Stress intensity formulas for three-dimensional cracks in homogeneous and bonded dissimilar materials

Engineering Fracture Mechanics

Volumn 71, Issue 1, 2004, Pages 1-15

  Noda, Nao Aki ^a  

^a KYUSHU INSTITUTE OF TECHNOLOGY   (Japan)

Author keywords

Bimaterial interface; Defects; Fracture mechanics; Stress intensity factor; Three dimensional cracks; area parameter

Indexed keywords

CRACKS; LOADING; STRESS INTENSITY FACTORS;

ELLIPTICAL CRACKS;

FRACTURE MECHANICS;

FRACTURE MECHANICS; LAMINATED MATERIAL;

EID: 0141993237     PISSN: 00137944     EISSN: None     Source Type: Journal    
DOI: 10.1016/S0013-7944(03)00101-2     Document Type: Article

References (11)

1. Murakami Y. Nemat-Nasser S. Growth and stability of surface flaws of arbitrary shape Engng. Fract. Mech. 17 3 1983 193-210
2. Murakami Y. Analysis of stress intensity factors of modes I, II and III for inclined surface cracks of arbitrary shape Engng. Fract. Mech. 22 1 1985 101-114
3. Murakami Y. Endo M. Quantitative evaluation of fatigue strength of metals containing various small defects or cracks Engng. Fract. Mech. 17 1 1983 1-15
4. Murakami Y. Kodama S. Konuma S. Quantitative evaluation of effects of nonmetallic inclusions on fatigue strength of high strength steel Trans. Jpn. Soc. Mech. Engrs. 54 500 1988 688-695
5. Sakae C, Murakami Y, Ohkomori Y. Stress intensity factors for a small subsurface circular cracks under moving contact load and evaluation of allowable defect size. Material Science Research International, Special Technical Publication, vol. 1. 2001. p. 145-50
6. Wang Q. Noda N.A. Honda M. Chen M.C. Variation of stress intensity factor along the front of a 3D rectangular crack by using a singular integral equation method Int. J. Fract. 108 2001 119-131
7. Noda N.A. Kihara T.A. Variation of stress intensity factor along the front of a 3D rectangular crack subjected to mixed mode loadings Arch. Appl. Mech. 72 2002 599-614
8. Qin T.Y. Noda N.A. Analysis of a three-dimensional crack terminating at an interface using a hypersingular integral equation method Trans. ASME J. Appl. Mech. 69 2002 626-631
9. Qin TY, Noda NA. Stress intensity factors of a rectangular crack meeting a bimaterial interface. Int J Solids Struct, in press
10. Cook T.S. Erdogan F. Stress in bonded materials with a crack perpendicular to the interface Int. J. Engng. Sci. 10 1972 677-697
11. Chen D.H. Nisitani H. Stress intensity factors of a crack meeting the bimaterial interface Trans. Jpn. Soc. Engrs., Series A 59 558 1993 325-331