Cracking paths at the ply interface in a cross-ply laminate

Author keywords

Anisotropy; Bimaterials; Crack path; Delamination; Interface crack; Laminate; Transverse cracks

Indexed keywords

ANISOTROPY; CRACK PROPAGATION; CRACKS; DELAMINATION; INTERFACES (MATERIALS); LOADS (FORCES); STRENGTH OF MATERIALS; TENSILE STRESS;

EID: 0038147434     PISSN: 13598368     EISSN: None     Source Type: Journal    
DOI: 10.1016/S1359-8368(03)00019-2     Document Type: Article
Times cited : (8)

References (23)
  • 1
    • 0023828557 scopus 로고
    • A simplified analysis of transverse ply cracking in cross-ply laminates
    • Han Y.M., Hahn H.T., Croman R.B. A simplified analysis of transverse ply cracking in cross-ply laminates. Compos Sci Technol. 31:1988;165-177.
    • (1988) Compos Sci Technol , vol.31 , pp. 165-177
    • Han, Y.M.1    Hahn, H.T.2    Croman, R.B.3
  • 2
    • 84973198463 scopus 로고
    • Progressive transverse cracking in composite laminates
    • Laws N., Dvorak G.J. Progressive transverse cracking in composite laminates. J Compos Mater. 22:1988;900-916.
    • (1988) J Compos Mater , vol.22 , pp. 900-916
    • Laws, N.1    Dvorak, G.J.2
  • 3
    • 0025208713 scopus 로고
    • Poisson's ratio as a damage parameter in the static tensile loading of simple crossply laminates
    • Smith P.A., Wood J.R. Poisson's ratio as a damage parameter in the static tensile loading of simple crossply laminates. Compos Sci Technol. 38:1990;85-93.
    • (1990) Compos Sci Technol , vol.38 , pp. 85-93
    • Smith, P.A.1    Wood, J.R.2
  • 4
    • 0022098062 scopus 로고
    • Analysis of cracked laminates: A variational approach
    • Hashin Z. Analysis of cracked laminates: a variational approach. Mech Mater. 4:1985;121-136.
    • (1985) Mech Mater , vol.4 , pp. 121-136
    • Hashin, Z.1
  • 5
    • 84970126128 scopus 로고
    • The strain energy release rate of composite microcracking: A variational approach
    • Nairn J.A. The strain energy release rate of composite microcracking: a variational approach. J Compos Mater. 23:1989;1106-1129.
    • (1989) J Compos Mater , vol.23 , pp. 1106-1129
    • Nairn, J.A.1
  • 6
    • 0026171255 scopus 로고
    • Multiple transverse cracking and stiffness reduction in cross-play laminates
    • Varna J., Berglund L.A. Multiple transverse cracking and stiffness reduction in cross-play laminates. J Compos Technol Res JCTRER. 27:1991;99-106.
    • (1991) J Compos Technol Res JCTRER , vol.27 , pp. 99-106
    • Varna, J.1    Berglund, L.A.2
  • 7
    • 0027642827 scopus 로고
    • Transverse cracking in fiber-reinforced brittle matrix, cross-ply laminates
    • Xia Z.C., Carr R.R., Hutchinson J.W. Transverse cracking in fiber-reinforced brittle matrix, cross-ply laminates. Acta Metall. 41:1993;2365-2376.
    • (1993) Acta Metall , vol.41 , pp. 2365-2376
    • Xia, Z.C.1    Carr, R.R.2    Hutchinson, J.W.3
  • 8
    • 0027309822 scopus 로고
    • Analysis of stiffness loss in cross-ply composite laminates
    • Tay T.E., Lim E.H. Analysis of stiffness loss in cross-ply composite laminates. Compos Struct. 25:1993;419-425.
    • (1993) Compos Struct , vol.25 , pp. 419-425
    • Tay, T.E.1    Lim, E.H.2
  • 11
    • 0026634605 scopus 로고
    • Transverse cracking and stiffness reduction in cross ply laminates of different matrix toughness
    • Talreja R., Yalvac S., Yats L.D., Wetters G. Transverse cracking and stiffness reduction in cross ply laminates of different matrix toughness. J Compos Mater. 26:1992;1644-1663.
    • (1992) J Compos Mater , vol.26 , pp. 1644-1663
    • Talreja, R.1    Yalvac, S.2    Yats, L.D.3    Wetters, G.4
  • 12
    • 0032045288 scopus 로고    scopus 로고
    • Evolution of transverse matrix cracking in cross-ply laminates
    • Qu J., Hoiseth K. Evolution of transverse matrix cracking in cross-ply laminates. Int J Fatigue Fract Engng Mater Struct. 21:1996;451-464.
    • (1996) Int J Fatigue Fract Engng Mater Struct , vol.21 , pp. 451-464
    • Qu, J.1    Hoiseth, K.2
  • 13
    • 0024884622 scopus 로고
    • Crack deflection at an interface between dissimilar elastic materials
    • He M.Y., Hutchinson J.W. Crack deflection at an interface between dissimilar elastic materials. Int J Solids Struct. 25:1989;1053-1067.
    • (1989) Int J Solids Struct , vol.25 , pp. 1053-1067
    • He, M.Y.1    Hutchinson, J.W.2
  • 14
    • 0028485551 scopus 로고
    • Energy criterion for crack deflection at an interface between two orthotropic media
    • Martinez D., Gupta V. Energy criterion for crack deflection at an interface between two orthotropic media. J Mech Phys Solids. 42:1994;1247-1271.
    • (1994) J Mech Phys Solids , vol.42 , pp. 1247-1271
    • Martinez, D.1    Gupta, V.2
  • 16
    • 85024598889 scopus 로고
    • The elastic moduli of heterogeneous materials
    • Hashin Z. The elastic moduli of heterogeneous materials. J Appl Mech. 29:1962;143-150.
    • (1962) J Appl Mech , vol.29 , pp. 143-150
    • Hashin, Z.1
  • 17
    • 11644304284 scopus 로고
    • A self consistent mechanics of composite materials
    • Hill R. A self consistent mechanics of composite materials. J Mech Phys Solids. 13:1965;213-222.
    • (1965) J Mech Phys Solids , vol.13 , pp. 213-222
    • Hill, R.1
  • 19
    • 0027610396 scopus 로고
    • Fracture mechanics of interface cracks in anisotropic materials
    • Qu J., Bassani J.L. Fracture mechanics of interface cracks in anisotropic materials. J Appl Mech. 60:1993;422-431.
    • (1993) J Appl Mech , vol.60 , pp. 422-431
    • Qu, J.1    Bassani, J.L.2
  • 22
    • 0001349846 scopus 로고
    • Damage mechanics and the mechanical properties of a laminated 0/90 ceramic/matrix composite
    • Beyerle D.S., Spearing M.S., Evans A.G. Damage mechanics and the mechanical properties of a laminated 0/90 ceramic/matrix composite. J Am Ceram Soc. 75:1992;3321-3330.
    • (1992) J Am Ceram Soc , vol.75 , pp. 3321-3330
    • Beyerle, D.S.1    Spearing, M.S.2    Evans, A.G.3


* 이 정보는 Elsevier사의 SCOPUS DB에서 KISTI가 분석하여 추출한 것입니다.