Influence of different seeds on transformation of aluminum hydroxides and morphology of alumina grains by hot-pressing

Materials and Design

Volumn 24, Issue 3, 2003, Pages 209-214

  Xie, Zhi Peng ^a   Lu, Ji Wei ^a   Gao, Li Chun ^b   Li, Wen Chao ^b   Xu, Li Hua ^b   Wang, Xi Dong ^b  

^a TSINGHUA UNIVERSITY   (China)

^b UNIVERSITY OF SCIENCE AND TECHNOLOGY BEIJING   (China)

Author keywords

Alumina seed; Aluminum hydroxide; Elongated grains

Indexed keywords

ALUMINA; ANISOTROPY; CERAMIC MATERIALS; GRINDING (COMMINUTION); HOT PRESSING; MICROSTRUCTURE; MORPHOLOGY; RAW MATERIALS; SINTERING;

MILLING BALL;

HYDRATED ALUMINA;

ALUMINUM ALLOY; ALUMINUM HYDROXIDE; GRAIN; HOT PRESSING; MILLING; MORPHOLOGY; TEMPERATURE EFFECT;

EID: 0038304578     PISSN: 02641275     EISSN: None     Source Type: Journal    
DOI: 10.1016/S0261-3069(02)00147-4     Document Type: Article

References (10)

1. Alford NMcN, Brichall JD, Kedall K. High strength ceramic through colloidal control to remove defects. Nature 1987;330(5):51-53.
2. Becher PF. Microstructural design of toughned ceramics. J Am Ceram Soc 1991;74(2):255-269.
3. 18 systems. J Am Ceram Soc 1995;78(7):1853-1856.
4. Seabaugh MM, Kerscht IH, Messing GL. Texture development by templated grain growth in liquid-phase-sintered α-Alumina. J Am Ceram Soc 1997;80(5):1181-1188.
5. Brandom D, Chen D, Chan H. Contr ol of texture in monolithic alumina. Mater Sci Eng A 1995;195:189-196.
6. Yoshizawa Y, Toriyama M, Kanzaki S. Preparation of high fracture toughness alumina sintered bodies from bayer aluminum hydroxide. J Ceram Soc Jpn 1998;106(12):1172-1177.
7. Xie ZP, Liu T, Huang Y, Cheng YB. Fracture toughness improvement of alumina with elongated grains. J Aust Ceram Soc 2000;36(2):97-102.
8. Yoshizawa Y, Saito F. Characterization of abrasive powder worn from alumina balls in wet milling and its phase transformation during heating. J Ceram Soc Jpn 1996;104:668-672.
9. Burkin AR. Production of aluminum and alumina. Chechester (Wes; Sussex): Wiley, 1987. p. 43.
10. Kumagai M, Messing GL. Enhanced densification of boehmite sol gel by α-alumina seeding. J Am Ceram Soc 1984;67:C230-231.