Synthesis of nanosized A-type zeolites from sodium silicates and sodium aluminates in the presence of a crystallization inhibitor

Chemistry Letters

Volumn 32, Issue 7, 2003, Pages 586-587

  Hosokawa, Hiroji ^a   Oki, Kazuo ^a  

^a KAO CORPORATION   (Japan)

Author keywords

[No Author keywords available]

Indexed keywords

MACROGOL; SILICATE; SODIUM DERIVATIVE; SURFACTANT; ZEOLITE;

ADSORPTION; ARTICLE; CRYSTALLIZATION; ION EXCHANGE; NANOPARTICLE; SYNTHESIS; X RAY DIFFRACTION;

EID: 0141540719     PISSN: 03667022     EISSN: None     Source Type: Journal    
DOI: 10.1246/cl.2003.586     Document Type: Article

References (19)

1. A. E. Persson, B. J. Schoeman, J. Sterte, and J. E. Otterstedt, Zeolites, 14, 557 (1994).
2. M. Yamamura, K. Chaki, T. Wakatsuki, H. Okado, and K. Fujimoto, Zeolites, 14, 643 (1994).
3. E. F. S. Aguiar, A. Liebsch, B. C. Chaves, and A. F. Costa, Microporous Mesoporous Mater., 25, 185 (1998).
4. M. Tsapatsis, M. Lovallo, T. Okubo, M. E. Davis, and M. Sadakata, Chem. Mater., 7, 1734 (1995).
5. M. A. Camblor, A. Corma, A. Mifsud, J. Perez-Pariente, and S. Valencia, Stud. Surf. Sci. Catal., 105, 341 (1997).
6. B. J. Schoeman, J. Sterte, and J. E. Otterstedt, Zeolites, 14, 110 (1994).
7. For example, O. Okumura, T. Yoshida, T. Satoh, Y. Tsuruta, and H. Nishio, J. Clay Sci. Soc. Jpn., 27, 21 (1987).
8. I. Schmidt, C. Madsen, and C. J. H. Jacobsen, Inorg. Chem., 39, 2279 (2000).
9. -1 which are assignable to alkyl chains of C12E6, which indicates that almost of C12E6 could be removed from NZ by the processes of filtration and wash with deionized water.
10. The primary particle size of the amorphous aluminosilicates was 30 nm (variation coefficient: 20%) by the FE-SEM observation.
11. 2/g, respectively. The larger experimental values than the calculated ones may be due to the rough surface and shape (not perfect) of the zeolite particles.
12. 27Al NMR, respectively.
13. V. G. Engelhardt, D. Hoebbel, M. Tarmak, A. Samoson, and E. Lippmaa, Z. Anorg. Allg. Chem., 484, 22 (1982).
14. R. Ravishankar, C. Kirschhock, B. J. Schoeman, P. Vanoppen, P. J. Grobet, S. Storck, W. F. Maier, J. A. Martens, F. C. De Schryver, and P. A. Jacobs, J. Phys. Chem. B, 102, 2633 (1998).
15. 3), and stirred at 5°C for 1 minute or 10 minutes, and the mixture was filtered with a disposable filter with 0.2 μm pore size. Thereafter, 10 mL of the resulting filtrate is taken and assayed for a Ca content in the filtrate by using a photomeric titration apparatus (Kyoto Electronics AT-310). The Ca content exchanged per 1 g of the zeolite in 1 minute or 10 minutes is referred to as CER or CEC, respectively.
16. R. M. Barrer and L. Hinds, J. Chem. Soc., 1953, 1879.
17. 19
18. T. B. Reed and D. W. Breck, J. Am. Chem. Soc., 78, 5972 (1956).
19. G. J. Myatt, P. M. Budd, C. Price, F. Hollway, and S. W. Carr, Zeolites, 14, 190 (1994).