Effects of different whiskers on the reinforcement of dental resin composites

Dental Materials

Volumn 19, Issue 5, 2003, Pages 359-367

  Xu, Hockin H K ^a   Quinn, Janet B ^a   Smith, Douglas T ^a   Giuseppetti, Anthony A ^a   Eichmiller, Frederick C ^a  

^a NATIONAL INSTITUTE OF STANDARDS AND TECHNOLOGY   (United States)

Author keywords

Brittleness; Dental resin composite; Elastic modulus; Fracture toughness; Reinforcement mechanisms; Strength; Whisker

Indexed keywords

BRITTLENESS; CRYSTAL WHISKERS; ELASTIC MODULI; FRACTURE; REINFORCEMENT; SILICA; TOUGHNESS;

DENTAL RESINS;

DENTAL MATERIALS;

INORGANIC COMPOUND; RESIN; SILICON CARBIDE; SILICON DERIVATIVE; SILICON NITRIDE;

ANALYSIS OF VARIANCE; ARTICLE; CHEMISTRY; COMPARATIVE STUDY; DENTAL CARE; DENTAL SURGERY; ELASTICITY; HARDNESS; MATERIALS TESTING; SCANNING ELECTRON MICROSCOPY;

ANALYSIS OF VARIANCE; CARBON COMPOUNDS, INORGANIC; COMPOSITE RESINS; DENTAL STRESS ANALYSIS; ELASTICITY; HARDNESS; INLAYS; MATERIALS TESTING; MICROSCOPY, ELECTRON, SCANNING; SILICON COMPOUNDS;

EID: 0041992448     PISSN: 01095641     EISSN: None     Source Type: Journal    
DOI: 10.1016/S0109-5641(02)00078-7     Document Type: Article

References (46)

1. Bowen R.L. Properties of a silica-reinforced polymer for dental restorations. J Am Dent Assoc. 66:1963;57-64.
2. Lloyd C.H., Iannetta R.V. The fracture toughness of dental composites: I. The development of strength and fracture toughness. J Oral Rehabil. 9:1982;55-66.
3. Asmussen E. Restorative resins: hardness and strength vs. quantity of remaining double bonds. Scand J Dent Res. 90:1982;484-489.
4. Davis D.M., Waters N.E. An investigation into the fracture behavior of a particulate-filled bis-GMA resin. J Dent Res. 66:1987;1128-1133.
5. Calais J.G., Söderholm K.J.M. Influence of filler type and water exposure on flexural strength of experimental composite resins. J Dent Res. 67:1988;836-840.
6. Rueggeberg F.A., Ergle J.W., Lockwood P.E. Effect of photoinitiator level on properties of a light-cured and post-cure heated model resin system. Dent Mater. 13:1997;360-364.
7. Eick J.D., Kaufman G.M., Chappelow C.C. Applications of polymers: what are the future trends? Acad Dent Mater Trans. 10:1997;89-98.
8. Ferracane J.L., Berge H.X., Condon J.R. In vitro aging of dental composites in water - effect of degree of conversion, filler volume, and filler/matrix coupling. J Biomed Mater Res. 42:1998;465-472.
9. Watts D.C., Hindi A.A. Intrinsic soft-start polymerization shrinkage-kinetics in an acrylate-based resin composite. Dent Mater. 15:1999;39-45.
10. Krause W.R., Park S.H., Straup R.A. Mechanical properties of bis-GMA resin short glass fiber composites. J Biomed Mater Res. 23:1989;1195-1211.
11. Bayne S.C., Thompson J.Y. Mechanical property analysis of two admixed PRIMM-modified commercial dental composites. Acad Dent Mater Trans. 9:1996;238.
12. Ferracane J.L., Condon J.R. Post-cure heat treatments for composites: properties and fractography. Dent Mater. 8:1992;290-295.
13. Ferracane J.L., Hopkin J.K., Condon J.R. Properties of heat-treated composites after aging in water. Dent Mater. 11:1995;354-358.
14. Loza-Herrero M.A., Rueggeberg F.A., Caughman W.F., Schuster G.S., Lefebvre C.A., Gardner F.M. Effect of heating delay on conversion and strength of a post-cured resin composite. J Dent Res. 77:1998;426-431.
15. Wendt S.L. The effect of heat as a secondary cure upon the physical properties of three composite resins: I. Diametral tensile strength, compressive strength and marginal dimensional stability. Quintessence Int. 18:1987;265-271.
16. Wendt S.L., Leinfelder K.F. The clinical evaluation of heat-treated composite resin inlays. J Am Dent Assoc. 120:1990;177-181.
17. Asmussen E., Peutzfeldt A. Mechanical properties of heat-treated restorative resin for use in the inlay/onlay technique. Scand J Dent Res. 98:1990;564-567.
18. McCabe J.F., Kagi S. Mechanical properties of a composite inlay material following post-curing. Br Dent J. 171:1991;246-248.
19. Sakaguchi R.L., Cross M., Douglas W.H. A simple model of crack propagation in dental restorations. Dent Mater. 8:1992;131-136.
20. Wilder A.D. Jr., Bayne S.C., Heymann H.O. Long-term clinical performance of direct posterior composites. Acad Dent Mater Trans. 9:1996;151-169.
21. Christensen G.J. Porcelain-fused-to-metal vs. nonmetal crowns. J Am Dent Assoc. 130:1999;409-411.
22. Drummond J.L., Savers E.E. In vitro aging of a heat/pressure-cured composite. Dent Mater. 9:1993;214-216.
23. Donly K.J., Jensen M.E., Triolo P., Chan D. Clinical comparison of resin composite inlay and onlay posterior restorations and cast-gold restorations at 7 years. Quintessence Int. 30:1999;163-169.
24. Xu H.H.K., Martin T.A., Antonucci J.M., Eichmiller F.C. Ceramic whisker reinforcement of dental resin composites. J Dent Res. 78:1999;706-712.
25. Xu H.H.K. Dental composite resins containing silica-fused ceramic single-crystalline whiskers with various filler levels. J Dent Res. 78:1999;1304-1311.
26. Xu H.H.K., Quinn J.B., Giuseppetti A.A., Eichmiller F.C. Effects of whisker-to-silica ratio on the reinforcement of dental resin composites with silica-fused whiskers. J Dent Res. 79:2000;1844-1849.
27. Xu H.H.K. Whisker-reinforced heat-cured dental resin composites: Effects of filler level and heat-cured temperature and time. J Dent Res. 79:2000;1392-1397.
28. Oliver W.C., Pharr G.M. An improved technique for determining hardness and elastic modulus using load and displacement sensing indentation experiments. J Mater Res. 7:1992;1564-1583.
29. Willems G., Celis J.P., Lambrechts P., Braem M., Vanherle G. Hardness and Young' modulus determined by nanoindentation technique of filler particles of dental restorative materials compared with human enamel. J Biomed Mater Res. 27:1993;747-755.
30. Xu H.H.K., Smith D.T., Jahanmir S., Romberg E., Kelly J.R., Thompson V.P., Rekow E.D. Indentation damage and mechanical properties of human enamel and dentin. J Dent Res. 77:1998;472-480.
31. Lawn B.R. Fracture of brittle solids. 1993;Cambridge University Press, London. Chapter 8.
32. Ferracane J.L. Indentation fracture toughness testing and crack propagation mode in dental composites. Mater Res Soc Symp Proc. 110:1989;619-624.
33. Van Meerbeek B., Willems G., Celis J.P., Roos J.R., Braem M., Lambrechts P., Vanherle G. Assessment by nano-indentation of the hardness and elasticity of the resin-dentin bonding area. J Dent Res. 72:1993;1434-1442.
34. Xu H.H.K., Smith D.T., Schumacher G.E., Eichmiller F.C., Antonucci J.M. Indentation modulus and hardness of whisker-reinforced heat-cured dental resin composites. Dent Mater. 16:2000;248-254.
35. Xu H.H.K., Eichmiller F.C., Giuseppetti A.A., Johnson C.E. Cyclic contact fatigue of a silver alternative to amalgam. Dent Mater. 14:1998;11-20.
36. Xu H.H.K., Smith D.T., Jahanmir S. Influence of microstructure on indentation and machining of dental glass-ceramics. J Mater Res. 11:1996;2325-2337.
37. Iwanaga H., Kawai C. Tensile strength of silicon nitride whiskers synthesized by reacting amorphous silicon nitride and titanium dioxide. J Am Ceram Soc. 81:1998;773-776.
38. Xu H.H.K., Eichmiller F.C., Giuseppetti A.A. Reinforcement of a self-setting calcium phosphate cement with different fibers. J Biomed Mater Res. 52:2000;107-114.
39. ASTM F417-78. Standard test method for flexural strength of electrical grade ceramics. Philadelphia, PA: ASTM; 1984.
40. 4-matrix/SiC-fiber composites. J Am Ceram Soc. 77:1994;1889-1896.
41. The Versailles Project on Advanced Materials and Standards (VAMAS) and The European Structural Integrity Society (ESIS). Fracture toughness of ceramics using the SEVNB method; round robin. Swiss Federal Laboratories for Materials Testing and Research; 1999.
42. American Society for Testing and Materials, Standard Test Methods for Determination of Fracture Toughness of Advanced Ceramics at Ambient Temperatures. ASTM C1421-99. 1999;ASTM, West Conshohochen, PA.
43. Hood PE, Pickers JO. Silicon carbide whisker composites. US Patent 4,463,058; 1984.
44. Hirata Y., Matsushita S., Nakagama S., Ishihara Y., Hori S. Rheological properties and consolidation of the suspension in the alumina powder-silicon nitride whisker system. J Ceram Soc Jpn. 97:1989;866-871.
45. Xu H.H.K., Jahanmir S., Ives L.K. Material removal and damage formation mechanisms in grinding silicon nitride. J Mater Res. 11:1996;1717-1724.
46. Quinn J.B., Quinn G.D. Indentation brittleness of ceramics: a fresh approach. J Mater Sci. 32:1997;4331-4346.