Influence of steel - Concrete interface quality on reinforcement corrosion induced by chlorides

Magazine of Concrete Research

Volumn 55, Issue 2, 2003, Pages 151-159

  Castel, A ^a   Vidal, T ^a   Francois R ^a   Arliguie, G ^a  

^a Laboratoire Materiaux et Durabilite des Constructions   (France)

Author keywords

[No Author keywords available]

Indexed keywords

CONCRETE BEAMS AND GIRDERS; DRYING; QUALITY ASSURANCE; SODIUM CHLORIDE; STEEL; STEEL CORROSION; WETTING;

CORROSION INITIATION; INTERFACE QUALITY;

REINFORCED CONCRETE;

EID: 0037383164     PISSN: 00249831     EISSN: None     Source Type: Journal    
DOI: 10.1680/macr.2003.55.2.151     Document Type: Article

References (21)

1. Pourbaix H. Atlas of electrochemical equilibrium in aqueous solution, Oxford University Press, Oxford, 1966.
2. Hausmann D. A. Steel corrosion in concrete. Materials Protection, 1967, 4, No. 11.
3. Gouda V. K. Corrosion and corrosion inhibition of reinforcing steel. British Corrosion Journal, 1970, 5, 198-203.
4. Nilsson L. O., Poulsen E., Sandberg P., Sorensen H. E. and Klinghoffer O. Transport processes-corrosion initiation, test methods and prediction models. HETEK Chloride penetration into concrete, State of the art. Report No. 53, Road Directorate, Ministry of Transport, Denmark, 1996.
5. Vassie P. Reinforcement corrosion and durability of concrete bridges. Proc. Instn Civil Engnrs, 1984, 76, 713-723.
6. Yonezawa T., Ashworth V. and Procter R. P. M. Pore solution composition and chloride effects on the corrosion of steel in concrete. Corrosion Engineering, 1988, 44, No. 7, 489-499.
7. Mohammed T. U., Otsuki N. and Hisada M. Corrosion of steel bars with respect to orientation in concrete. ACI Material Journal, 1999, March-April, 154-159.
8. Mohammed T. U. and Hamada H. A discussion on the paper 'Chloride threshold values to depassivate reinforcing bars embedded in a standardised OPC mortar'. CCR, 2001, 31, 835-838.
9. Glass G. K. and Buenfeld N. R. Chloride threshold level for corrosion induced deterioration of steel in concrete. Chloride Penetration into Concrete. RILEM Proceeding, 1995, St-Rémy-lès-Chevreuse, France.
10. François R., Arliguie G. and Maso J. C. Durability of Reinforced Concrete, Syntheses Report, LMDC INSA-UPS, Toulouse, France, 1994 [in French].
11. François R. and Arliguie G. Effect of microcracking and cracking on the development of corrosion in reinforced concrete members. Magazine of Concrete Research, 1999, 51, No. 2, 143-150.
12. Poulsen E. Chloride Profiles - Analysis and Interpretation of Abservations. AEC Consulting Engineers Ltd, Vedbaek Denmark, 1993.
13. Gonzalez J. A., Andrade C., Alonso C. and Feliu S. Comparison of rates of general corrosion and maximum pitting penetration on concrete embedded steel reinforcements. Cement and Concrete Research, 1995, 25, No. 2, 257-264.
14. RILEM technical committee 124-SRC. Draft recommendation for repair strategies for repair strategies for concrete structures damaged by reinforcement corrosion. Materials and Structures, 1994, 27, 415-436.
15. Konin A., François R. and Arliguie G. Durabilité des BHP armés soumis à l'action des chlorures, influence de la fissuration et de la microfissuration. Annales du B.T.P., 1999, 3, 17-29.
16. Joisel A. Les fissures du ciment, Edition de la revue des matériaux de Construction, Paris, 1961.
17. François R. and Arliguie G. Durability of loaded reinforced concrete in chloride environment. Proc. Third CANMET/ACI Int. Conf., 1994, ACI SP145 -30, (V. M. MAlhotra (Ed.)), Nice, France, pp. 573-595.
18. François R. and Arliguie G. Influence of service cracking on reinforcement steel corrosion. Journal of Materials in Civil Engineering, 1988, 10, No. 1, 14-20.
19. Goto Y. Cracks formed in concrete around deformed tension bars. ACI J. Proc., 1971, 68, No. 4, 244-251.
20. Konin A., François R. and Arliguie G. Analysis of progressive damage to reinforced ordinary and high performance concrete in relation to loading. Materials and Structures, 1998, 1, 27-35.
21. Monfore G. E. and Verbeck G. J. Corrosion of prestressed wire in concrete. ACI J. Proc., 1960, 11, 491-515.