In situ ultrasonic measurement of crack closure

International Journal of Fatigue

Volumn 25, Issue 1, 2002, Pages 51-58

  Rokhlin, S I ^a   Kim, J Y ^a  

^a OHIO STATE UNIVERSITY   (United States)

Author keywords

Crack closure stress measurement; Fatigue; In situ experiment; Surface acoustic wave

Indexed keywords

ALUMINUM ALLOYS; CRACK INITIATION; FATIGUE OF MATERIALS; PLASTICITY; STRESS ANALYSIS; ULTRASONIC MEASUREMENT;

CRACK CLOSURES; SURFACE ACOUSTIC WAVE METHODS;

FATIGUE TESTING;

EID: 0037208414     PISSN: 01421123     EISSN: None     Source Type: Journal    
DOI: 10.1016/S0142-1123(02)00056-7     Document Type: Article

References (20)

1. Suresh S. Fatigue of Materials. 2nd ed. 1998;Cambridge University Press, New York.
2. Shin C.S., Smith R.A. Fatigue crack growth at stress concentrations - the role of notch plasticity and crack closure. Engineering Fracture Mechanics. 29:1988;301-315.
3. Elber W. The significance of fatigue crack closure. Damage tolerance in aircraft structures. ASTM STP. 486:1971;230-242.
4. McEvily AJ. On crack closure in fatigue crack growth. In: Newman JC, Jr, Elber W, editors. Mechanics of fatigue crack closure, ASTM STP 982, 1988. p. 35-43.
5. Donald K., Paris P.C. An evaluation of Dkeff estimation procedures on 6061-T6 and 2024-T3 aluminum alloys. Int J Fatigue. 21:1999;S47-S57.
6. Kujawski D. Enhanced model of partial crack closure for correlation of R-ratio effects in aluminum alloys. Int J Fatigue. 22:2001;95-102.
7. Hou C-Y, Lawrence FV. A crack-closure model for the fatigue behavior of notched component. In: Mitchell MR, Langraf RW, editors. Advanced in fatigue lifetime prediction techniques: 3rd volume, ASTM STP 1292, 1996. p.116-35.
8. Hou C.-Y., Charng J.J. Estimation of plasticity-induced crack closure in a pre-existing plastic zone. Int J Fatigue. 18:(7):1996;463-474.
9. Irving P.E., Robinson J.L., Beevers C. J Engng Fract Mech. 7:(2):1975;619-630.
10. Van Stone R.H., Richardson T.L. Automated test methods for fracture and fatigue crack growth. ASTM STP. 877:1985;148-159.
11. Sharpe W.N. Jr., Grandt A.F. Jr. A preliminary study of fatigue crack retardation using laser interferomerty to measure crack surface displacement, mechanics of crack growth. ASTM STP. 590:1976;302-320.
12. Shin C.S., Smith R.A. Fatigue crack growth from sharp notches. Int J Fatigue. 7:1985;87-93.
13. Buck O, Thompson RB, Rehbein DK. Using acoustic waves for the characterization of closed fatigue cracks. In: Newman JC, Jr, Elber W, editors. Mechanics of fatigue crack closure, ASTM STP 982, 1988. p. 536-47.
14. Resch MT, Nelson DV. An ultrasonic method for measurement of size and opening behavior of small fatigue cracks. In: Larsen JM, Allison JE, editors. Small-crack test methods, ASTM STP 1149, 1992. p.169-96.
15. Tittman BR, Buck O. Fatigue lifetime prediction with the aid of SAW NDE. In: Proceedings of the DARPA/AFML Review of Progress in Quantitative NDE, 1980. p. 411-21.
16. Kim J.-Y., Rokhlin S.I. Surface acoustic wave measurements of small fatigue cracks initiated from a surface cavity. Int J Solids Struct. 39:(6):2002;1487-1504.
17. Dai W., Kim J.-Y., Rokhlin S.I. In situ surface acoustic wave monitoring of fatigue crack initiation and propagation. Thompson D.O., Chimenti D.E., Review of Progress in Quantitative Nondestructive Evaluation, vol. 18B. 1999;2225-2233 Plenum Press, New York.
18. Rokhlin S.I., Kim J.Y. In situ ultrasonic monitoring of surface fatigue crack initiation and growth from surface cavity. Int J Fatigue. 25:(1):2002;41-49.
19. Pilkey W.D. Peterson's Stress Concentration Factors. 1997;Wiley, New York.
20. Rokhlin S.I., Kim J.-Y., Nagy H., Zoofan B. Effect of pitting corrosion on the fatigue crack initiation and fatigue life. Engng Fract Mech. 62:1999;425-444.