Fracture mechanics approach to facesheet delamination in honeycomb: Measurement of energy release rate of the adhesive bond

Engineering Fracture Mechanics

Volumn 70, Issue 1, 2003, Pages 93-103

  Ural, Ani ^a   Zehnder, Alan T ^a   Ingraffea, Anthony R ^a  

^a Department of Obstetrics Gynecology   (United States)

Author keywords

Composite material; Double cantilever beam test; Energy release rate; Flatwise tension test; Honeycomb sandwich panel

Indexed keywords

FRACTURE MECHANICS; SANDWICH STRUCTURES; STRUCTURAL PANELS; TENSILE STRENGTH;

FACESHEETS;

HONEYCOMB STRUCTURES;

FRACTURE MECHANICS;

FRACTURE MECHANICS;

EID: 0037216399     PISSN: 00137944     EISSN: None     Source Type: Journal    
DOI: 10.1016/S0013-7944(02)00024-3     Document Type: Article

References (28)

1. Delamination buckling and propagation analysis of honeycomb panel using cohesive element approach
2. The splitting strength of mica
3. Direct measurement of the surface energies of crystals
4. Determination of fracture surface energies by the cleavage technique
5. New load introduction concept for improved and simplified delamination beam testing
6. Strength of composite sandwich panels containing debonds
7. Debonding and crack kinking in foam core sandwich beams-I. Analysis of fracture specimens
8. Debonding and crack kinking in foam core sandwich beams-II. Experimental investigation
9. A test technique for assessing core-skin adhesion in composite sandwich structures
10. A study of skin-core adhesion in glass reinforced sandwich materials
11. Interfacial fracture in sandwich laminates
12. Characterization of facesheet/core shear fracture of composite sandwich beams
13. On the design of the cracked sandwich beam (CSB) specimen
14. Strength of sandwich beams with interface debonding
15. PVC sandwich core materials: Fracture behaviour under mode II loading and mixed-mode conditions
16. Strength of sandwich beams with interfacial debondings in the core
17. Large deflection of cantilever beams
18. A method for determining the mode I delamination fracture toughness of elastic and viscoelastic composite materials