Nanoporous copper silicates with one-dimensional 12-ring channel systems

Angewandte Chemie - International Edition

Volumn 42, Issue 18, 2003, Pages 2044-2047

  Wang, Xiqu ^a   Liu, Lumei ^a   Jacobson, Allan J ^a  

^a University of Houston   (United States)

Author keywords

Copper; Hydrothermal synthesis; Silicates transition metals; Zeolite analogues

Indexed keywords

CRYSTAL STRUCTURE; POROSITY; SILICATES; SYNTHESIS (CHEMICAL); ZEOLITES;

NANOPOROUS MATERIALS;

COPPER COMPOUNDS;

ALKALI METAL; COPPER DERIVATIVE; SILICATE; ZEOLITE;

ARTICLE; CRYSTAL STRUCTURE; POROSITY; STRUCTURE ANALYSIS; SYNTHESIS;

EID: 0038587674     PISSN: 14337851     EISSN: None     Source Type: Journal    
DOI: 10.1002/anie.200351121     Document Type: Article

References (25)

1. A. K. Cheetham, G. Férey, T. Loiseau, Angew. Chem. 1999, 111, 3466; Angew. Chem. Int. Ed. 1999, 38, 3268.
2. A. K. Cheetham, G. Férey, T. Loiseau, Angew. Chem. 1999, 111, 3466; Angew. Chem. Int. Ed. 1999, 38, 3268.
3. H. V. Bekkum, E. M. Flanigen, P. A. Jacobs, J. C. Jansen, Introduction to Zeolite Science and Practice, Elsevier, Amsterdam, 2001.
4. M. E. Davis, Nature 2002, 417, 813.
5. F. Schüth, W. Schmidt, Adv. Mater. 2002, 14, 629.
6. J. Rocha, M. W. Anderson, Eur. J. Inorg. Chem. 2000, 801.
7. X. Wang, L. Liu, A. J. Jacobson, Angew. Chem. 2001, 113, 2232; Angew. Chem. Int. Ed. 2001, 40, 2174.
8. X. Wang, L. Liu, A. J. Jacobson, Angew. Chem. 2001, 113, 2232; Angew. Chem. Int. Ed. 2001, 40, 2174.
9. X. Wang, L. Liu, A. J. Jacobson, J. Am. Chem. Soc. 2002, 124, 7812.
10. X. Wang, L. Liu, A. J. Jacobson, Mater. Res. Soc. Symp. Proc 2003, in press.
11. R. J. Francis, A. J. Jacobson, Chem. Mater. 2001, 13, 4676.
12. X. Wang, J. Huang, L. Liu, A. J. Jacobson, J. Mater. Chem. 2002, 12, 406.
13. J. Huang, X. Wang, A. J. Jacobson, J. Mater. Chem. 2003, 13, 191.
14. H. Li, M. Eddaoudi, J. Plevert, M. O'Keefe, O. M. Yaghi, J. Am. Chem. Soc. 2000, 122, 12409.
15. K. Kawamura, A. Kawahara, Acta Crystallogr. Sect. B 1976, 32, 2419.
16. K. Kawamura, A. Kawahara, Acta Crystallogr. Sect. B 1977, 33, 1071.
17. A. Heinrich, V. Gramlich, Naturwissenschaften 1982, 69, 142.
18. I. Watanabe, A. Kawahara, Acta Crystallogr Sect. C 1993, 49, 854.
19. A. Möller, Z. Anorg. Allg. Chem. 1997, 623, 1685.
20. A. R. Heinrich, C. Baerlocher, Acta Crystallogr. Sect. C 1991, 47, 237.
21. We use the general notation MSH-nA (Metal Silicate Houston, n is the framework type and A is the nonframework cation) to designate this series of compounds. Thus CuSH-n is used for the copper silicate family.
22. 6]): H 1.32, Na 11.40, Cu 10.50, Si 27.85; found: H 1.31, Na 11.13, Cu 10.38, Si 27.46
23. Kα radiation at 293 K for CuSH-1Na and at 243 K for the other three phases. The structures were solved by direct methods and refined using the SHELXTL program. All ordered non-hydrogen atom positions were refined anisotropically in the final refinements. The disordered water oxygen atoms were forced to have an equal but variable displacement parameter in order to refine their relative occupancies. The total amount of observed water is consistent with that measured from TGA measurements, and was fixed to the formula based on the TGA data. Further details on the crystal structure investigation may be obtained from the Fachinformationszentrum Karlsruhe, 76344 Eggenstein-Leopoldshafen, Germany (fax: (+49) 7247-808-666; e-mail: crysdata@fiz-karlsruhe. de), on quoting the depository numbers CSD-412966, -412967, - 412968, -412969.
24. F. Liebau, Structural chemistry of silicates, Springer, Berlin, 1985.
25. N. E. Brese, M. O'Keeffe, Acta Crystallogr. Sect. B 1991, 47, 192.