Failure mechanisms of high strength steels in bicarbonate solutions under anodic polarization

Corrosion Science

Volumn 45, Issue 9, 2003, Pages 2017-2030

  Proverbio, E ^a   Longo, P ^a  

^a UNIVERSITY OF MESSINA   (Italy)

Author keywords

A. Steel; B. Polarization; B. SEM; C. Hydrogen embrittlement; C. Stress corrosion

Indexed keywords

BRITTLE FRACTURE; CONCRETE CONSTRUCTION; CONCRETE REINFORCEMENTS; CRACKS; FAILURE ANALYSIS; HYDROGEN; SOLUTIONS; STRENGTH OF MATERIALS; STRESS CORROSION CRACKING;

HIGH STRENGTH STEELS;

STEEL CORROSION;

ANODIC CORROSION; BICARBONATE; FAILURE; HIGH STRENGTH STEEL; POLARIZATION;

EID: 0038792266     PISSN: 0010938X     EISSN: None     Source Type: Journal    
DOI: 10.1016/S0010-938X(03)00037-4     Document Type: Article

References (19)

1. G. Sergi, Corrosion of Steel in Concrete: Cement Matrix Variables PhD Thesis, University of Aston, Birmingham, 1986
2. Alonso M.C. Andrade M.C. Corros. Sci. 29 9 1989 1129
3. Parkins R.N. Corros. Sci. 20 1980 147
4. Alonso M.C. Andrade M.C. Saenz de Santa Maria M. Corros. Sci. 34 6 1993 961
5. Parkins R.N. Elices M. Sànchez Gàlvez V. Caballero L. Corros. Sci. 22 5 1982 379
6. J. Fullea, Experimental methods to evaluate the susceptibility of prestressing steels to stress corrosion cracking, in: Proceedings of the International Workshop on Failures of Post-tensioned Concrete Structures, Messina, 2000, p. 17
7. Li R. Ferreira M.G.S. Corros. Sci. 38 2 1996 317
8. Galvele J.R. Corros. Sci. 27 1 1987 1
9. American Society for Testing of Materials, Standard practice for preparing, cleaning, and evaluating corrosion test specimens, ASTM standard G1-81, Philadelphia, PA, 1981
10. Lukito H. Szklarska-Smialowska Z. Corros. Sci. 39 12 1997 2151
11. Patanè G. Proverbio E. Risitano A. Eng. Failure Anal. 9 4 2002 481
12. Astiz M.A. Int. J. Fract. 31 1986 105
13. Valiente A. Elices M. Eng. Failure Anal. 5 3 1998 219
14. Davies D.H. Burstein G.T. Corrosion 36 8 1980 416
15. Galvele J.R. Corros. Sci. 10 8 1990 955
16. Rhead G.E. Surf. Sci. 22 1970 223
17. Vogt H. Speidel M.O. Corros. Sci. 40 23 1998 251
18. Galvele J.R. Modern Aspects Electrochem. 27 1995 223
19. Speidel M.O. Metall. Trans. A 19 1988 1583