Effects of shot-peening on fretfing-fatigue behavior of Ti-8Al-4V

Journal of Engineering Materials and Technology

Volumn 124, Issue 2, 2002, Pages 222-228

  Namjoshi, S A ^a   Jain, V K ^b   Mall, S ^c,d  

^a Air Force Institute of Technology   (United States)

^b University of Dayton   (United States)

^c AIR FORCE RESEARCH LABORATORY   (United States)

^d AIR FORCE INSTITUTE OF TECHNOLOGY   (United States)

Author keywords

[No Author keywords available]

Indexed keywords

COMPRESSIVE STRESS; CORROSION FATIGUE; CRACK INITIATION; FINITE ELEMENT METHOD; FRETTING CORROSION; RESIDUAL STRESSES; SCANNING ELECTRON MICROSCOPY; SHOT PEENING; STRESS ANALYSIS; TENSILE STRESS; X RAY DIFFRACTION ANALYSIS;

CYCLIC FREQUENCY; FRETTING FATIGUE; TI-6AL-4V ALLOY;

TITANIUM ALLOYS;

EID: 0141746042     PISSN: 00944289     EISSN: None     Source Type: Journal    
DOI: 10.1115/1.1448323     Document Type: Article

References (25)

1. Hoeppner, D. W., Chandrasekaran, V., and Elliot, C. B., eds., 2000, "Fretting-Fatigue: Current Technologies and Practices," ASTM STP 1367, American Society for Testing and Materials, Philadelphia.
2. Hoeppner, D., and Goss, G., 1974, "A Fretting-fatigue Damage Threshold Concept," Wear, 27, pp. 61-70.
3. Rayaproula, D., and Cook, R., 1992, "A Critical Review of Fretting-fatigue Investigations at the Royal Aerospace Establishment," Standardization of Fretting-fatigue Test Methods and Equipment. ASTM STP 1159, M. Helmi and R. Waterhouse, eds. American Society for Testing and Materials, Philadelphia, pp. 129-152.
4. Waterhouse, R., 1492, "Fretting-Fatigue," Int. Mater. Rev., 37, No. 2, pp. 77-97.
5. Lykins, C. D., Mall, S., and Jain, V. K., 2000, "An Evaluation of Parameters for Predicting Fretting-fatigue Crack Initiation," Int. J. Fatigue, 22, pp. 703-716.
6. Waterhouse, R. B., 1981, "Avoidance of Fretting Fatigue Failures," Fretting Fatiaue, Applied Science Publishers, London, pp. 221-240.
7. Leadbeater, G., Noble, B., and Waterhouse, R. B., 1984, "The Fatigue of an Aluminum Alloy Produced by Fretting on Shot Peened Surfaces, " Proceedings of 6th Int. Conf. on Fracture, India, Vol. 3, pp. 2125-2132.
8. Gabel, M. K., and Bethk, J. J., 1979, "Coatings for Fretting Prevention," Wear, 46, pp. 81-96.
9. Vardiman, R. G., Creighton, D., et al., 1982, "Effect of Ion Implantation on Fretting tangue in Ti-6Al-4V Alloy," ASTM STP 780, American Society for Testing and Materials, Philadelphia, pp. 138-149.
10. Tanaka, K., Mutoh, Y., and Sakoda, S., 1985, "Effect of Contact Materials on Fretting Fatigue in a Spring Steel," Trans. Jpn. Soc. Mech. Eng., Ser, A, 51, No. 464, pp. 1200-1207.
11. De Los Rios, E. R., Brown, M. W., et al., 1999, "Effect of Shot-Peening on the Fretting Fatigue Behavior of BS L65 Aluminum Alloy," International Committee on Aeronautical Fatigue, 25'th Conference, Seattle WA.
12. De Los Rios, E. R., Trooll, M., and Levers, A., 1999, "Improving the Fatigue Crack Resistance of 2024-T351 Aluminum Alloy by Shot Peening," Life Extension-Aerospace Technology Opportunities, The Royal Aeronautical Society Publication, pp. 26.1-26.8.
13. Mutoh, Y., Satoh, T., and Tsunoda, E., 1992, "Improving Fretting Fatigue Strength at Elevated Temperatures by Shot-Peening in Steam Turbine Steel," Standardization of Fretting Fatigue Test Methods and Equipment, ASTM STP 1159, M, Helmi Attia and R. B. Waterhouse, eds., American Society for Testing and Materials Philadelphia, pp. 199-209.
14. Conez., R., Mall, S., and Calcaterra, J. R., 2000, "Interaction of High-Cycle and Low-Cycle Fatigue on Fretting-fatigue Behavior of Ti-6AL-4V," Fretting-Fatigue: Current Technology and Practices. ASTM STP 1367, D. W. Hoeppner, V. Chandrasekaran, and C. B. Elliot, eds. American Society for Testing and Materials, West Conshohocken, PA. pp. 183-198.
15. Iyer, K., and Mall, S., 2000, "Effects of Cycling Frequency and Contact Pressure on Fretting Fatigue under Two-Level Block Loading," Fatigue Fract. Eng. Mater. Struct., 23, pp. 335-346.
16. ABAQUS v5.8 Theory Manual. 1998, Pawtucket, RI (USA): Hibbit, Karlsson & Sorensen, Inc.
17. Tsai, C. T., and Mall, S., 2000, "Elasto-Plastic Finite Element Analysis of Fretting Stresses in Pre-Stressed Strip in Contact with Cylindrical Pad," Finite Elem. Anal. Design. 36, pp. 171-187.
18. Nowell, D., and Hills, D. A., 1987, "Mechanics of Fretting Fatigue Tests," Int. J. Mech. Sci., 29, pp. 355-365.
19. Lykins, C. D., Mull, S., and Jain, V. K., 2001, "A Shear Based Parameter for Fretting-fatigue Crack Initiation," Fatigue Fract. Eng. Mater. Struct., 24, pp. 461-473.
20. Coffin, Jr., L. F., 1954, "A Study of the Effects of Cyclic Thermal Stresses on a Ductile Metal," Trans. ASME, 76, 931-950.
21. Manson, S. S., 1953, "Behavior of Materials Under Conditions of Thermal Stress," Technical Report TN 2933, NACA.
22. Basquin, O. H., 1910, "The Exponential Law of Endurance Tests, " Am. Soc. Test. Mater. Proc., Vol 10, pp. 625-630.
23. Waterhouse, R B., 2000, "Plastic Deformation in Fretting Processes - a Review," Fretting-Fatigue: Current Technology and Practices, ASTM STP 1367. D. W. Hoeppner, V. Chandrasekaran, and C. B. Elliot, eds. American Society for Testing and Materials, West Conshohocken, PA, pp. 3-18.
24. Walker, K., 1970, "The Effect of Stress Ratio During Crack Propagation and Fatigue for 2024-T3 and 7075-T6 Aluminum," Effects of Environment and Complex Load History on Fatigue Life, ASTM STP 462, American Society for Testing and Materials, West Conshohocken, PA. pp. 1-14.
25. Namjoshi, S. A., Mall, S., Jain, V. K., and Jin, O., "Fretting Fatigue Crack Initiation Mechanism in Ti-6Al-4V, " submitted for publication.