. J., 1995, "Properties of Plasma Sprayed Bond Coats, Proceedings of TBC Workshop, NASA-LeRC, pp. 189-202
3. Chaudhury, Z. A., Newaz, G. M., Nusier, S. Q. and Ahmed, T., 1997, "Interfacial Damage in EB-PVD Thermal Barrier Coatings Due to Thermal Cycling", accepted in the J. of Materials Science and Engineering.
4. Chaudhury, Z. A., Newaz, G. M., Nusier, S. Q., Ahmed, T., and R. L. Thomas, 1997, "Chronological Evaluation of Interfacial Damage in TBC Due to Thermal Cycling", accepted in the J. of Materials Science (July, 1997).
5. DeMasi-Marcin, J.T., Sheffler, K.D. and Bose, S., 1989, "Mechanisms of Degradation and Failure in a Plasma Deposited Thermal Barrier Coating," ASME Paper 89-GT-132, New York:American Society of Mechanical Engineers.
6. Hillery, R.V., Pilsner, B.H., Mcknight, R.L., Cook, T.S. and Hartle, M.S., 1988, "Thermal Barrier Coating Life Prediction Model Development," Final Report, NASA-CR-180807, Washington, DC: National Aeronautics and Space Administration.
7. Manning-Meier, S.M., Nissley, D.M., Sheffler, K.D. and Cruse, T.A., 1991, "Thermal Barrier Coating Life Prediction Model Development," ASME Paper 91-GT-40. New York: American Society of Mechanical Engineers.
8. Miller, R.A., and Lowell, C.E., 1982, "Failure Mechanisms of Thermal Barrier Coatings Exposed to Elevated Temperatures," Thin Solid Films, 95(3):265-273.
9. Newaz, G. M., Nusier, S. Q., and Chaudhury, Z. A., 1998, "Damage Accumulation Mechanisms in Thermal Barrier Coatings", J. of Eng. Mat. & Tech., Vol. 120, pp. 149-153.
10. Neu, R. W., and Sehitoglu H., 1989, "Thermomechanical Fatigue, Oxidation, and Creep: Part I. Damage Mechanisms", Met. Trans., A 20A, pp. 1755-1767.
11. Neu, R. W, and Sehitoglu H., 1989, "Thermomechanical Fatigue, Oxidation, and Creep: Part II. Life Prediction", Met. Trans. A 20A, pp. 1769-1783.
12. Nusier, S. Q., Newaz, G. M., and Chaudhury, Z. A., "Experimental and Analytical Evaluation of Damage Processes in Thermal Barrier Coatings", submitted to International Journal of Solids and Structures, June, 1997, (Revised on April 1998).
13. Probst, H. B., and Lowell, C. E., 1988, "Computer Simulation of Cyclic Oxidation", Journal of Metals, 40(10): 18.
14. Strangman. T.E., 1985, "Thermal Barrier Coatings for Turbine Airfoils", Thin Solid Films, 127:93-105.
15. Wittig, L. A., I993, "A Micromechanical Model of Oxidation Effects in SiC/Ti Metal Matrix Composites", Master's thesis, Texas A&M University, College Station, Texas.
16. Wittig, L. A., and Allen, D. H., 1994, "Modeling the Effects of Oxidation on Damage in SiC/Ti-15-3 Metal Matrix Composites", J. of Eng. Mat. and Tech. 116, pp.421-427.
17. Wright, K.P., 1996, Private Communication, GE - Evendale, Ohio.
18. Wright, I.G., Sethis, V.K. and Nagarajan, V., 1991, "An Approach to Describing the Simultaneous Erosion and High-Temperature Oxidation of Alloys," Journal of Engineering for Gas Turbines and Power, 113(October):616.