Identification of SAGBO-induced damage zone ahead of crack tip to characterize sustained loading crack growth in alloy 783

Scripta Materialia

Volumn 48, Issue 9, 2003, Pages 1271-1276

  Ma, Longzhou ^a   Chang, Keh Minn ^b  

^a UNIVERSITY OF NEVADA   (United States)

^b WEST VIRGINIA UNIVERSITY   (United States)

Author keywords

Alloy 783; Diffusion; Fatigue; Fracture; Scanning electron microscope (SEM)

Indexed keywords

ANNEALING; CRACK PROPAGATION; CRACKS; GRAIN BOUNDARIES; TENSILE STRESS;

FATIGUE CRACK PROPAGATION (FCP); STRESS ACCELERATED GRAIN BOUNDARY OXIDATION (SAGBO);

SUPERALLOYS;

EID: 0037408718     PISSN: 13596462     EISSN: None     Source Type: Journal    
DOI: 10.1016/S1359-6462(03)00049-6     Document Type: Article

References (9)

1. Smith H.H., Michel D.J. Metall. Trans. A. 17A(February):1986;370-374.
2. Chang K-M. G.E. R&D Report no: 89CRD116, June 1989, G.E. R&D Center, Schenectady, NY. p. 1-20.
3. Nicholas T., Weerasooriya T. Fracture mechanics. ASTM STP 905. vol. 17:1986;155-168.
4. Smith J.S., Heck K.A. Superalloy 1996. 1996;TMS, Warrendale, PA. p. 91-100.
5. Ma L., Chang K.-M., Mannan S.K., Patel S.J. Metall. Trans. A. 33A(November):2002;3465-3478.
6. Valerio P., Gao M., Wei R. Scr. Metall. Mater. 30:1994;1269-1274.
7. Shewmon P. Diffusion in solids. 1989;TMS, Warrendale, PA. p. 21.
8. Ghonem H., Zheng D. Mater. Sci. Eng. A. (150):1992;151-160.
9. Longzhou Ma, PhD dissertation, West Virginia University, Morgantown, WV, 2001. p. 142-50.