Failure of a 17-4 PH stainless steel sailboat propeller shaft

Engineering Failure Analysis

Volumn 10, Issue 6, 2003, Pages 711-717

  Arisoy, C Fahir ^a   Başman, Gokhan ^a   Şeşen, M Kelami ^a  

^a ISTANBUL TECHNICAL UNIVERSITY   (Turkey)

Author keywords

Failure analysis; Fatigue; Martensite; Shafts; Stress corrosion cracking

Indexed keywords

FAILURE ANALYSIS; FRACTURE; PROPELLERS; SHAFTS (MACHINE COMPONENTS); STRESS CORROSION CRACKING;

PROPELLER SHAFTS;

STAINLESS STEEL;

FAILURE ANALYSIS; PROPELLER SHAFT; STAINLESS STEEL;

EID: 0142259697     PISSN: 13506307     EISSN: None     Source Type: Journal    
DOI: 10.1016/S1350-6307(03)00041-4     Document Type: Article

References (10)

1. Spotts MF. Design of machine elements. 4th ed. 1971.
2. Hsiao C.N. Chiou C.S. Yang J.R. Aging reactions in a 17-4 PH stainless steel Materials Chemistry and Physics 74 2002 134-142
3. Failure analysis and prevention, vol. 11. In: ASM metals handbook. 10th ed. ASM International; 1993.
4. Tsay L.W. Yang T.Y. Young M.C. Embrittlement of laser surface-annealed 17-4 PH stainless steel Mat. Sci. Eng. A311 2001 64-73
5. El Hilali F. Habashi M. Mohsine A. Comportement mécanique de l'acier inoxydable martensitique 17-4 PH en corrosion sous contrainte et àla fragilisation par l'hydrogène environnemental Ann. Chim. Sci. Mat. 24 1999 169-194
6. Komai K. Failure analysis and prevention in SCC and corrosion fatigue cases Int. J. Fat 20 2 1998 145-154
7. Wulpi, DJ. Understanding how components fail. 2nd ed. The Materials Information Society; 1999.
8. Colangelo VJ, Heiser FA. Analysis of metallurgical failures. USA: John Wiley - Sons; 1974.
9. Fatigue and fracture, vol. 19. In: ASM metals handbook. 10th ed. ASM International; 1993.
10. Wegst C.W. Stahlschlüssel 1989 D-7142 Marbach Verlag Stahlschlüssel Wegst GMBH