Determination of the length dependence of the threshold for the fatigue crack propagation

Engineering Fracture Mechanics

Volumn 69, Issue 8, 2002, Pages 899-907

  Tabernig, B ^a   Pippan, R ^a  

^a UNIVERSITY OF LEOBEN   (Austria)

Author keywords

Extrinsically small cracks; Fatigue crack growth testing; Pre cracking; R(resistance) curve against fatigue crack propagation; Threshold of stress intensity factor range

Indexed keywords

COMPACTION; CRACK PROPAGATION; FATIGUE OF MATERIALS; LOAD TESTING; RESIDUAL STRESSES;

STRESS INTENSITY FACTOR RANGE;

FRACTURE MECHANICS;

FATIGUE CRACK;

EID: 0037156784     PISSN: 00137944     EISSN: None     Source Type: Journal    
DOI: 10.1016/S0013-7944(01)00129-1     Document Type: Article

References (16)

1. Resistance-curve method for predicting propagation threshold of short fatigue cracks at notches
2. The influence of crack length on fatigue crack growth in deep sharp notches
3. Short fatigue crack behavior in relation to three dimensional aspects and crack closure effect
4. Near threshold short fatigue crack growth
5. Mechanisms of fatigue crack propagation in metals, ceramics and composites: The role of crack tip shielding
6. Effects of defects, inclusions and inhomogeneities on fatigue strength
7. Threshold value for engineering application
8. Resistance curves for the threshold of fatigue crack propagation in particle reinforced aluminium alloys
9. The use of fatigue specimens pre-cracked in compression for measuring threshold values and crack growth
10. th
11. Crack initiation in cyclic compression and its application
12. Fatigue crack propagation of short and long cracks: Physical basis, prediction methods and engineering significance
13. The growth of short cracks under cyclic compression
14. Hysteresis in near-threshold fatigue crack propagation: A reconsideration
15. Growth of cracks under four field cyclic compressive loads: Numerical and experimental results