Analysis and simulation of cracking patterns in coating under biaxial tensile or thermal stress using analysis/FEM strain-accommodation method

Engineering Fracture Mechanics

Volumn 70, Issue 12, 2003, Pages 1573-1591

  Gao, S ^a   Nakasa, K ^b   Kato, M ^b  

^a IWAKI MEISEI UNIVERSITY   (Japan)

^b HIROSHIMA UNIVERSITY   (Japan)

Author keywords

Coating; Cracking pattern; FEM; Simulation; Thermal stress analysis

Indexed keywords

CERAMIC MATERIALS; COATINGS; FINITE ELEMENT METHOD; STRAIN; THERMAL STRESS; THERMOELASTICITY;

CRACKING PATTERNS;

CRACKS;

TENSILE CRACK;

EID: 0037411843     PISSN: 00137944     EISSN: None     Source Type: Journal    
DOI: 10.1016/S0013-7944(02)00123-6     Document Type: Article

References (13)

1. Meakin P, Li G, Sandar LM, Yan H, Guinea F, Pla O, et al. Disorder and fracture. In: Charmet JC, Roux S, Guyon E, editorsNew York: Plenum Press; 1990.
2. Meakin P. Statistical models for the fracture of disordered media. In: Herrmann HJ, Roux S, editors Elsevier Science PublisherBV; 1990.
3. Sotoike Y, Kuriyama K, Shimamura S. Monte Carlo simulation for evaluating crack patterns. J Soc Mater Sci Jpn 1991;40(457):1264-9.
4. Nakasa K, Nakatsuka J. Crack initiation, propagation and branching in a disk of brittle material under axisymmetric tension. Engng Fract Mech 1991;39(4):661-70.
5. Nakasa K, Nakatsuka J. Analysis of crack branching morphology in a disk of brittle material under axisymmetric tension by usingbranching dimension. Engng Fract Mech 1994;47(3):403-15.
6. Nakasa K, Takata S, Ichigo H. An analysis of island-delamination type cracking pattern in the brittle film coated on a disk underaxisymmetric tension. Engng Fract Mech 1998;59(2):191-202.
7. Nakasa K, Kato M, Zhang D, Gao S. Analysis of cracking pattern in the brittle film coated on a disk under axisymmetric tension. In: Proceedings of the 5th International Conference on Biaxial/Multi axial Fatigue and Fractals. Poland:Cracow; 1997. p. 525-42.
8. Gao S, Nakasa K, Kato M. An analysis of repeating-division type cracking pattern in brittle coating under equi-biaxial tension. Mater Sci Res Int 2000;6(2):136-43.
9. Jeong J, Kwon D. Evaluation of the adhesion strength in DLC .lm-coated systems using the film-cracking technique. J Adhes Sci Technol 1998;12(1):29-46.
10. Gao S, Nakasa K, Kato M. Simulation of cracking patterns in sprayed coating under equi-biaxial tension. JSME Int J Ser A 2001;44(3):406-13.
11. Gao S, Nakasa K, Kato M. Analysis of cracking and delamination processes in sprayed cermet and ceramic coatings under biaxial tension. J Soc Mater Sci Jpn 2000;49(3):296-303.
12. Gao S, Nakasa K, Kato M. Analysis and simulation of cracking patterns in brittle coating under biaxial tension. In: Proceeding of International Workshop on Experimental and Computational Mechanics in Engineering and Materials Behavior. China:Urumqi; 1999. p. 243-48.
13. Kitagawa H, Yuuki R. Stress intensity factors of bifurcated cracks under two-dimensional stresses. Trans Jpn Soc Mech Engng 1975;41(346):1641-8.