Investigation of sub-surface cracks in continuous cast billets

Engineering Failure Analysis

Volumn 10, Issue 3, 2003, Pages 363-370

  Das, G ^a   Ghosh, Sukomal ^a   Ghosh Chowdhury, S ^a   Ghosh, Sabita ^a   Das, Swapan ^a   Bhattacharaya, D K ^a  

^a NATIONAL CHEMICAL LABORATORY   (India)

Author keywords

Billet defects; Continuous casting; Cracks; Production failures; Segregation

Indexed keywords

CONTINUOUS CASTING; CRACK PROPAGATION; DEFECTS; FRACTURE TESTING; ROLLING; SCANNING ELECTRON MICROSCOPY; SEGREGATION (METALLOGRAPHY); STEEL;

CONTINUOUS CAST BILLETS;

BILLETS (METAL BARS);

CASTING; COPPER; CRACK; INCLUSION; SEGREGATION; STEEL;

EID: 0037409809     PISSN: 13506307     EISSN: None     Source Type: Journal    
DOI: 10.1016/S1350-6307(02)00037-7     Document Type: Article

References (20)

1. Datta R, Prasad A, Kumar S, Bhusan V, Mishra AS. Steel Times Int 1991;15(2):40.
2. Tate M. Nippon Kokan Tech Rep 1982;36:65.
3. Stilli A. Metal Plant Tech 1984;7(1):36.
4. He K, Baker TN. Mater Sci Technol 1992;8(12):1002.
5. Sims CE, Dable FB. Trans AES 1938;46(65):81.
6. Thomas GB, Gibbons TB. Metals Technol 1981;6:1979.
7. Dieter GE. Mechanical Metallurgy. UK: McGraw Hill Book Co; 1988.
8. Fawakhry KA, Mishreky ML, Eissa MM, Makkery MF. ISJI Int 1991;31(9):1020.
9. Baker MA. Diss Abs Int 1991;51(11):2281.
10. Souni M, Beaven PA. Surf Int Anal 1990;16(1-12).
11. ASM Handbook, Vol. 1, ASM, Metals Park, Ohio, 1993.
12. Salmon Cox PH. Journal of the Iron and Steel Institute 1995;May.
13. DeBarbadillo John J, Shape Edwin, editors. Sulphide inclusions in steel. ASM, Metals Park, Ohio, 1975.
14. Rungta R, editor. Inclusions and their influence on material behavior. ASM Int, Ohio, 1988.
15. Lakhtin Yu. Engineering Physical Metallurgy and Heat Treatment. Moscow: Mir Publisher; 1979.
16. Longauam Shi, Northwood DD. J Mater Sci 1992;27:5343.
17. Report on the inhomogeneity of steel ingots. JISI 1926;139-151.
18. Whitley JH. Report on the heterogeneity of steel ingots. ISI Spec Rep 1937:16.
19. Banks TM, Gladman T. Met Technol 1979;6(3):81.
20. Wilson RK. Weld J 1982;62(6):182.